Additive for quality determination of adhesive bond primers

Patent metadata

Field	Value
Publication number	US-11078386-B2
Application number	US-201816153539-A
Country	US
Kind code	B2
Filing date	Oct 5, 2018
Priority date	Oct 5, 2018
Publication date	Aug 3, 2021
Grant date	Aug 3, 2021

Abstract

A method of adhering a first component to a second component includes priming the first component with an adhesive bond primer containing a primer material, a corrosion inhibitor, and a chemical additive (such as a dye compound), and using an adhesive to attach the second component to the first component through the adhesive bond primer applied on the surface of the second component. The chemical additive allows inspection of the adhesive bond primer with a corresponding radiation source.

First claim

The invention claimed is:

1. An assembly comprising:
a first component;
a first adhesive bond primer thereon comprising:
a first primer material;
a corrosion inhibitor, wherein the corrosion inhibitor comprises:
a corrosion inhibitive cation selected from the group consisting of zinc, calcium, strontium, magnesium, aluminum, chromium, manganese, rare earth metals, and combinations thereof; and
a corrosion inhibitive anion selected from the group consisting of phosphate, molybdate, vanadate, silicate, tungstate, orthophosphate, and combinations thereof; and

a first chemical additive, wherein the first chemical additive interacts with electromagnetic radiation outside the human visual spectrum to produce an observable emission, wherein the first chemical additive comprises phosphorescent molecules selected from the group consisting of strontium aluminates, lanthanide doped strontium aluminates, manganese doped strontium aluminates, and copper activate zinc sulfide and the dye compound comprises particles up to 10 μm;
wherein the first adhesive bond primer can be cured between 250° F. and 350° F., and has a wedge crack growth of no more than 0.25 inches as measured by ASTM D3762 (wedge crack extension testing) and a minimum stress at failure of least 440 psi as measured by ASTM D1002 (lap shear testing); and

a second component;
a second adhesive bond primer thereon comprising:
a second primer material;
a corrosion inhibitor, wherein the corrosion inhibitor comprises:
a corrosion inhibitive cation selected from the group consisting of zinc, calcium, strontium, magnesium, aluminum, chromium, manganese, rare earth metals, and combinations thereof; and
a corrosion inhibitive anion selected from the group consisting of phosphate, molybdate, vanadate, silicate, tungstate, orthophosphate, and combinations thereof; and
a second chemical additive, wherein the second chemical additive interacts with electromagnetic radiation outside the human visual spectrum to produce an observable emission, wherein the second chemical additive comprises phosphorescent molecules selected from the group consisting of strontium aluminates, lanthanide doped strontium aluminates, manganese doped strontium aluminates, and copper activate zinc sulfide and the dye compound comprises particles up to 10 μm;
wherein the second adhesive bond primer can be cured between 250° F. and 350° F., and has a wedge crack growth of no more than 0.25 inches as measured by ASTM D3762 (wedge crack extension testing) and a minimum stress at failure of least 440 psi as measured by ASTM D1002 (lap shear testing); and

an adhesive adhering the first component to the second component through the first adhesive bond primer and the second adhesive bond primer.

2. The assembly of claim 1 , wherein the first and second components are selected from the group consisting of rotor blades, vanes, wings, heating panels, acoustic panels, floor or side panels, propellers, landing gear, nacelles, electronic boxes, fasteners, nuts, bolts, washers, and rivets.

3. The assembly of claim 1 , wherein the chemical additives emit in the visible spectrum when exposed to ultra violet light.

