Switchable water-based paint or coating compositions

Patent metadata

Field	Value
Publication number	US-11236250-B2
Application number	US-201615579424-A
Country	US
Kind code	B2
Filing date	Jun 6, 2016
Priority date	Jun 4, 2015
Publication date	Feb 1, 2022
Grant date	Feb 1, 2022

Abstract

The present application provides switchable, homogeneous paint composition and methods of painting and/or forming films or coatings using the composition. The composition includes a liquid having an aqueous solution and dissolved acid gas (e.g., carbonated water), and a switchable polymer. The switchable polymer converts from a protonated, water-soluble form in the liquid to a water-insoluble unprotonated form following removal or substantial removal of the liquid and acid gas.

First claim

We claim:

1. A method of forming a film on a substrate, comprising:
applying to a substrate a composition comprising:
a liquid medium; and
a polymer that has a T g in the range of from about 20° C. to about 50° C., and that comprises protonatable moieties, wherein a portion of the protonatable moieties are in their protonated form such that the degree of polymer protonation is sufficient to at least partially solvate the polymer in the liquid medium; the liquid medium comprising water or an aqueous solution and an acid gas dissolved at a concentration sufficient to maintain said portion of protonatable moieties in their protonated form;

crosslinking the composition, the composition comprising at least one cross-linking agent,
wherein the at least one crosslinking agent is inhibited from cross-linking by the dissolved acid gas,
wherein, when the composition is applied to the substrate under ambient conditions the concentration of dissolved acid gas decreases such that some or all of the portion of protonatable moieties switch from their protonated form to their non-protonated form and the degree of polymer protonation is reduced such that it becomes insufficient to maintain the at least partial dissolution of the polymer in the liquid medium, and the polymer forms a film that is substantially water-insoluble, water-resistant, and/or hydrophobic.

2. The method of claim 1 , wherein the acid gas is CO 2 , CS 2 , or COS.

3. The method of claim 1 , wherein the protonatable moieties of the composition comprise one or more of the following characteristics:
(i) the protonatable moieties are guanidines, amidines, tertiary amines, secondary amines, primary amines, or a combination of two or more of these moieties; and
(ii) the protonatable moieties comprise one or more of

where
the wiggly lines represent one or more bonds attaching the protonatable moiety to the remainder of the polymer; and
each of R 1 , R 2 , and R 3 is independently:
(a) H, an aliphatic group, a substituted aliphatic group, or absent, as required to satisfy valence rules;
(b) H, alkyl, substituted alkyl, cycloalkyl, substituted cycloalkyl, heterocycloalkyl, substituted heterocycloalkyl, alkenyl, substituted alkenyl, alkynyl, substituted alkynyl, aryl, substituted aryl, heteroaryl, or substituted heteroaryl;
(c) H; a substituted or unsubstituted C 1 to C 8 alkyl, alkenyl, or alkynyl group that is linear, branched, or cyclic; a substituted or unsubstituted C 1 to C 8 alkyl, alkenyl, or alkynyl group that is linear, branched, or cyclic, wherein one or more C of the alkyl group is replaced by {—Si(R 4 ) 2 —O—}; a substituted or unsubstituted C k Si m group where k and m are independently a number from 0 to 8 and k+m is a number from 1 to 8; a substituted or unsubstituted C 4 to C 8 aryl group; a substituted or unsubstituted C 4 to C 8 aryl group, wherein one or more C is replaced by {—Si(R 4 ) 2 —O—}; a substituted or unsubstituted aryl group having 4 to 8 ring atoms; a substituted or unsubstituted aryl group having 4 to 8 ring atoms, wherein said aryl group comprises one or more {—Si(R 4 ) 2 —O—}; a —(Si(R 4 ) 2 —O) p — chain in which p is from 1 to 8 which is terminated by H, or is terminated by a substituted or unsubstituted C 1 to C 8 aliphatic group; wherein R 4 is a substituted or unsubstituted C 1 to C 8 aliphatic group; or wherein any two of R 1 , R 2 , and R 3 , taken together with the nitrogen to which they are attached, are joined to form a heterocyclic ring; or
(d) H, C 1 -C 6 alkyl, substituted C 1 -C 6 alkyl, C 2 -C 6 alkenyl, substituted C 2 -C 6 alkenyl, C 2 -C 6 alkynyl, or substituted C 2 -C 6 alkynyl.

