Flow structures for use with an electrochemical cell

Patent metadata

Field	Value
Publication number	US-11105010-B2
Application number	US-201916383774-A
Country	US
Kind code	B2
Filing date	Apr 15, 2019
Priority date	Jun 13, 2012
Publication date	Aug 31, 2021
Grant date	Aug 31, 2021

Abstract

The design and method of fabrication of a three-dimensional, porous flow structure for use in a high differential pressure electrochemical cell is described. The flow structure is formed by compacting a highly porous metallic substrate and laminating at least one micro-porous material layer onto the compacted substrate. The flow structure provides void volume greater than about 55% and yield strength greater than about 12,000 psi. In one embodiment, the flow structure comprises a porosity gradient towards the electrolyte membrane, which helps in redistributing mechanical load from the electrolyte membrane throughout the structural elements of the open, porous flow structure, while simultaneously maintaining sufficient fluid permeability and electrical conductivity through the flow structure.

First claim

What is claimed is:

1. A method of fabricating an open, porous flow structure for use in an electrochemical cell, the method comprising:
selecting a porous metallic substrate with a void volume between about 75% and about 98%;
compacting the porous metallic substrate causing plastic deformation and thereby forming a compacted porous metallic substrate having a void volume greater than about 55% and yield strength greater than about 12,000 psi; and
laminating at least one micro-porous material layer on one side of the compacted porous metallic substrate, wherein an average pore size of the at least one micro-porous material layer is smaller than an average pore size of the compacted porous metallic substrate.

2. The method of claim 1 , wherein the average pore size of the porous metallic substrate ranges from about 10 μm to about 1000 μm.

3. The method of claim 1 , wherein the compaction process of the porous metallic substrate is by at least one mechanical technique.

4. The method of claim 1 , wherein the ratio of the average pore sizes of the at least one micro-porous material layer and the compacted porous metallic substrate is less than about 0.5.

5. The method of claim 1 , wherein the porous metallic substrate comprises a metallic foam.

6. The method of claim 1 , wherein the porous metallic substrate comprises a sintered metallic frit.

7. The method of claim 1 , wherein the porous metallic substrate comprises two or more distinct regions with different porosities formed by laminating together two or more porous metallic materials having different pore sizes.

8. The method of claim 1 , where the compaction process of the porous metallic substrate is uniform across the porous metallic substrate.

9. The method of claim 1 , further comprising forming a porosity gradient through the flow structure by laminating a plurality of micro-porous material layers on the compacted porous metallic substrate, each micro-porous material layer having a pore size smaller than an immediately preceding layer.

10. The method of claim 1 , wherein a pore size of the at least one micro-porous material layer ranges from about 0.5 μm to about 10 μm.

11. The method of claim 1 , further comprising applying a filler to the compact porous metallic substrate to provide a substantially uniform outer surface.

12. The method of claim 11 , wherein the outer surface is smooth and flat such that the outer surface has a surface flatness of less than about 0.0005 inches.

13. The method of claim 11 , wherein the filler may form a substantially smoother outer covering for the compacted porous metallic substrate having a thickness between about 0.010 inches to about 0.0001 inches.

14. The method of claim 11 , wherein the filler includes a binder configured to increase the strength of the filler.

15. The method of claim 11 , wherein the filler includes at least one of pore formers, fibers, and powders.

16. The method of claim 11 , wherein the filler is formed of at least one of graphite epoxy, carbon black, carbon fibers, graphite beads, or glass beads.

17. The method of claim 1 , where the compaction process of the porous metallic substrate provides pressure equal to or greater than 4,000 psi.

18. A method of fabricating an open, porous flow structure for use in an electrochemical cell, the method comprising:
selecting a porous metallic substrate having greater than about 55% void volume;
compacting the porous metallic substrate using at least one mechanical technique, wherein compaction is uniform across the metallic substrate, causes plastic deformation, and increases the yield strength of the compacted porous metallic substrate; and
laminating at least one micro-porous material layer on one side of the compacted porous metallic substrate, wherein an average pore size of the at least one micro-porous material layer is smaller than an average pore size of the compacted porous metallic substrate.

19. The method of claim 18 , wherein the ratio of the average pore sizes of the at least one micro-porous material layer and the compacted porous metallic substrate is less than about 0.5.

20. The method of claim 18 , further comprising applying a filler to the compact porous metallic substrate to provide a substantially uniform outer surface.

Assignees

• Nuvera Fuel Cells Llc

Inventors

• Blanchet Scott
• Van Boeyen Roger

Classifications

• H01M4/808

  Foamed, spongy materials · CPC title

• Y02E60/50

  Fuel cells · CPC title

• Y10T156/1002

  with permanent bending or reshaping or surface deformation of self sustaining lamina · CPC title

• C25B15/08 Primary

  Supplying or removing reactants or electrolytes; Regeneration of electrolytes · CPC title

• H01M8/0245

  in the form of layered or coated products · CPC title