Lamination of electrochromic device to glass substrates

Patent metadata

Field	Value
Publication number	US-11241865-B2
Application number	US-201615065050-A
Country	US
Kind code	B2
Filing date	Mar 9, 2016
Priority date	Mar 5, 2010
Publication date	Feb 8, 2022
Grant date	Feb 8, 2022

Abstract

Electrochromic device laminates and their method of manufacture are disclosed.

First claim

The invention claimed is:

1. A process, comprising:
providing an electrochromic substrate, wherein the electrochromic substrate is annealed glass;
fabricating electrochromic device precursors on the electrochromic substrate;
cutting the electrochromic substrate into individual electrochromic devices, wherein cutting comprises inducing a surface crack in the electrochromic substrate and applying a bending moment to propagate the surface crack and separate the electrochromic devices from each other, wherein the crack is propagated along a length of the substrate, wherein the length is perpendicular to a thickness of the substrate, and wherein the length of propagation is greater than a depth of the surface crack; and
laminating each of the individual electrochromic devices to a corresponding glass pane, wherein the electrochromic substrate comprises a coefficient of thermal expansion that is different from a coefficient of thermal expansion of the corresponding glass pane, wherein each of the individual electrochromic devices has an edge strength of at least 60 MPa.

2. The process of claim 1 , wherein inducing the crack forms the crack only partly through and not completely through a thickness of the electrochromic substrate.

3. The process of claim 1 , wherein cutting the electrochromic substrate comprises locally heating the electrochromic substrate followed by cooling along a separation line.

4. The process of claim 1 , wherein each of the individual electrochromic devices has an edge strength of at least 75 MPa.

5. The process of claim 1 , wherein each of the individual electrochromic devices has an edge strength of at least 100 MPa.

6. The process of claim 1 , wherein:
a layout for the electrochromic device precursors has a space between the electrochromic device precursors; and
cutting includes cutting the electrochromic substrate along the space between the electrochromic device precursors.

7. The process of claim 1 , wherein laminating is performed such that an interlayer is disposed between the electrochromic substrate and its corresponding glass pane.

8. The process of claim 1 , wherein the interlayer comprises a polyvinylbutyral, an ionomeric material, an ethylenevinyl acetate, a polyurethane, or a mixture thereof.

9. The process of claim 1 , wherein cutting comprises laser cutting.

10. The process of claim 1 , wherein cutting comprises electrothermal cutting.

11. The process of claim 1 , wherein cutting comprises mechanical cutting.

12. The process of claim 1 , wherein each of the individual electrochromic devices is smaller than its corresponding glass pane in at least one dimension.

13. The process of claim 12 , wherein each of the individual electrochromic devices is indented about 0.5 mm to about 3 mm relative to the its corresponding glass pane in at least one dimension.

14. The process of claim 1 , wherein cutting comprises laser cutting or electrothermal cutting.

15. A process, comprising:
providing an electrochromic substrate, wherein the electrochromic substrate is annealed glass;
cutting the electrochromic substrate into one or more substrate daughter panes, wherein cutting includes inducing a surface crack in the electrochromic substrate and applying a bending moment to propagate the surface crack and separate the electrochromic substrate into the daughter panes, wherein the crack is propagated along a length of the substrate, wherein the length is perpendicular to a thickness of the substrate, and
wherein the length of propagation is greater than a depth of the surface crack;

fabricating electrochromic device precursors on each of the one or more daughter panes;
cutting the one or more daughter panes to form individual electrochromic devices, wherein each of the individual electrochromic devices includes a portion of the one or more daughter panes and at least one of the electrochromic device precursors, wherein each of the individual electrochromic devices has an edge strength of at least 60 MPa; and
laminating each of the individual electrochromic devices to a corresponding glass pane, wherein the electrochromic substrate comprises a coefficient of thermal expansion that is different from a coefficient of thermal expansion of the corresponding glass pane.

16. The process of claim 15 , wherein inducing the surface crack forms the surface crack only partly through and not completely through a thickness of the electrochromic substrate.

17. The process of claim 15 , wherein cutting the electrochromic substrate comprises locally heating the electrochromic substrate followed by cooling along a separation line.

18. A process, comprising:
providing an electrochromic substrate, wherein the electrochromic substrate is annealed glass;
fabricating electrochromic device precursors on the electrochromic substrate, wherein a layout for the electrochromic device precursors has a space between electrochromic device precursors;
laser cutting the electrochromic substrate along the space between the electrochromic device precursors into individual electrochromic devices, wherein:
laser cutting comprises inducing a surface crack only partly through, and not completely through, a thickness of the electrochromic substrate, and applying a bending moment to propagate the surface crack and separate the electrochromic devices from each other, wherein the crack is propagated along a length of the substrate, wherein the length is perpendicular to a thickness of the substrate, and wherein the length of propagation is greater than a depth of the surface crack;

laser cutting the electrochromic substrate includes locally heating the electrochromic substrate followed by cooling along a separation line; and
each of the individual electrochromic devices has an edge strength of at least 75 MPa; and
laminating each of the individual electrochromic devices to a corresponding glass pane, wherein the electrochromic substrate comprises a coefficient of thermal expansion that is different from a coefficient of thermal expansion of the corresponding glass pane, wherein each of the individual electrochromic devices is smaller than its corresponding glass pane in at least one dimension.

Assignees

• Sage Electrochromics Inc

Inventors

• Sbar Neil L
• Van Dine John E
• Mccoy Michael A

Classifications

• Y10T156/1062

  Prior to assembly · CPC title

• B32B17/10981

  Pre-treatment of the layers · CPC title

• Y10T156/1075

  of plural laminae from single stock and assembling to each other or to additional lamina · CPC title

• B32B38/0004

  Cutting, tearing or severing, e.g. bursting; Cutter details (cutting in general B26D; laminating combined with punching or perforating B32B38/04; removing all or part of the layers B32B38/10; cutting in combination with laying up and registration B32B38/185 takes precedence) · CPC title

• G02F1/133351

  Manufacturing of individual cells out of a plurality of cells, e.g. by dicing · CPC title