Abstract

Disclosed is a process whereby diverse classes of materials can be 3D printed and fully integrated into device components with active properties. An exemplary embodiment shows the seamless interweaving of five different materials, including (1) emissive semiconducting inorganic nanoparticles, (2) an elastomeric matrix, (3) organic polymers as charge transport layers, (4) solid and liquid metal leads, and (5) a UV-adhesive transparent substrate layer, demonstrating the integrated functionality of these materials. Further disclosed is a device for printing these fully integrated 3D devices.

First claim

What is claimed:

1. A method of making a device, comprising the steps of:
providing a first conductive ink; and
depositing the first conductive ink to form a first conductive pattern via 3D printing;
providing a first ink comprising at least one particle selected from the group consisting of a superconducting particle, a piezoelectric particle, a pyroelectric particle, a ferroelectric particle, a multiferroic particle, and a topological insulator particle;
depositing the first ink to form a first layer via 3D printing;
providing a second conductive ink; and
depositing the second conductive ink to form a second conductive pattern via 3D printing, the formed first layer being between the first conductive pattern and the second conductive pattern.

2. The method according to claim 1 , further comprising 3D printing at least one of an elastomeric matrix, organic polymers, solid or liquid metal leads, nanoparticle semiconductors, or a UV-adhesive transparent substrate layer.

3. The method according to claim 1 , further comprising:
identifying at least one material of an electrode, semiconductor, or polymer that possesses desired functionalities and exists in a printable format; and
patterning of the at least one identified material via direct dispensing onto a substrate.

4. The method according to claim 3 , further comprising:
scanning the topology of the surface of the substrate; and
providing information derived from the scanning step into the computer aided design (CAD) design of the device for conformal 3D printing.

5. The method according to claim 4 , wherein the substrate comprises at least one of a flat substrate, a non-flat substrate, a biological substrate, a glass substrate, a polyamide film, a polyimide film, and a 3D printed substrate.

6. The method according to claim 4 , wherein the substrate comprises a contact lens.

7. The method according to claim 6 , wherein electronics printed on the contact lenses provides a wearable display and/or a continuous on-eye glucose sensor.

8. The method according to claim 3 , wherein the device is an active device from among quantum dot light-emitting diodes (QD-LEDs), MEMS devices, transistors, solar cells, thermoelectrics, piezoelectrics, batteries, fuel cells, and photodiodes.

9. The method according to claim 3 , incorporating other classes of nanoscale functional building blocks and devices including metallic, semiconductor, plasmonic, biological, and ferroelectric materials, wherein the nanoscale functional building blocks and devices are comprised of at least one type selected from the group consisting of particles, wires, and a film.

10. The method according to claim 3 , wherein the first layer is printed by a method comprising the steps of: providing a syringe with a predetermined nozzle tip size, loading the ink comprising the semiconducting particles into the syringe, placing the syringe under vacuum, turning off the vacuum, lowering the syringe until the ink at the nozzle tip touches the substrate, holding the syringe in place for a predetermined period of time, and raising the syringe and placing the syringe under vacuum.

11. The method according to claim 3 , further comprising printing a conductive pattern connecting the first layer and a second layer.

12. The method according to claim 3 , further comprising dissolving or suspending the at least one material in a composition comprising a solvent.

13. The method according to claim 12 , wherein the composition further comprises a second solvent.

14. The method according to claim 12 , wherein the at least one material is present in the composition at between about 0.02 wt % and about 0.20 wt %.

15. The method according to claim 3 , wherein a pressure regulator is used to control a pressure for a nozzle used to deposit the first ink.

16. The method according to claim 15 , wherein the pressure for the nozzle is between 0 and 100 psi.

17. The method according to claim 1 , further comprising depositing at least one additional material.

18. The method according to claim 17 , wherein the at least one additional material has a type selected from the group consisting of semiconducting, piezoelectric, pyroelectric, superconducting, ferroelectric, magnetic, multiferroic, and topological insulator materials.

19. The method according to claim 17 , wherein depositing material is deposited via a method selected from the group consisting of electrospinning, electrohydrodynamic printing, or inkjet printing.

20. The method according to claim 1 , wherein the ink is deposited via a method selected from the group consisting of electrospinning, electrohydrodynamic printing, or inkjet printing.

21. The method according to claim 1 , wherein the device comprises at least the first layer and a non-3D printed layer or component.

22. The method according to claim 21 , wherein the non-3D printed layer or component is a contact lens.

23. A method of making a device, comprising the steps of:
providing a first ink comprising at least one particle selected from the group consisting of a semiconductor particle, a superconducting particle, a piezoelectric particle, a pyroelectric particle, a ferroelectric particle, a magnetic particle, a multiferroic particle, and a topological insulator particle;
depositing the first ink via 3D printing to form at least one active electronic layer;
providing an additional ink; and
depositing the additional ink via 3D printing onto the at least one active electronic layer to form a conductive pattern, the conductive pattern adapted to allow an electric potential to be applied across the active electronic layer.

Assignees

• Univ Princeton

Inventors

• Mcalpine Michael C
• Kong Yong Lin

Classifications

• Y02E10/549

  Organic PV cells · CPC title

• B33Y10/00

  Processes of additive manufacturing · CPC title

• B29C64/112 Primary

  using individual droplets, e.g. from jetting heads · CPC title

• Y02P70/50

  Manufacturing or production processes characterised by the final manufactured product · CPC title

• H01L51/0022

  Electricity · mapped topic