LiDAR reflecting dark colored pigments and vehicles comprising the same

Patent metadata

Field	Value
Publication number	US-11118062-B2
Application number	US-201715833154-A
Country	US
Kind code	B2
Filing date	Dec 6, 2017
Priority date	Dec 6, 2017
Publication date	Sep 14, 2021
Grant date	Sep 14, 2021

Abstract

A LiDAR reflecting dark colored pigment includes a core layer formed from a reflecting material and a first layer formed from a first absorber material or a first dielectric material extending across the core layer. A second layer formed from a second absorber material different than the third absorber material extends across the first layer and a third layer formed from a third absorber material or a second dielectric material extends across the second layer. The third absorber material is different than the second absorber material. The LiDAR reflecting dark colored pigment reflects less than 10% of incident visible electromagnetic radiation and more than 60% of incident near-IR electromagnetic radiation with wavelengths between and including 850 nm and 950 nm for all incident angles of the visible and near-IR electromagnetic radiation between and including 0° and 45°. A color reflected by the multilayer stack has a lightness in CIELAB color space less than or equal to 40.

First claim

What is claimed is:

1. A pigment comprising:
a core layer formed from a reflecting material;
a first layer extending across the core layer, the first layer formed from a first absorber material or a first dielectric material, wherein the first layer has a thickness from about 5 nm to about 500 nm;
a second layer extending across the first layer, the second layer formed from a second absorber material different than the first absorber material, wherein the second layer has a thickness from about 5 nm to about 50 nm; and
a third layer extending across the second layer, the third layer formed from a third absorber material or a second dielectric material, the third absorber material being different than the second absorber material, wherein the third layer has a thickness from about 5 nm to about 500 nm;
wherein:
the pigment reflects less than 10% of incident visible electromagnetic radiation for all incident angles of the visible electromagnetic radiation between and including 0° and 45°; and
the pigment reflects more than 60% of incident near-IR electromagnetic radiation with wavelengths between and including 850 nm and 950 nm for all incident angles of the near-IR electromagnetic radiation between and including 0° and 45°.

2. The pigment of claim 1 , wherein the first layer is formed from the first absorber material and the first absorber material comprises a selective absorber material.

3. The pigment of claim 2 , wherein the selective absorber material is at least one of Fe 2 O 3 , TiN, Cu and brass.

4. The pigment of claim 1 , wherein the first layer is formed from the first dielectric material and the first dielectric material comprises at least one of ZnS, MgF 2 and TiO 2 .

5. The pigment of claim 1 , wherein the second absorber material is a non-selective absorber material comprising at least one of Cr, Ge, Ni, stainless steel, Pd, Ti, Si, V, Co, W, Mo, Nb, and alloys thereof.

6. The pigment of claim 1 , wherein the third layer is formed from the third absorber material and the third absorber material comprises a selective absorber material.

7. The pigment of claim 6 , wherein the selective absorber material is at least one of Fe 2 O 3 , TiN, Cu and brass.

8. The pigment of claim 1 , wherein the third layer is formed from the second dielectric material.

9. The pigment of claim 8 , wherein the second dielectric material is at least one of ZnS, MgF 2 and TiO 2 .

10. The pigment of claim 1 , wherein:
the reflecting material is at least one of Al or an alloy thereof;
the first layer is formed from the first dielectric material and the first dielectric material comprises ZnS;
the second absorber material is Cr or an alloy thereof; and
the third layer is formed from the third absorber material and the third absorber material comprises Fe 2 O 3 .

11. The pigment of claim 1 , wherein:
the reflecting material is at least one of Al or an alloy thereof;
the first layer is formed from the first dielectric material and the first dielectric material comprises ZnS;
the second absorber material is Cr or an alloy thereof; and
the third layer is formed from the second dielectric material and the second dielectric material comprises ZnS.

12. The pigment of claim 1 , wherein:
the reflecting material is at least one of Al or an alloy thereof;
the first layer is formed from the first absorber material and the first absorber material comprises Fe 2 O 3 ;
the second absorber material is Cr or an alloy thereof; and
the third layer is formed from the third absorber material and the third absorber material comprises Fe 2 O 3 .

