High temperature zinc complex grease

Patent metadata

Field	Value
Publication number	US-11236285-B2
Application number	US-202117140891-A
Country	US
Kind code	B2
Filing date	Jan 4, 2021
Priority date	Jan 3, 2020
Publication date	Feb 1, 2022
Grant date	Feb 1, 2022

Abstract

Zinc complex greases with different complexing acids having dropping points comparable to lithium greases and tailor-made dropping points can be made by processing at low temperature in open as well as close kettle process. The present invention discloses a process of manufacturing Zinc complex greases—through reaction of fatty acid and complexing acid with zinc oxide in mineral oil to obtain zinc complex greases having high dropping points of 180 to 280° C.

First claim

The invention claimed is:

1. A lubricating zinc complex grease composition consisting of:
a) base oils;
b) saponifiable materials;
c) zinc oxide;
d) complexing agents; and
e) water;
wherein the complexing agent is selected from dicarboxylic acid, polycarboxylic acid, mono carboxylic acids, boric acid, phthalic acid, and acetic acid and wherein the lubricating zinc complex grease composition has a dropping point in a range of 200 to 280° C.

2. The zinc complex grease composition according to claim 1 , wherein the saponifiable material is selected from fatty acids, hydroxy-substituted fatty acids, esters, or mixtures thereof.

3. The zinc complex grease composition according to claim 1 , wherein the saponifiable material is 12-hydroxystearic acid, stearic acid, or mixtures thereof.

4. The zinc complex grease composition according to claim 1 , wherein the base oil is selected from API group I-III mineral base oils, synthetic base oils of API group IV, preferably paraffinic base oil, naphthenic base oil.

5. The zinc complex grease composition as claimed in claim 1 , wherein the base oil is present in an amount of about 50 parts by weight to about 80 parts by weight of the composition.

6. The zinc complex grease composition as claimed in claim 1 , wherein the saponifiable material is present in an amount of about 10 parts by weight to about 30 parts by weight of the composition.

7. The zinc complex grease composition as claimed in claim 1 , wherein the zinc oxide is present in an amount of about 3 parts by weight to about 6 parts by weight of the composition.

8. The zinc complex grease composition as claimed in claim 1 , wherein the complexing acid is present in an amount of about 1 part by weight to about 6 parts by weight of the composition.

9. An open kettle process for preparing a zinc complex composition, the process consisting of the steps of:
a) adding saponifiable materials with a suitable base oil and heating to form a mixture;
b) adding zinc oxide to the mixture of step (a) and heating gradually to 100-110° C. while controlling frothing and stirring for one hour;
c) adding complexing acids and remaining amount of zinc oxide to the mixture of step (b); raising temperature to 135-140° C. and maintaining at this temperature for one hour with continuous stirring;
d) heating to elevated temperatures of around 170-175° C. with continuous stirring;
e) dehydrating a resultant mass of step (d) with the help of vacuum;
f) addition of remaining base oils as cut back;
g) cooling and homogenizing/milling to obtain final product: and
h) adding water; and
wherein the complexing agent is selected from dicarboxylic acid, polycarboxylic acid, mono carboxylic acids, boric acid, phthalic acid, and acetic acid.

10. A closed kettle process for preparing a zinc complex composition, the process consisting the steps of:
a. adding saponifiable materials, complexing acids and zinc oxide with a suitable base oil to a kettle/reactor in a single step;
b. closing the kettle/reactor securely;
c. heating gradually to 110-115° C. and maintaining at this temperature for one hour under continuous stirring;
d. further raising temperature to 170-175° C. in one hour period and maintaining this temperature under stirring for one hour;
e. de-pressurizing with caution to avoid any soap leakage followed by dehydrating a resultant mass from step (d) under vacuum with continuous stirring for half an hour;
f. adding remaining base oils as cut back
g. cooling and homogenizing/milling to obtain a smooth product; and
h. adding water; wherein the complexing agent is selected from dicarboxylic acid, polycarboxylic acid, mono carboxylic acids, boric acid, phthalic acid, and acetic acid.

11. The zinc complex grease composition as claimed in claim 1 , having higher dropping points, good low temperature, inherent extreme pressure, anti-wear, water repellent and water resistance properties.

Assignees

• Indian Oil Corp Ltd

Inventors

• Vennampalli Manohar
• Pokhriyal Naveen Kumar
• Kumar Virender
• Bansal Veena Rani
• Saxena Deepak
• RAMAKUMAR Sankara Sri Venkata

Classifications

• C10N2020/01

  Physico-chemical properties · CPC title

• C10N2030/08

  Resistance to extreme temperature · CPC title

• C10N2030/00

  Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives · CPC title

• C10N2050/10

  semi-solid; greasy · CPC title

• C10M101/025

  waxes · CPC title