Polyurethane hybrid system combining high compressive strength and early water resistance

Patent metadata

Field	Value
Publication number	US-11214517-B2
Application number	US-201816158586-A
Country	US
Kind code	B2
Filing date	Oct 12, 2018
Priority date	Apr 10, 2014
Publication date	Jan 4, 2022
Grant date	Jan 4, 2022

Abstract

The invention relates to the use of a multi-component composition comprising A) a polyol component (A) comprising at least one polyol and water, B) a hardener component (B) comprising at least one polyisocyanate, and C) a solid component (C) comprising a hydraulic binder and one or more aggregates, as an early water resistant construction or repair material for constructing, repairing or refurbishing component parts, wherein the mixed and applied multi-component composition is immersed in water not later than 8 hours, preferably not later than 2 h, after application.The use as an early water resistant construction or repair material is especially suitable for component parts, which are in contact with water during operation such as offshore wind energy plants or water retaining systems, e.g. pipelines.

First claim

The invention claimed is:

1. A method for constructing, repairing, or refurbishing at least one component part, the method comprising:
i) providing a multi-component composition consisting of:
A) a polyol component (A) comprising at least one polyol, water, and optionally at least one first additive that is selected from the group consisting of a plasticizer, a pigment, an adhesion promoter, a stabilizer against heat light and UV radiation, a thixotropic agent, a flow improving additive, a flame retardant, a defoamer, a wetting agent, a flow control agent, a deaerating agent, a biocide, and an emulsifier,
B) a hardener component (B) comprising at least one polyisocyanate, and optionally a solvent, and
C) a solid component (C) comprising a hydraulic binder, one or more aggregates that is selected from the group consisting of sand, slag, calcined flint, clay, pumice, perlite, and vermiculite, and optionally at least one second additive that is selected from the group consisting of a superplastizicer, an oil, cellulose fibers, a pigment, and lime,
wherein:
the polyol component (A), the hardener component (B), and the solid component (C) are separately provided, and
a content of the at least one polyisocyanate is in a range of 10 to 25% by weight, based on a total weight of the polyol component (A), the hardener component (B), and the solid component (C),

ii) mixing components (A), (B), and (C) of the multi-component composition to form a mixture,
iii) applying the mixture either on the component part to repair or refurbish the component part or in a space that is not in contact with water to form the component part, and
iv) immersing the applied mixture not earlier than 10 minutes and not later than 8 hours after the mixture is applied.

2. The method according to claim 1 , further comprising curing the applied mixture after the mixture is applied.

3. The method according to claim 2 , wherein at least part of the curing of the applied mixture is carried out underwater.

4. The method according to claim 1 , wherein the applied mixture is immersed in water not later than 4 hours after the mixture is applied.

5. The method according to claim 1 , wherein the applied mixture is immersed in water not later than 2 hours after the mixture is applied.

6. The method according to claim 1 , wherein the application of the mixture on the component part occurs when the component part is not in contact with water.

7. The method according to claim 1 , wherein the polyol component (A) comprises castor oil.

8. The method according to claim 7 , wherein in the polyol component (A):
an amount of the at least one polyol is in a range of from 35 to 55% by weight, based on a total content of component (A), and
an amount of the castor oil is in a range of from 33 to 45% by weight, based on the total content of component (A).

9. The method according to claim 1 , wherein the hardener component (B) comprises a methylene diphenyl diisocyanate.

10. The method according to claim 9 , wherein the polyol component (A) comprises castor oil.

11. The method according to claim 1 , wherein the hydraulic binder comprises cement or calcined paper sludge.

12. The method according to claim 1 , wherein the applying includes coating, flooring, grouting, or puttying the mixture.

13. The method according to claim 1 , wherein the mixture is a flooring material, a coating composition, a grout, or a putty.

14. The method according to claim 1 , wherein the component part is configured for offshore applications, pipeline repair, or lining applications.

15. The method according to claim 1 , wherein the component part is part of a wind energy plant, a water treatment plant, a dam, a sea wall, or a water retaining system.

16. The method according to claim 1 , wherein the component part is configured to be in contact with water in applications that require the component part to contact water.

17. The method according to claim 1 , wherein the method is configured for refurbishment, grouting, lock assembly, or tightening of bushings or joints.

Assignees

• Sika Tech Ag

Inventors

• Conrad Lars
• Bracht Kathrin
• Grötzinger Jochen

Classifications

• C04B26/16 Primary

  Polyurethanes · CPC title

• C04B28/003 Primary

  containing hybrid binders other than those of the polycarboxylate type · CPC title

• C04B2111/00543

  for wet surfaces · CPC title

• C04B2111/74

  Underwater applications · CPC title

• C04B28/04

  Portland cements · CPC title