4. An adhesive bond primer comprising:
an adhesive primer;
a corrosion inhibitor, wherein the corrosion inhibitor comprises:
a corrosion inhibitive cation selected from the group consisting of zinc, calcium, strontium, magnesium, aluminum, chromium, manganese, rare earth metals, and combinations thereof; and
a corrosion inhibitive anion selected from the group consisting of phosphate, molybdate, vanadate, silicate, tungstate, orthophosphate, and combinations thereof; and

a dye compound that interacts with electromagnetic radiation outside the human visual spectrum but not electromagnetic radiation that is within the human visual spectrum to produce an observable emission, wherein the dye compound comprises phosphorescent molecules selected from the group consisting of strontium aluminates, lanthanide doped strontium aluminates, manganese doped strontium aluminates, and copper activate zinc sulfide and the dye compound comprises particles up to 10 μm;
wherein the adhesive bond primer can be cured between 250° F. and 350° F., and has a wedge crack growth of no more than 0.25 inches as measured by ASTM D3762 (wedge crack extension testing) and a minimum stress at failure of least 440 psi as measured by ASTM D1002 (lap shear testing).

5. The primer of claim 4 , wherein the adhesive bond primer has a thickness between 0.0001 inches and 0.0004 inches.

6. The primer of claim 4 , wherein the dye compound further comprises fluorescent molecules selected from the group consisting of polycyclic hydrocarbons, polyaromatic hydrocarbons, and combinations thereof.

7. The primer of claim 6 , wherein the polycyclic or polyaromatic hydrocarbons are selected from the group consisting of anthra-thioxanthene, thioxanthene benzanthrone, anthraquinones, xanthene, benzothioxanthene-dicarboximide, aminoketones, coumarin, hydroxycoumarin, naphthalimide and perylene.

8. The primer of claim 4 , wherein the dye compound comprises less than 15% by weight of the adhesive bond primer.

9. The primer of claim 8 , wherein the dye compound comprises less than 10% by weight of the adhesive bond primer.

10. The primer of claim 9 , wherein the dye compound comprises less than 5% by weight of the adhesive bond primer.

11. The primer of claim 4 , wherein the dye compound further comprises a photoluminescent material.

12. The primer of claim 11 , wherein the photoluminescent material is quantum dots, yttrium aluminum garnet, or a mixture thereof.

13. A method of inspecting an adhesive bond of a first component to a second component comprising:
applying electromagnetic radiation to an adhesive bond primer comprising a primer material, a corrosion inhibitive pigment(s), and a chemical additive that interacts with electromagnetic radiation outside the human visual spectrum but not electromagnetic radiation that is within the human visual spectrum to produce an observable emission,
wherein the corrosion inhibitive pigment(s) includes a corrosion inhibitor that comprises:
a corrosion inhibitive cation selected from the group consisting of zinc, calcium, strontium, magnesium, aluminum, chromium, manganese, rare earth metals, and combinations thereof; and
a corrosion inhibitive anion selected from the group consisting of phosphate, molybdate, vanadate, silicate, tungstate, orthophosphate, and combinations thereof; and
a first chemical additive comprises phosphorescent molecules selected from the group consisting of strontium aluminates, lanthanide doped strontium aluminates, manganese doped strontium aluminates, and copper activate zinc sulfide and the dye compound comprises particles up to 10 μm;
wherein the adhesive bond primer can be cured between 250° F. and 350° F., and has a wedge crack growth of no more than 0.25 inches as measured by ASTM D3762 (wedge crack extension testing) and a minimum stress at failure of least 440 psi as measured by ASTM D1002 (lap shear testing); and

inspecting the integrity of the adhesive bond primer by observing emissions from the chemical additive in response to the electromagnetic radiation.

14. The method of claim 13 , further comprising curing the adhesive bond primer on the first component.

15. The method of claim 14 , further comprising curing the adhesive bond primer between 250 and 350 degrees Fahrenheit.

16. The method of claim 13 , wherein inspecting the integrity of the adhesive bond primer further comprises inducing fluorescence in the chemical additive.

Assignees

• Hamilton Sundstrand Corp

Inventors

• Emerson Sean C
• Smith Blair A
• Li Weina
• Zafiris Georgios S
• Van Hassel Bart Antoine

Classifications

• C09D5/08 Primary

  Anti-corrosive paints · CPC title

• C09J11/06

  organic · CPC title

• C09K11/08

  containing inorganic luminescent materials · CPC title

• C08K13/02

  Organic and inorganic ingredients · CPC title

• B32B7/12

  using interposed adhesives or interposed materials with bonding properties · CPC title