Abstract

Solutions to the problems of scuffing and chipping of the paint films in high traffic areas and in tight spaces, such as dressing rooms in department stores, where multiple scrapings of the wall paints are created by consumers, clothes hangers, shoes, etc., and hallways and conference rooms in office and other commercial buildings are disclosed. Wax seeded latex polymers admixed with an added wax in architectural compositions and optionally with polyurethane resin are utilized to create paint films that are resistant to scuffing and chipping.

First claim

We claim:

1. An architectural aqueous coating composition that forms a paint film, said paint film is capable of resisting scuffing or chipping, wherein the architectural aqueous coating composition comprises:
a wax seeded latex, wherein the wax seeded latex comprises a hydrophobic, wax compound entrapped within a polymeric matrix,
a wax, wherein the wax makes up from 1.04 wt. % to 4.77 wt. % of the architectural aqueous coating composition, and
a coalescent aid, wherein a range of wax seeded latex to coalescent aid weight ratios is from 14.7 to 16.15.

2. The architectural aqueous coating composition accordingly to claim 1 further comprising an opacifying pigment.

3. The architectural aqueous coating composition accordingly to claim 2 , wherein a range of opacifying pigment to wax weight ratios is from 5.6 to 8.

4. The architectural aqueous coating composition accordingly to claim 1 further comprising a polyurethane resin.

5. The architectural aqueous coating composition accordingly to claim 4 , wherein a range of weight ratios of the wax seeded latex to the polyurethane resin is about 2.17±10%.

6. The architectural aqueous coating composition accordingly to claim 1 further comprising a polymeric synthetic pigment.

7. The architectural aqueous coating composition accordingly to claim 6 , wherein a range of weight ratios of the wax seeded latex to the polymeric synthetic pigment is about 12.11±10%.

8. The architectural aqueous coating composition accordingly to claim 1 , wherein the wax has an average particle size (mV) from about 10 μm to about 13 μm.

9. An architectural aqueous coating composition that forms a paint film, said paint film is capable of resisting scuffing or chipping, wherein the architectural aqueous coating composition comprises:
a wax seeded latex, wherein the wax seeded latex comprises a hydrophobic, wax compound entrapped within a polymeric matrix,
an optional opacifying pigment,
a wax, wherein the wax makes up from about 2.0 wt. % to about 12.0 wt. % of the architectural aqueous coating composition
wherein the wax has an average particle size (mV) from about 1 microns (μm) to about 25 μm.

10. The architectural aqueous coating composition accordingly to claim 9 , wherein the wax makes up from about 3.0 wt. % to 10.0 wt. % of the architectural aqueous coating composition.

11. The architectural aqueous coating composition accordingly to claim 9 , wherein the wax makes up from about 3.0 wt. % to 7.0 wt. % of the architectural aqueous coating composition.

12. The architectural aqueous coating composition accordingly to claim 9 further comprising the opacifying pigment and wherein a range of opacifying pigment to wax weight ratios less than about 8.0.

13. The architectural aqueous coating composition accordingly to claim 12 , wherein the range of opacifying pigment to wax weight ratios less than about 6.0.

14. The architectural aqueous coating composition accordingly to claim 9 further comprising a coalescent aid, wherein a range of wax seeded latex to coalescent aid weight ratios is from about 15 to about 35.

15. The architectural aqueous coating composition accordingly to claim 9 further comprising a polyurethane resin.

16. The architectural aqueous coating composition accordingly to claim 15 , wherein a range of wax seeded latex to polyurethane resin weight ratios is from about 1.0 to about 2.5.

17. The architectural aqueous coating composition accordingly to claim 16 , wherein the range of wax seeded latex to polyurethane resin weight ratios is from about 1.25 to about 2.25.

18. The architectural aqueous coating composition according to claim 9 , wherein the wax comprises a HDPE oxidized powder.

19. The architectural aqueous coating composition according to claim 9 , wherein the wax comprises a dispersion of wax in water or another solvent.

20. The architectural aqueous coating composition according to claim 9 , wherein the wax seeded latex comprises a wax center having a molecular weight (Mn or Mw) from about 200 to about 1000.

21. The architectural aqueous coating composition according to claim 20 , wherein the wax seeded latex comprises an acrylic matrix polymer.

22. The architectural aqueous coating composition accordingly to claim 9 further comprising an opacifying pigment.

23. The architectural aqueous coating composition according to claim 9 further comprising a color pigment or a colorant.

24. The architectural aqueous coating composition according to claim 9 , wherein the wax has an average particle size (mV) from about 3 um to about 22 μm.

25. The architectural aqueous coating composition according to claim 9 , wherein the wax has an average particle size (mV) from about 5 um to about 20 μm.

26. The architectural aqueous coating composition according claim 9 , wherein the wax has an average particle sizes (mV) from about 6 to about 7.5 μm, from about 10 to about 13 μm, and/or from about 16 to about 19 μm.

27. An architectural aqueous coating composition that forms a paint film, said paint film is capable of resisting scuffing or chipping, wherein the architectural aqueous coating composition comprises:
a wax seeded latex, wherein the wax seeded latex comprises a hydrophobic, wax compound entrapped within a polymeric matrix,
an optional opacifying pigment,
a wax, wherein the wax makes up from about 0.25 wt. % to about 2.0 wt. % of the architectural aqueous coating composition, and
a coalescent aid, wherein the coalescent aid makes up from about 2.5 wt. % to about 5 wt. % of the architectural aqueous coating composition
wherein the wax has an average particle size (mV) from about 1 microns (μm) to about 25 μm.

28. The architectural aqueous coating composition accordingly to claim 27 , wherein the wax makes up from about 0.25 wt. % to about 1.75 wt. % of the architectural aqueous coating composition.

29. The architectural aqueous coating composition accordingly to claim 27 , wherein the coalescent aid makes up from about 2.8 wt. % to about 5 wt. % of the architectural aqueous coating composition.

30. The architectural aqueous coating composition according to claim 27 , wherein the wax has an average particle size (mV) from about 3 μm to about 22 μm.

31. The architectural aqueous coating composition according to claim 27 , wherein the wax has an average particle size (mV) from about 5 μm to about 20 μm.

32. The architectural aqueous coating composition according claim 27 , wherein the wax has an average particle sizes (mV) from about 6 to about 7.5 μm, from about 10 to about 13 μm, and/or from about 16 to about 19 μm.

Assignees

• Columbia Insurance Co

Inventors

• Dugan Jonathan
• Agens Ashlee
• Ament Ed
• Cooper Glenn
• Garcia Johanna
• Hood Jeff
• Lee Kevin
• O'Connor Kate
• Saad Rogina
• Saturne Marie
• Spillane Jeffrey T

Classifications

• C08F283/01

  on to unsaturated polyesters {(C08F283/004 takes precedence)} · CPC title

• C08F283/12

  on to polysiloxanes · CPC title

• C08F289/00

  Macromolecular compounds obtained by polymerising monomers on to macromolecular compounds not provided for in groups C08F251/00 - C08F287/00 · CPC title

• C09D5/00

  Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced {(electrically insulating plastics, resins or waxes H01B3/30)}; Filling pastes · CPC title

• C09D191/06

  Waxes · CPC title