Production of rounded salt particles

Patent metadata

Field	Value
Publication number	US-11078085-B2
Application number	US-201816155683-A
Country	US
Kind code	B2
Filing date	Oct 9, 2018
Priority date	May 26, 2016
Publication date	Aug 3, 2021
Grant date	Aug 3, 2021

Abstract

The present disclosure generally relates to methods of preparing spherical salt particles for industrial, medical, and other uses. The methods can include combining the angular salt particles with a quantity of finishing media, for example, into a receptacle. Thereafter, the angular salt particles and the finishing media can be moved or agitated until the angular salt particles have a desired sphericity.

First claim

What is claimed is:

1. A method for producing rounded salt particles from angular salt particles, the method comprising combining the angular salt particles with a quantity of about 1 mm to about 10 mm ball-shaped finishing media in a receptacle, and moving or agitating the angular salt particles and the finishing media at a frequency of about 2 Hz to about 4 Hz for about 6 hours to about 12 days until the angular salt particles have a sphericity of greater than about 0.75.

2. The method of claim 1 , wherein the angular salt particles have a particle size in the range of about 100 to about 1200 μm.

3. The method of claim 1 , wherein the angular salt particles are sodium chloride.

4. The method of claim 1 , wherein the finishing media is selected from the group consisting of porcelain, aluminum oxide, and silicon carbide.

5. The method of claim 1 , wherein the finishing media is in a particulate form having a particle size of about 4 mm.

6. The method of claim 1 , wherein the angular salt particles and the finishing media are provided in a weight ratio of angular salt to finishing media of about 0.6:1.

7. The method of claim 1 , wherein the moving comprises combining the angular salt particles and the finishing media into a mixture and continuously or semi-continuously shaking, vibrating, or stirring the mixture.

8. The method of claim 7 , wherein the moving comprises vibrating the mixture of angular salt particles and finishing media.

9. The method of claim 1 , wherein the moving is performed in a cyclical manner at a frequency of about 2 Hz to about 4 Hz.

10. The method of claim 1 , wherein the predetermined sphericity is greater than about 0.900.

11. The method of claim 1 , further comprising the step of separating the rounded salt particles from the finishing media.

12. The method of claim 1 , wherein the angular salt particles have a particle size in the range of about 420 to about 600 μm.

13. A process for manufacturing a soft prosthetic breast implant, the process comprising:
forming a flexible shell of silicone elastomer, the silicone elastomer having a thickness;
adhering on an exterior of the flexible shell an even distribution of the rounded salt particles formed by the method of claim 1 ;
curing the flexible shell with the rounded salt particles adhered thereto; and
removing the rounded salt particles from the exterior of the flexible shell.

14. The process of claim 13 , wherein the removing forms an open-pored structure on the exterior of the flexible shell such that the exterior of the flexible shell exhibits an undulating topography, the open-pored structure comprising round cavities defined by impressions of the rounded salt particles.

15. The process of claim 14 , wherein the open-pored structure does not extend through an entire thickness of the silicone elastomer.

16. The process of claim 13 , further comprising processing the flexible shell such that it forms a closed envelope.

17. A method for producing rounded sodium chloride salt particles from angular sodium chloride salt particles having a particle size in the range of about 420 to about 600 μm, the method comprising:
combining the angular sodium chloride salt particles with a quantity of 4 mm porcelain ceramic balls in a receptacle, wherein the angular sodium chloride salt particles and the porcelain ceramic balls are provided in a weight ratio of angular salt to finishing media is about 0.6:1; and
vibrating the angular sodium chloride salt particles and the porcelain ceramic balls until the angular sodium chloride salt particles have a sphericity of greater than about 0.75, wherein the vibrating is performed for a period of time in the range of about 6 hours to about 12 days and at a frequency of about 2 Hz to about 4 Hz.

18. The method of claim 17 , wherein the vibrating the angular sodium chloride salt particles and the porcelain ceramic balls comprises continuously vibrating the angular sodium chloride salt particles and the porcelain ceramic balls.

19. The method of claim 17 , wherein the vibrating the angular sodium chloride salt particles and the porcelain ceramic balls comprises semi-continuously vibrating the angular sodium chloride salt particles and the porcelain ceramic balls.

20. The method of claim 17 , wherein the predetermined sphericity is greater than about 0.900.

21. The method of claim 17 , further comprising the step of separating the rounded sodium chloride salt particles from the porcelain ceramic balls.

Assignees

• Allergan Inc

Inventors

• Schuessler David J
• Flores-Pujol Alberto J

Classifications

• C01D3/04 Primary

  Chlorides · CPC title

• A61F2002/0081

  directly machined on the prosthetic surface, e.g. holes, grooves (A61F2/30771 takes precedence) · CPC title

• C01P2004/32

  Spheres · CPC title

• C01P2002/30

  Three-dimensional structures · CPC title

• C01P2004/02

  obtained by optical microscopy · CPC title