Laminate, sliding member, and method for manufacturing laminate

Patent metadata

Field	Value
Publication number	US-11148195-B2
Application number	US-201816482628-A
Country	US
Kind code	B2
Filing date	Feb 2, 2018
Priority date	Feb 3, 2017
Publication date	Oct 19, 2021
Grant date	Oct 19, 2021

Abstract

A laminate includes a base substrate, and a coating layer formed on the base substrate. The coating layer includes a copper alloy portions derived from precipitation-hardening copper alloy particles and hard particle portions which are harder than the copper alloy portions, the hard particle portions are derived from hard particles, and the parts bond with each other via an interface. Each of the hard particle portions has a non-spherical shape.A sliding member includes the laminate in at least one sliding portion.A method for manufacturing a laminate includes a step of spraying a mixture in a non-molten state including precipitation-hardening copper alloy particles and hard particles having a non-spherical shape and being harder than the copper alloy particles onto a base substrate, to form a coating layer on the base substrate.

First claim

The invention claimed is:

1. A laminate comprising:
a base substrate; and
a coating layer formed on the base substrate;
wherein the coating layer includes copper alloy portions derived from precipitation-hardening copper alloy particles and hard particle portions which are harder than the copper alloy portions;
the hard particle portions are derived from hard particles;
the portions bond with each other via an interface;
each of the hard particle portions has a non-spherical shape;
an aspect ratio of the hard particle portions is 1.3 or more in a median value; and
an average particle size of the copper alloy particles and the hard particles are within a range of 15.8 μm to 40 μm.

2. The laminate according to claim 1 , wherein the hard particle portions comprise at least one type of hard particle selected from the group consisting of: iron-based alloy particles, cobalt-based alloy particles, chromium-based alloy particles, nickel-based alloy particles, molybdenum-based alloy particles, or ceramic-based particles.

3. The laminate according to claim 1 , wherein a proportion of the hard particle portions in a cross section of the coating layer is 1 area % to 50 area %.

4. The laminate according to claim 1 , wherein the copper alloy portions contain nickel and silicon as additive elements.

5. The laminate according to claim 4 , wherein each of the copper alloy portions further contains, as an additive element, at least one type of element selected from the group consisting of: chromium, zirconium, or vanadium.

6. The laminate according to claim 1 , wherein at least one of the base substrate and the coating layer comprises at least one plastically deformed portion.

7. The laminate according to claim 1 , wherein a porosity in a cross section of the coating layer is 3 area % or less.

8. The laminate according to claim 1 , comprising at least one intermediate layer formed at least partially between the base substrate and the coating layer, and the aforementioned at least one intermediate layer includes at least one of at least one diffusion layer or at least one intermetallic compound layer.

9. The laminate according to claim 1 , wherein a proportion of the hard particle portions in a cross section of the coating layer is 5.3 area % to 50 area %.

10. A sliding member comprising a laminate at a sliding portion, the laminate comprising;
a base substrate; and
a coating layer formed on the base substrate;
wherein the coating layer includes copper alloy portions derived from precipitation-hardening copper alloy particles and hard particle portions which are harder than the copper alloy portions;
the hard particle portions are derived from hard particles;
the portions bond with each other via an interface;
each of the hard particle portions has a non-spherical shape;
an aspect ratio of the hard particle portions is 1.3 or more in a median value; and
an average particle size of the copper alloy particles and the hard particles are within a range of 15.8 μm to 40 μm.

11. A method for manufacturing a laminate, the laminate comprising a base substrate and a coating layer formed on the base substrate, wherein the coating layer includes copper alloy portions derived from precipitation-hardening copper alloy particles and hard particle portions which are harder than the copper alloy portions, the hard particle portions are derived from hard particles, the portions bond with each other via an interface, each of the hard particle portions has a non-spherical shape, an aspect ratio of the hard particle portions is 1.3 or more in a median value, and an average particle size of the copper alloy particles and the hard particles are within a range of 15.8 μm to 40 μm the method comprising:
a step of spraying a mixture in a non-molten state including precipitation-hardening copper alloy particles and hard particles having a non-spherical shape, and being harder than the copper alloy particles, onto a base substrate to form a coating layer on the base substrate.

12. The method for manufacturing the laminate according to claim 11 , wherein the hard particles comprise at least one type of hard particle selected from the group consisting of iron-based alloy particles, cobalt-based alloy particles, chromium-based alloy particles, nickel-based alloy particles, molybdenum-based alloy particles or ceramic-based particles.

13. The method for manufacturing the laminate according to claim 11 , wherein, when the mixture is sprayed onto the base substrate, the mixture is sprayed onto the base substrate at such a speed that makes the copper alloy particles be sprayed onto the base substrate to form at least one plastically deformed portion in at least one of the base substrate or the coating layer.

14. The method for manufacturing the laminate according to claim 11 , wherein each of the copper alloy particles is in a supersaturated solid solution state.

15. The method for manufacturing the laminate according to claim 11 , wherein each of the copper alloy particles is a rapid solidified particle.

16. The method for manufacturing the laminate according to claim 11 , wherein each of the hard particles is a particle manufactured by water atomization.

17. The method for manufacturing the laminate according to claim 11 , wherein a grain size of the copper alloy particles and a grain size of the hard particles are equal to or less than 150 μm.

18. The method for manufacturing the laminate according to claim 11 , wherein a grain size of the copper alloy particles and a grain size of the hard particles are 75 μm or less.

19. The method for manufacturing the laminate according to claim 11 , wherein an average particle size of the copper alloy particles is smaller than an average particle size of the hard particles.

Assignees

• Nissan Motor
• Fukuda Metal Foil & Powder Co Ltd

Inventors

• Izawa Yoshinori
• Arai Junichi
• Mabuchi Yutaka
• Otobe Katsunori
• Nishimura Shinichi

Classifications

• B22F1/12

  Metallic powder containing non-metallic particles (containing lubricating or binding agents or organic material B22F1/10) · CPC title

• B22F1/09

  Mixtures of metallic powders · CPC title

• B32B15/017

  one layer being formed of aluminium or an aluminium alloy, another layer being formed of an alloy based on a non ferrous metal other than aluminium · CPC title

• B22F7/08

  with one or more parts not made from powder {(B22F7/062 takes precedence)} · CPC title

• B22F7/06

  of composite workpieces or articles from parts, e.g. to form tipped tools {(B22F7/002 takes precedence)} · CPC title