Pre-mix useful in the manufacture of a fiber based product

Patent metadata

Field	Value
Publication number	US-11198973-B2
Application number	US-201716465426-A
Country	US
Kind code	B2
Filing date	Nov 30, 2017
Priority date	Dec 1, 2016
Publication date	Dec 14, 2021
Grant date	Dec 14, 2021

Abstract

The present invention relates to a process wherein microfibrillated cellulose (MFC) is mixed with at least two retention aids, selected from a cationic or amphoteric polymer and a microparticle or nanoparticle as a pre-mix before dosing it to the stock in a process for manufacture of a fiber based product.

First claim

The invention claimed is:

1. A process for the production of a fiber based product comprising the steps of:
preparing a pre-mix comprising:
a) microfibrillated cellulose, wherein the amount of the microfibrillated cellulose is 0.1 kg to 50 kg per ton dry furnish;
b) cationic or amphoteric polymer, wherein the amount of the cationic or amphoteric polymer is 0.01 kg to 10 kg per ton dry furnish;
c) microparticles or nanoparticles, wherein the amount of microparticles or nanoparticles is 0.01 kg to 10 kg per ton dry furnish, wherein said microparticles or nanoparticles are silica, microsilica, bentonite or microbentonite particles; and,
d) salt in an amount between 0.1 to 50% (wt/wt) based on a solids content of the pre-mix, wherein the salt is selected from a group consisting of sodium chloride, calcium chloride, magnesium chloride, and aluminum chloride; and,

dosing said pre-mix to a stock for manufacturing a fiber based product with a furnish comprising the stock.

2. The process according to claim 1 , wherein said microparticles or nanoparticles are anionic at neutral or alkaline pH.

3. The process according to claim 1 , wherein the weight ratio of polymer to microparticles or nanoparticles is in the range of from 1:3 to 1:20.

4. The process according to claim 1 , wherein said cationic or amphoteric polymer is a cationic polymer.

5. The process according to claim 4 , wherein said cationic polymer is selected from starch, polyaminoamide-epichlorohydrin and cationic polyacryl amide or copolymer thereof.

6. The process for the production of a fiber based product as claimed in claim 1 , wherein the pre-mix is prepared by co-refining or co-fluidizing the components of the pre-mix when manufacturing the microfibrillated cellulose.

7. The process according to claim 1 , wherein the weight ratio of polymer to microparticles or nanoparticles is in the range of from 1:5 to 1:12.

Assignees

• Stora Enso Oyj

Inventors

• Backfolk Kaj
• Heiskanen Isto
• Saukkonen Esa

Classifications

• D21H17/67

  Water-insoluble compounds, e.g. fillers, pigments · CPC title

• D21H17/20

  Macromolecular organic compounds · CPC title

• D21H17/68

  siliceous, e.g. clays · CPC title

• D21H17/29

  cationic · CPC title

• D21H17/74

  of organic and inorganic material · CPC title