Electrically conductive particles, composition, article and method of manufacturing electrically conductive particles

Patent metadata

Field	Value
Publication number	US-11072711-B2
Application number	US-201816955957-A
Country	US
Kind code	B2
Filing date	Dec 21, 2018
Priority date	Dec 22, 2017
Publication date	Jul 27, 2021
Grant date	Jul 27, 2021

Abstract

The invention is directed to electrically conductive particles comprising a metallic core, a dielectric layer encapsulating said metallic core, and a silver containing outer-layer, wherein said metallic core comprises or consists of elemental metal selected from the group consisting of aluminum, copper, iron, nickel, zinc, and alloys, and mixtures thereof, said dielectric layer comprises at least one metal oxide selected from the group consisting of the group consisting of silicon oxide, aluminum oxide, titanium oxide, zirconium oxide, tin oxide, organic polymer, and mixtures thereof, wherein said silver containing layer is a continuous and opaque layer, wherein a silver ion coordinating layer is arranged between said dielectric layer and said silver containing layer and, optionally a further outer surface modification layer in amount of 0 to 3 wt.-%, based on the total weight of the electrically conductive particles. The invention is also directed to a composition and an article comprising the electrically conductive particles as well as to a method for producing said electrically conductive particles.

First claim

The invention claimed is:

1. Electrically conductive particles comprising metallic cores, a dielectric layer encapsulating the metallic cores, a silver containing outer-layer, and a silver ion coordinating layer arranged between the dielectric layer and the silver containing outer-layer,
wherein the metallic cores comprise one or more of elemental aluminum, elemental copper, elemental iron, elemental nickel, elemental zinc, aluminum alloy, copper alloy, iron alloy, nickel alloy, zinc alloy, aluminum oxide, copper oxide, iron oxide, nickel oxide, and zinc oxide,
the dielectric layer comprises one or more of an organic polymer and a metal oxide, the metal oxide including one or more of silicon oxide, aluminum oxide, titanium oxide, zirconium oxide, and tin oxide, and the silver containing outer-layer includes a continuous and opaque layer,
the dielectric layer includes a silicon oxide layer, and
the metallic cores have a median diameter d 50 in the range of 2 μm to 100 μm.

2. The electrically conductive particles according to claim 1 ,
wherein the silver ion coordinating layer includes one or more of an organofunctional silane comprising a silver ion coordinating moiety, an organofunctional titanate comprising a silver ion coordinating moiety, an organofunctional aluminate comprising a silver ion coordinating moiety, and an organofunctional zirconate comprising a silver ion coordinating moiety.

3. The electrically conductive particles according to claim 1 ,
wherein the silver ion coordinating layer comprises at least one silane of formula (I):
(R 1 O) (4-a-b-c) Si(R 2 X) a (R 3 ) b (R 4 ) c   (I),

wherein:
a is an integer selected from 1, 2, or 3,
b and c are independently selected integers from 0, 1, or 2, with the proviso that a+b+c is an integer from 1 to 3,
R 1 is alkyl with 1 to 4 carbon atoms,
each R 2 independently represents a branched-chain having 1 to 14 carbon atoms, a straight chain alkylene having 1 to 14 carbon atoms, or a cycloalkylene having 5 to 11 carbon atoms, and each R 3 and R 4 independently represents a branched-chain alkyl having 1 to 14 carbon atoms, a straight chain alkyl having 1 to 14 carbon atoms, a cycloalkyl having 5 to 11 carbon atoms, or H, and X is a silver ion coordinating moiety.

4. The electrically conductive particles according to claim 3 ,
wherein the silver ion coordinating moiety X independently represents one or more of mercapto, thioalkylether having 1 to 6 carbon atoms, amino, thiosulfate, thiocyanate, cyanate, cyanide, ureido, carbamate, and bipyridyl.

5. The electrically conductive particles according to claim 1 ,
wherein the silver ion coordinating layer comprises one or more of mercapto silane, amino silane, and thiocyanate silane.

6. The electrically conductive particles according to claim 1 ,
wherein the silver ion coordinating layer comprises mercaptosilane.

7. The electrically conductive particles according to claim 1 ,
wherein the dielectric layer is present in an amount in a range of 0.5 to 15 wt.-%, based on the total weight of the metallic cores.

8. The electrically conductive particles according to claim 1 ,
wherein the dielectric layer comprises a hybrid mixture of silicon oxide and one or more of an organic oligomer and an organic polymer.

9. The electrically conductive particles according to claim 1 ,
wherein the dielectric layer includes a first sublayer comprising the silicon oxide layer, the silicon oxide layer comprising silicon dioxide, and a second sublayer comprising a polymer, wherein the second sublayer is located either directly on the first sublayer or between the silver ion coordinating layer and the first sublayer.

10. The electrically conductive particles according to claim 1 ,
wherein the silver containing outer-layer is present in an amount of 5 to 45 wt-%, based on the electrically conductive particles.

11. The electrically conductive particles according to claim 1 ,
wherein the electrically conductive particles have an electrical powder resistivity in a range of 0.2 to below 100 mΩ cm.

12. The electrically conductive particles according to claim 1 ,
wherein the metallic cores have one or more of a spherical form, plate-like form, and a dendritic form.

13. The electrically conductive particles of claim 1 , wherein the particles further comprise an outer surface modification layer in amount of 0 to 3 wt.-%, based on the total weight of the electrically conductive particles.

14. The electrically conductive particles of claim 1 , wherein the silver ion coordinating layer comprises one or more of 3-mercaptopropyl trimethoxysilane, mercaptopropyl methyl dimethoxysilane, 3-mercaptopropyl triethoxysilane, and 3-thiocyanatopropyl triethoxysilane.

15. The electrically conductive particles of claim 1 , wherein the dielectric layer is present in an amount in a range of 0.5 to 15 wt. %, based on the total weight of the metallic core.

16. The electrically conductive particles of claim 1 , wherein the d 50 of the metallic core is in the range from 3 μm to 85 μm.

17. The electrically conductive particles of claim 1 , wherein the d 50 of the metallic core is in the range from 4 μm to 75 μm.

18. A method of manufacturing electrically conductive particles, the method comprising:
providing metallic core particles, the metallic core particles having a median diameter d50 in the range of 2 μm to 100 μm,
applying a dielectric layer on the metallic core particles, the dielectric layer including a silicon oxide layer,
applying a coordinating layer for silver ions on the dielectric layer,
contacting the coordinating layer of the coated particles with silver ions, the silver ions being provided by a silver compound dissolved in a solvent, to coordinate at least part of the silver ions on the coordinating layer, and
reducing the silver ions coordinated on the surface of the coordinating layer and reducing additional silver ions to provide a continuous and opaque silver containing layer on the coordinating layer.

19. The method of claim 18 , further comprising applying an outer surface modification layer to the particles.

Assignees

• Eckart Gmbh

Inventors

• Schilling Christine
• Hiltl Stephanie

Classifications

• C01P2004/80

  Particles consisting of a mixture of two or more inorganic phases · CPC title

• C01P2004/32

  Spheres · CPC title

• C01P2004/03

  obtained by SEM · CPC title

• H01B1/02 Primary

  mainly consisting of metals or alloys · CPC title

• H01B3/12

  ceramics · CPC title