Polyolefin material having a low density

Patent metadata

Field	Value
Publication number	US-11155688-B2
Application number	US-201414895054-A
Country	US
Kind code	B2
Filing date	Jun 6, 2014
Priority date	Jun 12, 2013
Publication date	Oct 26, 2021
Grant date	Oct 26, 2021

Abstract

A polyolefin material that is formed by solid state drawing of a thermoplastic composition containing a continuous phase that includes a polyolefin matrix polymer and nanoinclusion additive is provided. The nanoinclusion additive is dispersed within the continuous phase as discrete nano-scale phase domains. When drawn, the nano-scale phase domains are able to interact with the matrix in a unique manner to create a network of nanopores.

First claim

What is claimed is:

1. A polyolefin material that is formed by drawing of a thermoplastic composition, wherein the thermoplastic composition contains a continuous phase that includes a polyolefin matrix polymer and a polymeric nanoinclusion additive and a polymeric microinclusion additive dispersed within the continuous phase in the form of discrete domains,
wherein the polymeric nanoinclusion additive is in the form of nano-scale domains and the polymeric microinclusion additive is in the form of micro-scale domains,
wherein the polymeric nanoinclusion additive constitutes from about 0.05 wt % to about 20 wt. % of the composition, based on the weight of the continuous phase; and
wherein the polymeric microinclusion additive constitutes from about 1 wt % to about 20 wt % of the composition, based on the weight of the continuous phase;
wherein a porous network is defined in the drawn thermoplastic composition that includes a plurality of micropores, and a plurality of nanopores adjacent to the nano-scale domains and/or the micro-scale domains, the nanopores having an average cross-sectional dimension of about 800 nanometers or less, the drawn thermoplastic composition having a density of about 0.90 g/cm 3 or less;
wherein the polyolefin material exhibits a hydrohead value of about 50 centimeters or more and a water vapor transmission rate of about 300 g/m 2 -24 hours or more.

2. The polyolefin material of claim 1 , wherein the nanopores have an average cross-sectional dimension of from about 5 to about 700 nanometers.

3. The polyolefin material of claim 1 , wherein nanopores have an average axial dimension of from about 100 to about 5000 nanometers.

4. The polyolefin material of claim 1 , wherein the polyolefin matrix polymer has a melt flow rate of from about 0.5 to about 80 grams per 10 minutes as determined at a load of 2160 grams and at 230° C. in accordance with ASTM D1238.

5. The polyolefin material of claim 1 , wherein the polyolefin matrix polymer is a propylene homopolymer, propylene/α-olefin copolymer, ethylene/α-olefin copolymer, or a combination thereof.

6. The polyolefin material of claim 1 , wherein the polyolefin matrix polymer is a substantially isotactic polypropylene homopolymer or a copolymer containing at least about 90% by weight propylene.

7. The polyolefin material of claim 1 , wherein the continuous phase constitutes from about 60 wt. % to about 99 wt. % of the thermoplastic composition.

8. The polyolefin material of claim 1 , wherein the polymeric nanoinclusion additive has a nonpolar component and a polar component.

9. The polyolefin material of claim 8 , wherein the polymeric nanoinclusion additive is a functionalized polyolefin.

10. The polyolefin material of claim 9 , wherein the functionalized polyolefin is a polyepoxide.

11. The polyolefin material of claim 8 , wherein the polymeric nanoinclusion additive has melt flow rate of from about 0.1 to about 100 grams per 10 minutes, determined at a load of 2160 grams and at a temperature at least about 40° C. above the melting temperature in accordance with ASTM D1238.

12. The polyolefin material of claim 8 , wherein the ratio of the melt flow rate of the polyolefin to the melt flow rate of the polymeric nanoinclusion additive is from about 0.2 to about 8.

13. The polyolefin material of claim 1 , wherein the nano-scale domains have an average cross-sectional dimension of from about 1 nanometer to about 1000 nanometers.

