Polymer composition filled with an inorganic filler material mixture

Patent metadata

Field	Value
Publication number	US-11098191-B2
Application number	US-201515314649-A
Country	US
Kind code	B2
Filing date	Jun 2, 2015
Priority date	Jun 5, 2014
Publication date	Aug 24, 2021
Grant date	Aug 24, 2021

Abstract

The present invention relates to a polymer composition comprising at least 20.0 wt.-%, based on the total weight of the polymer composition, of at least one biodegradable polymer resin, from 0.1 to 20.0 wt.-%, based on the total weight of the polymer composition, of at least one polyolefin selected from polyethylene and/or polypropylene and from 5.9 to 60.0 wt.-%, based on the total weight of the polymer composition, of an inorganic filler material dispersed in the at least one polyolefin and the at least one biodegradable polymer resin, a process for the preparation of such a polymer composition, the use of an inorganic filler material for increasing the thermal stability and/or processability of a polymer composition, the use of the polymer composition for the preparation of an article as well as in a process selected from extrusion process, co-extrusion process, blown film extrusion process, cast film extrusion or sheet extrusion process, extrusion coating process, injection molding process, blow molding process, thermoforming process as well as an article comprising the polymer composition.

First claim

The invention claimed is:

1. A polymer composition comprising:
a) from 45.0 to 94.0 wt.-%, based on the total weight of the polymer composition, of at least one biodegradable polymer resin selected from the group consisting of polylactic acid, a polylactic acid-based polymer, and a mixture thereof,
b) from 0.1 to 20.0 wt.-%, based on the total weight of the polymer composition, of at least one polyolefin selected from a low-density polyethylene, an isotactic polypropylene having a melt flow rate MFR (230° C., 2.16 kg) measured according to ISO 1133 of from 0.5 to 100.0 g/10 min, and/or a crystallinity percentage of greater than 20%, based on the total weight of the polypropylene, or mixture thereof, and
c) from 5.9 to 50.0 wt-%, based on the total weight of the polymer composition, of an inorganic filler material dispersed in the at least one polyolefin and the at least one biodegradable polymer resin, wherein the inorganic filler material consists of:
i) from 10.0 to 17.5 wt.-%, based on the total weight of the inorganic filler material, of at least one acidic inorganic filler material and the at least one acidic inorganic filler material is talc, and
ii) from 82.5 to 90.0 wt.-%, based on the total weight of the inorganic filler material, of at least one alkaline inorganic filler material comprising calcium carbonate in an amount of ≥75.0 wt.-%, based on the total weight of the at least one alkaline inorganic filler material.

2. The polymer composition according to claim 1 , wherein the at least one polymer composition comprises:
a) from 45.0 to 94.0 wt.-%, based on the total weight of the polymer composition, of the at least one biodegradable polymer resin,
b) from 0.1 to 15.0 wt.-%, based on the total weight of the polymer composition, of the at least one polyolefin, and
c) from 5.9 to 50.0 wt.-%, based on the total weight of the polymer composition, of the inorganic filler material dispersed in the at least one polyolefin and the at least one biodegradable polymer resin.

3. The polymer composition according to claim 1 , wherein the at least one biodegradable polymer resin is a polylactic acid-based polymer.

4. The polymer composition according to claim 1 , wherein the at least one biodegradable polymer resin is polylactic acid.

5. The polymer composition according to claim 1 , wherein the at least one polyolefin is a low-density polyethylene.

6. The polymer composition according to claim 5 , wherein the low-density polyolefin is a linear low-density polyethylene.

7. The polymer composition according to claim 1 , wherein the at least one polyolefin is a linear low-density polyethylene having a melt flow rate MFR (190° C., 2.16 kg) measured according to ISO 1133 of from 0.5 to 100.0 g/10 min.

8. The polymer composition according to claim 1 , wherein the at least one polyolefin is a linear low-density polyethylene having a melt flow rate MFR (190° C., 2.16 kg) measured according to ISO 1133 of from 5.0 to 90.0 g/10 min.

9. The polymer composition according to claim 1 , wherein the at least one polyolefin is an isotactic polypropylene having a melt flow rate MFR (230° C., 2.16 kg) measured according to ISO 1133 of from 0.5 to 100.0 g/10 min, and/or a crystallinity percentage of greater than 20%, based on the total weight of the polypropylene.

