Metal pretreatment composition containing zirconium, copper, zinc and nitrate and related coatings on metal substrates

Patent metadata

Field	Value
Publication number	US-11131027-B2
Application number	US-201815961262-A
Country	US
Kind code	B2
Filing date	Apr 24, 2018
Priority date	Dec 28, 2009
Publication date	Sep 28, 2021
Grant date	Sep 28, 2021

Abstract

A pretreatment composition for metal that provides enhanced corrosion resistance, enhanced paint adhesion and reduced chip damage to a wide variety of metal substrates. The pretreatment is also cleaner because it is based on zirconium rather than zinc phosphates. The pretreatment coating composition in use preferably comprises 50 to 300 parts per million (ppm) zirconium, 0 to 100 ppm of SiO 2 , 150-2000 ppm of total fluorine and 10-100 ppm of free fluorine, 150 to 10000 ppm of zinc and 10 to 10000 ppm of an oxidizing agent and has a pH of 3.0 to 5.0, preferably about 4.0. The coating composition can optionally include 0 to 50 ppm of copper. The suitable oxidizing agents can be selected from a large group.

First claim

What is claimed is:

1. A metal pretreatment coating composition comprising the following components: 50 to 300 ppm of zirconium; 10 to 50 ppm of copper; 10 to 100 ppm of SiO 2 ; 150 to 2000 ppm total fluorine; 10 to 100 ppm free fluorine; 600 to 7900 ppm zinc; and 10 to 10,000 ppm of an oxidizing agent; and having an acidic pH; wherein at least one oxidizing agent is nitrate, present in an amount of from 600 to 10,000 ppm and said components are selected such that the coating composition is capable of depositing an amount of zirconium and a coating thickness that are both less than an otherwise identical coating composition that is devoid of zinc under the same process conditions.

2. The metal pretreatment coating composition according to claim 1 comprising 75 to 300 ppm of zirconium, 10 to 40 ppm of copper and 20 to 100 ppm of SiO 2 .

3. The metal pretreatment coating composition according to claim 1 wherein said oxidizing agent comprises at least one of a nitrite ion or salt, an inorganic peroxide, a permanganate ion or salt, a persulfate ion or salt, a perborate ion or salt, a chlorate ion or salt, a hypochlorite ion or salt, a vanadate ion or salt, a vanadyl ion or salt, a ceric ion or salt, a tungstate ion or salt, a stannic ion or salt, a hydroxylamine, a nitro-compound, an amine oxide, hydrogen peroxide, or a mixture thereof.

4. The metal pretreatment coating composition according to claim 3 wherein said oxidizing agent comprises at least one of ammonium nitrate, sodium nitrate, potassium nitrate, sodium nitrite, sodium peroxide, potassium permanganate, sodium persulfate, sodium perborate, sodium chlorate, sodium hypochlorite, sodium vanadate, vanadyl sulfate, ceric sulfate, ceric ammonium sulfate, ceric ammonium nitrate, sodium tungstate, stannic fluoride, hydroxylamine, hydroxylamine sulfate, sodium nitrobenzene sulfonate, sodium m-nitrobenzene sulfonate, and N-methylmorpholine N-oxide.

5. The metal pretreatment coating composition according to claim 3 wherein said oxidizing agent comprises hydrogen peroxide present in an amount of from 10 to 30 ppm.

6. The metal pretreatment coating composition according to claim 1 having a pH of about 3.0 to about 5.0.

7. The metal pretreatment coating composition according to claim 1 wherein said oxidizing agent comprises hydrogen peroxide present in an amount of from 10 to 30 ppm and has a pH of about 3.5 to about 4.5.

8. The metal pretreatment coating composition according to claim 1 wherein said oxidizing agent further comprises an ion or salt of sulfate present in an amount of from 600 to 10000 ppm.

9. The metal pretreatment coating composition according to claim 1 wherein Zn is present in an amount of 900 ppm or more and the oxidizing agent is present in an amount greater than 5000 ppm.

10. The metal pretreatment coating composition according to claim 1 wherein zinc is present in an amount greater than 5000 ppm and the oxidizing agent also contains hydrogen peroxide.

11. The metal pretreatment coating composition according to claim 1 wherein the composition comprises 50-300 ppm of zirconium, 10-50 ppm of copper, 10-100 ppm SiO 2 , 150-2000 ppm total fluorine, 10-100 ppm free fluorine, 1200 to 4800 ppm zinc, and 3000 to 10,000 ppm nitrate.