14. The polyolefin material of claim 1 , wherein the polymeric microinclusion additive is polylactic acid.

15. The polyolefin material of claim 1 , wherein the polymeric microinclusion additive has a glass transition temperature of about 0° C. or more.

16. The polyolefin material of claim 1 , wherein the polymeric microinclusion additive has a melt flow rate of from about 5 to about 200 grams per 10 minutes, determined at a load of 2160 grams and at a temperature of 210° C.

17. The polyolefin material of claim 1 , wherein the ratio of the melt flow rate of the polymeric microinclusion additive to the melt flow rate of the polyolefin matrix polymer is from about 0.5 to about 10.

18. The polyolefin material of claim 1 , wherein the ratio of the Young's modulus elasticity of the polyolefin matrix polymer to the Young's modulus of elasticity of the polymeric microinclusion additive is from about 1 to about 250.

19. The polyolefin material of claim 1 , wherein the micro-scale domains have an average axial dimension of from about 1 micrometer to about 400 micrometers.

20. The polyolefin material of claim 1 , wherein the thermoplastic composition further comprises an interphase modifier.

21. The polyolefin material of claim 1 , wherein the porous network is distributed in a substantially homogeneous fashion throughout the composition.

22. The polyolefin material of claim 1 , wherein the nanopores are distributed in generally parallel columns.

23. The polyolefin material of claim 1 , wherein the total pore volume of the polyolefin material is from about 15% to about 80%.

24. The polyolefin material of claim 1 , wherein nanopores constitute about 20 vol. % or more of the total pore volume of the polyolefin material.

25. The polyolefin material of claim 1 , wherein the drawn thermoplastic composition has a density of about 0.85 g/cm 3 or less.

26. The polyolefin material of claim 1 , wherein the thermoplastic composition is generally free of blowing agents.

27. The polyolefin material of claim 1 , wherein the thermoplastic composition is generally free of pore-initiating inorganic oxide fillers.

28. A method for forming a polyolefin material, the method comprising:
forming a thermoplastic composition that contains a continuous phase that includes a polyolefin matrix polymer and a polymeric nanoinclusion additive and a polymeric microinclusion additive dispersed within the continuous phase in the form of discrete domains, wherein the polymeric nanoinclusion additive is in the form of nano-scale domains and the polymeric microinclusion additive is in the form of micro-scale domains, wherein the polymeric nanoinclusion additive constitutes from about 0.05 wt % to about 20 wt. % of the composition, based on the weight of the continuous phase, and the polymeric microinclusion additive constitutes from about 1 wt % to about 20 wt % of the composition, based on the weight of the continuous phase; and
solid state drawing the thermoplastic composition, wherein a porous network is defined in the drawn thermoplastic composition that includes a plurality of micropores, and a plurality of nanopores adjacent to the nano-scale domains and/or the micro-scale domains, the nanopores having an average cross-sectional dimension of about 800 nanometers or less, the drawn thermoplastic composition having a density of about 0.90 g/cm 3 or less;
wherein the polyolefin material exhibits a hydrohead value of about 50 centimeters or more and a water vapor transmission rate of about 300 g/m 2 -24 hours or more.

29. The method of claim 28 , wherein the thermoplastic composition is stretched to a draw ratio of from about 1.1 to about 3.0.

30. The polyolefin material of claim 1 , wherein the plurality of nanopores have an aspect ratio of from about 1 to about 30.

31. The polyolefin material of claim 1 , wherein the axial dimension of the micropores is

Assignees

• Kimberly Clark Co

Inventors

• Topolkaraev Vasily A
• Mceneany Ryan J
• Carrillo Antonio J

Classifications

• B01D71/262

  Polypropylene · CPC title

• A61F13/53

  characterised by the absorbing medium (A61F13/20 takes precedence) · CPC title

• B01D67/0027 Primary

  by stretching · CPC title

• A61L15/225

  Mixtures of macromolecular compounds · CPC title

• A61F2013/530233

  being thermoplastic fibres · CPC title