4. The method of claim 1 , wherein the polymer comprises one or more of the following characteristics:
(a) the polymer is a linear or branched homopolymer; a linear or branched co-polymer comprising two or more repeat units; a dendrimer; a self-assembled polymer; a cross-linking polymer; or any combination thereof;
(b) the polymer is a linear or branched homopolymer; a linear or branched co-polymer comprising two or more repeat units; a dendrimer; a self-assembled polymer; a cross-linking polymer; or any combination thereof; wherein the co-polymer, dendrimer, self-assembled polymer, or cross-linking polymer comprise repeat units having protonatable moieties, and repeat units having no protonatable moieties;
(c) the polymer is a linear or branched homopolymer; a linear or branched co-polymer comprising two or more repeat units; a dendrimer; a self-assembled polymer; a cross-linking polymer; or any combination thereof; wherein the co-polymer is a random co-polymer; a graft co-polymer; a block co-polymer; a star co-polymer; or any combination thereof;
(d) the polymer comprises one or more repeat units selected from the group consisting of:

(e) the polymer is poly(2-diethylamino)ethyl methacrylate, (p(DEAEMA)); or poly(methylmethacrylate)-poly(2-diethylamino)ethylmethacrylate (p(MMA-co-DEAEMA)); or, poly(N,N′-dimethylamino-propylmethacrylamide); or, poly(N,N′-dimethylaminopropylmethacrylamide)-co-poly(butylmethacrylate) (p(DMAPMAm-co-BMA)); or poly(dimethylaminopropylmethacrylamide-co-butylacrylate) (p(DMAPMAm-co-BA)); or poly(N,N′-dimethylaminopropylmethacrylamide)-poly(butylmethacrylate)-poly(2-hydroxyethylmethacrylate) (p(DMAPMAm-co-BMA-co-HEMA));
(f) the polymer has a T g in the range of from about 20° C. to about 50° C.; or, alternatively, from about 30° C. to about 50° C.; or, alternatively, from about 40° C. to about 50° C.; or, alternatively, from about 30° C. to about 45° C.;
(g) the polymer has a T g in the range of from about −20° C. to about 50° C.; or, alternatively, from about −15° C. to about 50° C.; or, alternatively from about −20° C. to about 20° C.;
(h) the polymer has a molecular weight between 5000-100000; or, between 10000-100000; or, between 10000-80000; or between 15000-80000; or, between 20000-75000; or, between 25000-70000; or between 40000-60000;
(i) the polymer is present at a concentration of from about 10-60% by weight, or from about 15-40% by weight; and
(j) the polymer is present at a concentration of from about 20-40% by weight, or from about 20-30% by weight, or about 20%, or about 25%.

5. The method of claim 1 , wherein the composition is applied to a surface at a temperature of:
(a) about room temperature; or, alternatively, at a temperature of about 25° C.; or, alternatively, at a temperature between about 25° C. to about 15° C.; or, alternatively at a temperature between about 25° C. to about 10° C.; or, alternatively at a temperature between about 25° C. to about 5° C.; or, alternatively at a temperature between about 25° C. to about 1° C.; or, alternatively at a temperature about 4° C.; or, alternatively at a temperature about, or below 0° C.; or
(b) about 250° C.; or, alternatively, at a temperature of about 150° C.; or, alternatively, at a temperature between about 60° C. to about 250° C.; or, alternatively at a temperature between about 60° C. to about 200° C.; or, alternatively at a temperature between about 60° C. to about 150° C.; or, alternatively at a temperature between about 60° C. to about 110° C.

6. The method of claim 1 , wherein applying is:
(a) spread, sprayed, flow coated, electrodeposited, roll-to-roll processed, painted, dipped, or cast on the substrate;
(b) applied to a substrate by brush, draw-down bar, doctor blades, knives, air knives, immersion, extrusion, spray, heated spray, or any other application method; or
(c) applied to the substrate by ink jets, roll

Assignees

• Univ Kingston

Inventors

• Resendes Rui
• Jessop Philip G
• Cunningham Michael F
• Mudraboyina Bhanu Prakash
• Ozvald Adam Michael
• Clark Timothy James
• Mariampillai Brian
• Yang Yun
• Holland Amy Marie
• Honeyman Charles Howard

Classifications

• C09D139/00

  Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a single or double bond to nitrogen or by a heterocyclic ring containing nitrogen; Coating compositions based on derivatives of such polymers · CPC title

• C09D133/066

  containing -OH groups · CPC title

• C09D11/106

  containing macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• C09D201/00

  Coating compositions based on unspecified macromolecular compounds · CPC title

• C09D133/10 Primary

  Homopolymers or copolymers of methacrylic acid esters · CPC title