Precursors of cathode materials for a rechargeable lithium ion battery

Patent metadata

Field	Value
Publication number	US-11189832-B2
Application number	US-201916568756-A
Country	US
Kind code	B2
Filing date	Sep 12, 2019
Priority date	Mar 8, 2017
Publication date	Nov 30, 2021
Grant date	Nov 30, 2021

Abstract

A method for manufacturing a cobalt based hydroxide carbonate compound having a malachite-rosasite mineral structure, comprising the steps of:providing an first aqueous solution comprising a source of Co,providing a second aqueous solution comprising Na2CO3,mixing both solutions in a precipitation reactor at a temperature above 70° C., thereby precipitating a cobalt based hydroxide carbonate compound whilst evacuating from the reactor any CO2 formed by the precipitation reaction, wherein the residence time of the compound in the reactor is between 1 and 4 hours, andrecovering the cobalt based hydroxide carbonate compound. The cobalt based hydroxide carbonate compound is used as a precursor of a lithium cobalt based oxide usable as an active positive electrode material in lithium ion batteries.

First claim

The invention claimed is:

1. A cobalt based hydroxide carbonate compound, having a crystal structure and the general formula [Co 1−a A a ] 2 (OH) 2 CO 3 , A being one or more of Ni, Mn, Al, Ti, Zr and Mg, with a≤0.05, wherein A is distributed in the crystal structure of the cobalt based hydroxide carbonate compound.

2. The cobalt based hydroxide carbonate compound of claim 1 , further comprising Na as an impurity of up to 0.3 wt %.

3. The cobalt based hydroxide carbonate compound of claim 1 , having a particle size distribution with D50 between 15 and 25 μm and a span <0.80.

4. The cobalt based hydroxide carbonate compound of claim 1 , wherein the compound has a spherical morphology and a tap density >1.8 g/cm 3 .

5. The cobalt based hydroxide carbonate compound of claim 1 , wherein A is one or both of Al and Mg, with 0.002≤a≤0.020, and wherein one or both of Al and Mg is homogeneously doped in the compound.

6. A Li-containing cathode active material powder prepared from a cobalt based hydroxide carbonate compound, having the general formula [Co 1−a A a ] 2 (OH) 2 CO 3 , A being one or more of Ni, Mn, Al, Ti, Zr and Mg, with a≤0.05.

7. A method for manufacturing a cobalt based hydroxide carbonate compound, having a crystal structure and the general formula [Co 1−a A a ] 2 (OH) 2 CO 3 , A being one or more of Ni, Mn, Al, Ti, Zr and Mg, with a≤0.05, wherein A is distributed in the crystal structure of the cobalt based hydroxide carbonate compound, the method comprising the steps of:
providing a first aqueous solution comprising a source of Co,
providing a second aqueous solution comprising Na 2 CO 3 ,
mixing both solutions in a precipitation reactor at a temperature above 70° C., thereby precipitating a cobalt based hydroxide carbonate compound whilst evacuating from the reactor any CO 2 formed by the precipitation reaction, wherein the residence time of the compound in the reactor is between 1 and 4 hours, and
recovering the cobalt based hydroxide carbonate compound.

8. The method according to claim 1 , wherein the second aqueous solution comprises:
a solution of at least 2N Na 2 CO 3 , or
a solution comprising between 0.5 and 3 mol/L of Na 2 CO 3 and between 1 and 6 mol/L NaOH, wherein the Na content in the Na 2 CO 3 is as high or higher than twice the Na content in the NaOH.

9. The method according to claim 1 , wherein the first aqueous solution further comprises a source of one or more of Ni, Mn, Al, Mg and Ti.

10. The method according to claim 1 , wherein the first solution comprising a source of Co comprises CoSO 4 , and further comprises one or more of MgSO 4 , Al 2 (SO 4 ) 3 , NiSO 4 and MnSO 4 , wherein one or more of Mg, Al, Ni and Mn are present in a molar ratio versus the Co content of between 0.2 and 5 mol %.

11. The method according to claim 1 , wherein during the step of mixing both solutions a nanometric powder comprising one or more of TiO 2 , MgO or Al 2 O 3 is added.

12. The method according to claim 1 , further comprising, after the precipitating step, transferring the compound from the precipitating reactor to a settlement reactor coupled to the precipitating reactor, wherein a solid precipitate of the compound settles to the bottom of the settlement reactor, and whereafter the settled solid precipitate of the compound is recirculated to the precipitation reactor.

13. A method for manufacturing a lithiated cobalt based oxide, comprising the steps of claim 1 , and subsequently additionally comprising the steps of:
mixing the cobalt based hydroxide carbonate compound with a source of Li, and
sintering the mixture at a temperature above 950° C. in an oxygen containing atmosphere.

14. The method according to claim 13 , wherein the precipitated cobalt based hydroxide carbonate compound comprises Na as an impurity between 0.1 and 0.3 wt %, and wherein either:
during the step of mixing the cobalt based hydroxide carbonate compound with the source of Li, or
during the step of sintering the mixture;

adding a sulfate compound, whereby the molar quantity of SO 4 is equal to or higher than the molar content of Na, and subsequently comprising the step of washing the lithiated cobalt based oxide with water, and drying the lithiated cobalt based oxide.

15. The method according to claim 14 , wherein the sulfate compound is one of Li 2 SO 4 , NaHSO 4 , CoSO 4 and Na 2 S 2 O 8 .

Assignees

• Umicore Nv
• Umicore Korea Ltd

Inventors

• Kim Dae-Hyun
• Paulsen Jens
• Oh Jindoo
• Blangero Maxime

Classifications

• C01P2006/11

  Powder tap density · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title

• C01G51/82

  Compounds containing cobalt, with or without oxygen or hydrogen, and containing two or more other elements · CPC title

• H01M10/052

  Li-accumulators · CPC title

• C01P2002/85

  by XPS, EDX or EDAX data · CPC title