13. The pigment of claim 1 , wherein:
the reflecting material is at least one of Al or an alloy thereof;
the first layer is formed from the first absorber material and the first absorber material comprises Fe 2 O 3 ;
the second absorber material is Cr or an alloy thereof; and
the third layer is formed from the second dielectric material and the second dielectric material comprises ZnS.

14. A paint comprising:
a paint binder;
a LiDAR reflecting dark colored pigment disposed in the paint binder and forming a LiDAR reflecting dark colored paint, the LiDAR reflecting dark colored pigment comprising:
a core layer formed from a reflecting material;
a first layer extending across the core layer, the first layer formed from a first absorber material or a first dielectric material, wherein the first layer has a thickness from about 5 nm to about 500 nm;
a second layer extending across the first layer, the second layer formed from a second absorber material different than the first absorber material, wherein the second layer has a thickness from about 5 nm to about 50 nm; and
a third layer extending across the second layer, the third layer formed from a third absorber material or a second dielectric material, the third absorber material being different than the second absorber material, wherein the third layer has a thickness from about 5 nm to about 500 nm;
wherein:
the LiDAR reflecting dark colored paint reflects less than 10% of incident visible electromagnetic radiation for all incident angles of the visible electromagnetic radiation between and including 0° and 45°;
the LiDAR reflecting dark colored paint reflects more than 60% of incident near-IR electromagnetic radiation with wavelengths between and including 850 nm and 950 nm for all incident angles of the near-IR electromagnetic radiation between and including 0° and 45°; and
the LiDAR reflecting dark colored paint has a color with a lightness in CIELAB color space less than or equal to 40.

15. The paint of claim 14 , wherein the first absorber material is a selective absorber material comprising at least one of Fe 2 O 3 , TiN, Cu and brass, and the first dielectric material comprises at least one of ZnS, MgF 2 and TiO 2 .

16. The paint of claim 14 , wherein the second absorber material is a non-selective absorber material selected from at least one of Cr, Ge, Ni, stainless steel, Pd, Ti, Si, V, Co, W, Mo, Nb, and alloys thereof.

17. The paint of claim 14 , wherein the third absorber material is a selective absorber material comprising at least one of Fe 2 O 3 , TiN, Cu and brass, and the second dielectric material comprises at least one of ZnS, MgF 2 and TiO 2 .

18. A vehicle comprising:
a body panel coated a LiDAR reflecting dark colored paint, the LiDAR reflecting dark colored paint comprising:
a paint binder;
a LiDAR reflecting dark colored pigment disposed in the paint binder, the LiDAR reflecting dark colored pigment comprising:
a core layer formed from a reflecting material;
a first layer extending across the core layer, the first layer formed from a first absorber material or a first dielectric material, wherein the first layer has a thickness from about 5 nm to about 500 nm;
a second layer extending across the first layer, the second layer formed from a second absorber material different than the first absorber material, wherein the second layer has a thickness from about 5 nm to about 50 nm; and
a third layer extending across the second layer, the third layer formed from a third absorber material or a second dielectric material, the third absorber material being different than the second absorber material, wherein the third layer has a thickness from about 5 nm to about 500 nm;
wherein:
the LiDAR reflecting dark colored paint reflects less than 10% of incident visible electromagnetic radiation for all incident angles of the visible electromagnetic radiation between and including 0° and 45°;
the LiDAR reflecting dark colored paint ref

Assignees

• Toyota Eng & Mfg North America

Inventors

• Banerjee Debasish
• Templeman Cynthia Gazepis

Classifications

• C09D5/004 Primary

  Reflecting paints; Signal paints · CPC title

• C09C2200/308

  Total thickness of the pigment particle · CPC title

• C09C2200/1054

  the core consisting of a metal · CPC title

• C09C2200/306

  Thickness of an absorbing layer · CPC title

• C09C2200/305

  Thickness of intermediate layers within the stack · CPC title