10. The polymer composition according to claim 1 , wherein the at least one polyolefin is an isotactic polypropylene having a melt flow rate MFR (230° C., 2.16 kg) measured according to ISO 1133 of from 5.0 to 90.0 g/10 min, and/or a crystallinity percentage from 30% to 90%, based on the total weight of the polypropylene.

11. The polymer composition according to claim 1 , wherein the at least one polyolefin is an isotactic polypropylene having a melt flow rate MFR (230° C., 2.16 kg) measured according to ISO 1133 of from 10.0 to 80.0 g/10 min, and/or a crystallinity percentage from 45% to 85%, based on the total weight of the polypropylene.

12. The polymer composition according to claim 1 , wherein the at least one acidic inorganic filler material and/or the at least one alkaline inorganic filler material has/have:
a) a weight median particle size d 50 value in the range from 1.0 μm to 12.0 μm, and/or
b) a specific surface area (BET) of from 0.1 to 15.0 m 2 /g as measured by the BET nitrogen method.

13. The polymer composition according to claim 1 , wherein the at least one alkaline inorganic filler material is selected from ground calcium carbonate (GCC) and/or precipitated calcium carbonate (PCC).

14. The polymer composition according to claim 1 , wherein the at least one alkaline inorganic filler material is ground calcium carbonate (GCC) selected from the group consisting of marble, chalk, dolomite, limestone, and any mixture thereof and/or at least one precipitated calcium carbonate (PCC) selected from one or more of the aragonitic, vateritic and calcitic mineralogical crystal forms.

15. The polymer composition according to claim 1 , wherein the at least one alkaline inorganic filler material comprises calcium carbonate in an amount ≥90.0 wt.-%, based on the total weight of the at least one alkaline inorganic filler material.

16. The polymer composition according to claim 1 , wherein the at least one alkaline inorganic filler material comprises calcium carbonate in an amount ≥95.0 wt.-%, based on the total weight of the at least one alkaline inorganic filler material.

17. The polymer composition according to claim 1 , wherein the at least one alkaline inorganic filler material comprises calcium carbonate in an amount from 97.0 to 99.9 wt.-%, based on the total weight of the at least one alkaline inorganic filler material.

18. The polymer composition according to claim 1 , wherein at least 1% of the accessible surface area of the at least one acidic inorganic filler material and/or the at least one alkaline inorganic filler material is covered by a coating comprising:
a) at least one aliphatic carboxylic acid having a total amount of carbon atoms from C4 to C24 and/or reaction products thereof, and/or
b) at least one mono-substituted succinic anhydride consisting of succinic anhydride mono- substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C2 to C30 in the substituent and/or reaction products thereof, and/or
c) a phosphoric acid ester blend of one or more phosphoric acid mono-ester and/or reaction products thereof and one or more phosphoric acid di-ester and/or reaction products thereof.

19. The polymer composition according to claim 1 , wherein at least 1% of the accessible surface area of the at least one acidic inorganic filler material and/or the at least one alkaline inorganic filler material is covered by a coating comprising stearic acid and/or reaction products thereof.

20. The polymer composition according to claim 1 , further comprising at least one additive selected from the group consisting of impact modifiers, lubricants, waxes, stabilizers, processing aids, pigments, coloring agents, and any mixture thereof.

21. An article comprising the polymer composition according to claim 1 .

22. The article according to claim 21 , which is a packaging article, a food packaging, a bottle, a container, a cup, or a food tray.

23. The article according to claim 21 , wherein the article is prepared by an extrusion process, a co-extrusion process, a blown film extrusion process, a cast film extrusion, a sheet extrusion process, an ext

Assignees

• Omya Int Ag

Inventors

• Blanchard Pierre
• Fornera Tazio

Classifications

• C08K3/01

  characterized by their specific function · CPC title

• C08L101/16

  the macromolecular compounds being biodegradable · CPC title

• C08L23/12

  Polypropene · CPC title

• C08L23/06

  Polyethylene · CPC title

• C08K3/34

  Silicon-containing compounds · CPC title