Friction stir welding tool member, friction stir welding apparatus using the same, and friction stir welding method

Patent metadata

Field	Value
Publication number	US-11130194-B2
Application number	US-201716324110-A
Country	US
Kind code	B2
Filing date	Aug 4, 2017
Priority date	Aug 9, 2016
Publication date	Sep 28, 2021
Grant date	Sep 28, 2021

Abstract

The friction stir welding tool member according to the present invention is made of a ceramic member in which a shoulder portion and a probe portion are integrally formed, wherein a root portion of the probe portion and an end portion of the shoulder portion have a curved surface shape; and the friction stir welding tool member has a ratio (R1/D) of 0.02 or more and 0.20 or less when a curvature radius of the end portion of the shoulder portion is defined as R1 (mm) and an outer diameter of the shoulder portion is defined as D (mm). In addition, the ceramic member is preferably made of a silicon nitride sintered body having a Vickers hardness of 1400 HV1 or more. According to the above-described configuration, a friction stir welding tool member having excellent durability can be provided.

First claim

The invention claimed is:

1. A friction stir welding tool member made of a ceramic member in which a shoulder portion and a probe portion are integrally formed,
a root portion of the probe portion and an end portion of the shoulder portion have a curved surface shape,
the friction stir welding tool member has a ratio (R1/D) of 0.02 or more and 0.20 or less, when a curvature radius of the end portion of the shoulder portion is defined as R1 (mm) and an outer diameter of the shoulder portion is defined as D (mm),
the ceramic member is a silicon nitride sintered body having an area ratio (%) of 60% or more of silicon nitride crystal particles having an aspect ratio of 2 or more per unit area of 50 μm×50 μm,
the silicon nitride sintered body contains, by mass, 15% or less of additive components other than silicon nitride in such a manner that the additive components include at least three elements selected from Y, a lanthanoid element, Al, Mg, Si, Ti, Hf, Mo, and C, and
an inclination angle (θ) of an inclined surface with respect to a direction perpendicular to an axis of the probe portion is: (i) larger than 0° and equal to or less than 10°, or (ii) equal to or larger than −10° and less than 0°, the inclined surface being provided from the end portion of the shoulder portion to the root portion of the probe portion.

2. The friction stir welding tool member according to claim 1 , wherein the ceramic member is made of a silicon nitride sintered body having a Vickers hardness of 1400 HV1 or more.

3. The friction stir welding tool member according to claim 1 , wherein a curvature radius R2 (mm) of the root of the probe portion is 0.1 mm or more.

4. The friction stir welding tool member according to claim 1 , wherein the inclination angle θ of the inclined surface with respect to a direction perpendicular to an axis of the probe portion is equal to or larger than −10° and less than 0°.

5. The friction stir welding tool member according to claim 1 , wherein a tip portion of the probe portion has a curved surface shape.

6. The friction stir welding tool member according to claim 1 , wherein a surface roughness Ra of a curved surface portion formed at the end portion of the shoulder portion is 10 μm or less.

7. A friction stir welding apparatus equipped with the friction stir welding tool member according to claim 1 .

8. A friction stir welding method in which the friction stir welding apparatus according to claim 7 is used, the friction stir welding method comprising:
superimposing two or more materials to be welded each other; and
pressing the friction stir welding tool member against the materials to be welded while the friction stir welding tool member is being rotated at a rotation speed of 300 rpm or more.

9. The friction stir welding method according to claim 8 , wherein the materials to be welded are steel.

10. The friction stir welding tool member according to claim 1 , wherein:
a curvature radius R2 (mm) of the root of the probe portion is 0.1 mm or more.

11. The friction stir welding tool member according to claim 1 , wherein:
the ceramic member is made of a silicon nitride sintered body having a Vickers hardness of 1400 HV1 or more; and
a curvature radius R2 (mm) of the root of the probe portion is 0.1 mm or more.

12. The friction stir welding tool member according to claim 1 , wherein:
a surface roughness Ra of a curved surface portion formed at the end portion of the shoulder portion is 10 μm or less; and
a curvature radius R2 (mm) of the root of the probe portion is 0.1 mm or more.

Assignees

• Univ Osaka
• Toshiba Materials Co Ltd

Inventors

• Fujii Hidetoshi
• Morisada Yoshiaki
• Funaki Kai
• Ikeda Isao
• Abe Yutaka
• Kato Masahiro

Classifications

• B23K20/1255 Primary

  Tools therefor, e.g. characterised by the shape of the probe · CPC title

• B23K20/122 Primary

  using a non-consumable tool, e.g. friction stir welding · CPC title

• B23K20/12

  the heat being generated by friction; Friction welding · CPC title

• B23K20/127 Primary

  Friction stir welding involving a mechanical connection · CPC title

• C04B35/584

  based on silicon nitride · CPC title