Strength enhancing admixture for cementitious compositions

Patent metadata

Field	Value
Publication number	US-11097988-B2
Application number	US-201716467724-A
Country	US
Kind code	B2
Filing date	Dec 21, 2017
Priority date	Dec 27, 2016
Publication date	Aug 24, 2021
Grant date	Aug 24, 2021

Abstract

A strength enhancing admixture for cementitious and/or pozzolanic compositions including, based on the total dry weight of the admixture, calcium silicate hydrate in an amount of from about 0.5 to about 94 weight percent, and: i) at least one alkanolamine in an amount of from about 0.5 to about 55 weight percent; ii) at least one inorganic accelerator in an amount of from about 0.5 to about 85 weight percent; and iii) at least one carbohydrate in an amount of from about 0.5 to about 50 weight percent; wherein the calcium silicate hydrate includes a product of a reaction of a water-soluble calcium compound with a water-soluble silicate compound in presence of a water-soluble dispersant; and wherein the at least one inorganic accelerator includes any inorganic accelerator(s) other than calcium silicate hydrate.

First claim

What is claimed is:

1. A strength enhancing admixture for cementitious and/or pozzolanic compositions comprising, based on the total dry weight of the admixture, without exceeding 100% by weight of the dry admixture, calcium silicate hydrate in an amount of from 1 to about 80 weight percent, and: i) at least one alkanolamine in an amount of from 7.5 to about 55 weight percent; ii) at least one inorganic accelerator in an amount of 7.5 to about 85 weight percent, wherein the at least one inorganic accelerator is selected from a nitrate-based compound, a thiocyanate-based compound and mixtures thereof; and iii) at least one carbohydrate in an amount of from 2.5 to about 50 weight percent; wherein the calcium silicate hydrate comprises a product of a reaction of a water-soluble calcium compound with a water-soluble silicate compound in presence of a water-soluble dispersant; and wherein the at least one inorganic accelerator comprises any inorganic accelerator(s) other than calcium silicate hydrate.

2. The strength enhancing admixture of claim 1 , wherein the water-soluble dispersant comprises at least one of a polycarboxylate ether or a polyaryl ether.

3. The strength enhancing admixture of claim 1 , wherein the water-soluble dispersant comprises a polycarboxylate ether.

4. The strength enhancing admixture of claim 1 , wherein the at least one alkanolamine comprises at least one of triisopropanolamine, triethanolamine, N,N,N′,N′-tetra(hydroxyethyl)ethylenediamine, monoethanolamine, methydiethanolamine, diethanolamine or diisopropanolamine.

5. The strength enhancing admixture of claim 1 , wherein the at least one inorganic accelerator comprises a further inorganic accelerator selected from the group consisting of at least one thiocyanate-based compound, sulfate-based compound, aluminate-based compound, nitrite-based compound, colloidal silica and mixtures thereof.

6. The strength enhancing admixture of claim 5 , wherein the sulfate-based compound comprises at least one of aluminum sulfate, aluminum hydroxy sulfate, calcium thiosulfate, sodium thiosulfate, potassium sulfate, calcium sulfate, calcium sulfate hemihydrate, calcium sulfate hemihydrate dehydrate or sodium sulfate.

7. The strength enhancing admixture of claim 5 , wherein the aluminate-based compound comprises sodium aluminate.

8. The strength enhancing admixture of claim 5 , wherein the nitrate-based compound is a nitrate salt of an alkali metal, alkaline earth metal, or aluminum.

9. The strength enhancing admixture of claim 5 , wherein the nitrite-based compound is a nitrite salt of an alkali metal, alkaline earth metal, or aluminum.

10. The strength enhancing admixture of claim 1 , wherein the at least one carbohydrate comprises at least one of sugar-containing substances, corn syrup, diutan gum, welan gum, molasses, or sucrose.

11. The strength enhancing admixture of claim 1 , further comprising a defoamer.

12. The strength enhancing admixture of claim 1 , further comprising at least one of set retarders, air detraining agents, air entraining agents, shrinkage reducing admixtures, water reducers, foaming agents, dampproofing admixtures, pumping aids, fungicidal admixtures, insecticidal admixtures, germicidal admixtures, alkali activity reducers, bonding admixtures, corrosion inhibitors or pigments.

13. A cementitious composition comprising at least one cementitious and/or pozzolanic material and a strength enhancing admixture according to claim 1 .

14. The cementitious composition of claim 13 , wherein the at least one cementitious and/or pozzolanic material comprises at least one of hydraulic cement, fly ash, limestone, slag, calcined clay, silica fume or metakaolin.

15. A method for improving early and/or late compressive strength of a cementitious composition comprising introducing into a cementitious and/or pozzolanic mixture a strength enhancing admixture according to claim 1 .

16. A method of preparing a cementitious composition comprising forming a mixture of water, at least one cementitious and/or pozzolanic material and a strength enhancing admixture according to claim 1 .

Assignees

• Construction Research & Technology Gmbh

Inventors

• Bui Van
• Schaef Steve
• Seiler Paul Horst

Classifications

• Y02W30/91

  Use of waste materials as fillers for mortars or concrete · CPC title

• C04B40/0039 Primary

  Premixtures of ingredients · CPC title

• C04B40/0042 Primary

  Powdery mixtures · CPC title

• C04B2103/10

  Accelerators; Activators · CPC title

• C04B22/085

  containing nitrogen in the anion, e.g. nitrites · CPC title