12. The metal pretreatment coating composition according to claim 1 wherein the composition comprises 100-200 ppm Zr, 10-40 ppm Cu, 10-100 ppm SiO 2 , 150-1100 total fluorine, 10-100 ppm free fluorine, 900-5000 ppm Zn, and 2000-10,000 ppm nitrate.

13. The metal pretreatment coating composition according to claim 1 wherein zinc is present in an amount of from 600 to 4800 ppm.

14. The metal pretreatment coating composition according to claim 1 wherein the pretreatment composition contains only further metal ions selected from the group consisting of sodium, potassium, tin, vanadium and cerium.

15. The metal pretreatment coating composition according claim 1 , wherein zinc is present in an amount of from 600 to 4800 ppm and the oxidizing agent is present in an amount of 900 to 7000 ppm.

16. The metal pretreatment coating composition according to claim 1 , wherein zinc is present in an amount of from 600 to 3000 ppm.

17. The metal pretreatment coating composition according claim 1 , wherein zinc is present in an amount of from 600 to 2400 ppm.

18. The metal pretreatment coating composition according claim 1 , wherein zinc is present in an amount of from 900 to 3000 ppm.

19. The metal pretreatment coating composition according claim 1 , wherein zinc is present in an amount of from 900 to 2700 ppm.

20. The metal pretreatment coating composition according claim 1 , wherein the nitrate is present in an amount of from 1,000 to 10,000 ppm.

21. The metal pretreatment coating composition according claim 1 , wherein the nitrate is present in an amount of from 5500 to 10,000 ppm.

22. A metal pretreatment coating composition consisting of: 50 to 300 ppm of zirconium, 10 to 50 ppm of copper, 10 to 100 ppm of SiO 2 , 150 to 2000 ppm total fluorine, 10 to 100 ppm free fluorine, 600 to 7900 ppm zinc, and 10 to 10,000 ppm of an oxidizing agent.

23. The metal pretreatment coating composition according to claim 22 wherein hydrogen peroxide is present as an oxidizing agent in an amount of from 10 to 100 ppm.

24. A metal pretreatment coating composition comprising: 50 to 300 ppm of zirconium, 10 to 50 ppm of copper, 10 to 100 ppm of SiO 2 , 150 to 2000 ppm total fluorine, 10 to 100 ppm free fluorine, 600 to 7900 ppm zinc, and 10 to 10000 ppm of an oxidizing agent, and wherein the pretreatment composition contains only further metal ions selected from the group consisting of sodium, potassium, tin, vanadium and cerium, wherein said components are selected such that the coating composition is capable of depositing an amount of zirconium and a coating thickness on a metal substrate that are both less than an otherwise identical coating composition that is devoid of zinc under the same process conditions.

25. The metal pretreatment coating composition according to claim 24 wherein zinc is present in an amount of from 600 to 4800 ppm.

26. The metal pretreatment coating composition according to claim 24 , wherein zinc is present in an amount of from 600 to 3000 ppm.

27. The metal pretreatment coating composition according claim 24 , wherein zinc is present in an amount of from 600 to 2400 ppm.

28. The metal pretreatment coating composition according claim 24 , wherein zinc is present in an amount of from 900 to 3000 ppm.

29. The metal pretreatment coating composition according claim 24 , wherein zinc is present in an amount of from 900 to 2700 ppm.

30. The metal pretreatment coating composition according to claim 24 , wherein said oxidizing agent comprises at least one of a nitrite ion or salt, an inorganic peroxide, a persulfate ion or salt, a perborate ion or salt, a chlorate ion or salt, a hypochlorite ion or salt, a vanadate ion or salt, a vanadyl ion or salt, a ceric ion or salt, a stannic ion or salt, a hydroxylamine, a nitro-compound, an amine oxide, or a mixture thereof.

31. The metal pretreatment coating composition according claim 24 , wherein at least one oxidizing agent is nitrate, present in an amount of from 600 to 10,000 ppm.

32. The metal pretreatment coating composition according claim 24 , wherein said oxidizin

Assignees

• Henkel Ag & Co Kgaa

Inventors

• Vonk Donald
• Kapic Edis
• Goodreau Bruce
• Bobadilla Alvaro

Classifications

• C23C22/34 Primary

  containing fluorides or complex fluorides · CPC title

• Y10T428/12139

  Nonmetal particles in particulate component · CPC title

• C23C22/78

  Pretreatment of the material to be coated · CPC title

• C23C22/80 Primary

  with solutions containing titanium or zirconium compounds · CPC title

• C23C22/06

  using aqueous acidic solutions with pH less than 6 · CPC title