Alkaline cell with improved discharge efficiency

Patent metadata

Field	Value
Publication number	US-11133497-B2
Application number	US-201615573427-A
Country	US
Kind code	B2
Filing date	May 12, 2016
Priority date	May 13, 2015
Publication date	Sep 28, 2021
Grant date	Sep 28, 2021

Abstract

A gelled anode for an alkaline electrochemical cell contains zinc-based particles, an alkaline electrolyte, a gelling agent, and two or more additives selected from the group consisting of an alkali metal hydroxide, an organic phosphate ester surfactant, a metal oxide, and tin, which as reduced cell gassing properties relative to cells lacking such additives.

First claim

What is claimed is:

1. A gelled anode for a primary alkaline electrochemical cell, the anode comprising:
zinc-based particles, an alkaline electrolyte comprising potassium hydroxide or sodium hydroxide, a gelling agent, lithium hydroxide, and tin metal powder; wherein lithium hydroxide is present at a concentration from about 0.005 wt % to about 5 wt % relative to the total weight of the gelled anode; and wherein tin metal powder is present at a concentration of from about 0.0001 wt % to about 0.15 wt % relative to the total weight of the gelled anode.

2. The gelled anode of claim 1 , further comprising a phosphate ester surfactant selected from the group consisting of poly(oxy-1,2-ethanediyl)-α-(dinonylphenyl)-ω-hydroxy-phosphate, polyoxyethylene tridecyl ether phosphate, poly(oxy-1,2-ethanediyl)-α-hydro-ω-hydroxy-C 8-10 -alkyl ether phosphate, polyoxyethylene isotridecyl phosphate, polyoxypropylene polyoxyethylene cetyl ether, C 10 -C 14 alcohol ethoxylate phosphate ester, tridecyl alcohol ethoxylate phosphate ester, and nonylphenol ethoxylate phosphate ester.

3. The gelled anode of claim 1 , wherein relative to the total weight of the gelled anode, the lithium hydroxide is present at a concentration from about 0.02 wt % to about 0.2 wt %, cerium oxide is present at a concentration from about 0.05 wt % to about 0.2 wt %, phosphate ester surfactant is present at a concentration from about 0.001 wt % to about 0.015 wt %, and the tin metal powder is present at a concentration of from about 0.05 wt % to about 0.15 wt %.

4. The gelled anode of claim 1 , wherein the zinc-based particles are zinc alloy particles comprising about 100 ppm to about 280 ppm of bismuth, and about 100 ppm to about 280 ppm of indium.

5. The gelled anode of claim 4 , wherein from about 20% to about 50%, of the zinc alloy, by weight relative to a total weight of zinc alloy, has a particle size of less than about 75 micrometers.

6. The gelled anode of claim 4 , wherein about 20% to about 40% of the zinc alloy, by weight relative to the total weight of zinc alloy, has a particle size of less than about 75 micrometers, and about 8% to about 20% of the zinc alloy, by weight relative to the total weight of zinc alloy, has a particle size of greater than about 150 micrometers.

7. The gelled anode of claim 1 , wherein the alkaline electrolyte comprises potassium hydroxide.

8. The gelled anode of claim 1 , wherein the alkaline electrolyte comprises potassium hydroxide at a concentration of less than about 40%.

9. A primary alkaline electrochemical cell comprising:
a positive current collector;
a cathode in contact with the positive current collector;
a gelled anode comprising zinc-based particles, an alkaline electrolyte comprising potassium hydroxide or sodium hydroxide, a gelling agent, lithium hydroxide, and tin metal powder;
a separator between the cathode and the anode; and
a negative current collector in electrical contact with the anode;
wherein lithium hydroxide is present at a concentration from about 0.005 wt % to about 5 wt % relative to the total weight of the gelled anode; and
wherein tin metal powder is present at a concentration of from about 0.0001 wt % to about 0.15 wt % relative to the total weight of the gelled anode.

10. The primary alkaline electrochemical cell of claim 9 , wherein the alkaline electrolyte comprises potassium hydroxide.

11. The primary alkaline electrochemical cell of claim 9 , wherein the gelled anode further comprises poly(oxy-1,2-ethanediyl)-a-(dinonylphenyl)-ω-hydroxyphosphate.

12. The primary alkaline electrochemical cell of claim 9 , wherein the zinc-based particles are zinc alloy particles.

13. The primary alkaline electrochemical cell of claim 12 , wherein the zinc alloy comprises:
about 100 ppm to about 280 ppm of bismuth; and
about 100 ppm to about 280 ppm of indium.

14. The primary alkaline electrochemical cell of claim 13 , wherein from about 20% to about 50% of the zinc alloy, by weight relative to a total weight of zinc alloy, has a particle size of less than about 75 micrometers.

15. The primary alkaline electrochemical cell of claim 14 , wherein about 20% to about 40% of the zinc alloy, by weight relative to the total weight of zinc alloy, has a particle size of less than about 75 micrometers, and about 8% to about 20% of the zinc alloy, by weight relative to the total weight of zinc alloy, has a particle size of greater than about 150 micrometers.

16. The primary alkaline electrochemical cell of claim 9 , wherein the alkaline electrolyte comprises potassium hydroxide at a concentration of less than about 40%.

Assignees

• Energizer Brands Llc

Inventors

• Armacanqui M Edgar
• Li Wen
• Crowe Donald Raymond
• Roszkowski Andrew J
• Hadley John
• Rose Janna

Classifications

• H01M6/085

  of the reversed type, i.e. anode in the centre · CPC title

• H01M6/06

  Dry cells, i.e. cells wherein the electrolyte is rendered non-fluid · CPC title

• H01M4/62 Primary

  Selection of inactive substances as ingredients for active masses, e.g. binders, fillers · CPC title

• H01M4/42

  Alloys based on zinc · CPC title

• H01M4/06 Primary

  Electrodes for primary cells · CPC title