Bio-electrode composition, bio-electrode, and method for manufacturing bio-electrode

Patent metadata

Field	Value
Publication number	US-11071485-B2
Application number	US-201715819724-A
Country	US
Kind code	B2
Filing date	Nov 21, 2017
Priority date	Dec 21, 2016
Publication date	Jul 27, 2021
Grant date	Jul 27, 2021

Abstract

The present invention provides a bio-electrode composition including a polymer compound having both an ionic repeating unit A and a (meth)acrylate repeating unit B, wherein the ionic repeating unit A is a repeating unit selected from the group consisting of sodium salt, potassium salt, and ammonium salt having either or both partial structures shown by the following general formulae (1-1) and (1-2), and the (meth)acrylate repeating unit B is a repeating unit shown by the following general formula (2).This can form a living body contact layer for a bio-electrode with excellent electric conductivity, biocompatibility, and light weight, which can be manufactured at low cost and does not cause large lowering of the electric conductivity even when it is wetted with water or dried.

First claim

The invention claimed is:

1. A bio-electrode composition comprising a polymer compound having both an ionic repeating unit A and a (meth)acrylate repeating unit B,
wherein the ionic repeating unit A is a repeating unit selected from the group consisting of sodium salt, potassium salt, and ammonium salt having either or both partial structures shown by the following general formulae (1-1) and (1-2), and the (meth)acrylate repeating unit B is a repeating unit shown by the following general formula (2),

wherein, Rf 1 to Rf 4 each independently represent a hydrogen atom, a fluorine atom, or a trifluoromethyl group, having one or more fluorine atoms in all of the Rf 1 to Rf 4 , Rf 1 and Rf 2 optionally bonded with an oxygen atom mutually to form a double bond; Rf 5 represents a fluorine atom or a trifluoromethyl group; “m” is an integer of 1 to 4; X + represents a sodium ion, a potassium ion, or an ammonium ion; R 1 represents a hydrogen atom or a methyl group; R 2 represents a linear, branched, or cyclic alkyl group having 1 to 39 carbon atoms, a linear, branched, or cyclic alkenyl group having 2 to 30 carbon atoms, a linear, branched, or cyclic alkynyl group having 2 to 30 carbon atoms, a phenyl group, or a naphthyl group, optionally having a hydroxy group, an ether group, an ester group, or an aromatic group in R 2 when R 2 is an alkyl group, an alkenyl group, or an alkynyl group; and “b” is a number satisfying 0<b<1.0.

2. The bio-electrode composition according to claim 1 , wherein the repeating unit A is one or more repeating units selected from the group consisting of repeating units A1 to A5 shown by the following general formula (3),

wherein, R 3 , R 5 , R 7 , R 10 , and R 12 each independently represent a hydrogen atom or a methyl group; R 4 , R 6 , R 8 , and R 11 each independently represent a single bond, an ester group, or a linear, branched, or cyclic hydrocarbon group having 1 to 12 carbon atoms optionally having at least one of an ether group and an ester group; R 9 represents a linear or branched alkylene group having 1 to 4 carbon atoms, and one or two hydrogen atoms in R 9 are each optionally substituted with a fluorine atom; Z 1 , Z 2 , Z 3 , and Z 4 each independently represent a single bond, a phenylene group, a naphthylene group, an ether group, an ester group, or an amide group; Z 5 represents a single bond, an ether group, or an ester group; Y represents an oxygen atom or an NR 13 group; R 13 represents a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, optionally bonded with R 6 to form a ring; a1, a2, a3, a4, and a5 are numbers satisfying 0≤a1<1.0, 0≤a2<1.0, 0≤a3<1.0, 0≤a4<1.0, 0≤a5<1.0, and 0<a1+a2+a3+a4+a5<1.0; Rf 5 , X + , and “m” have the same meanings as defined above.

3. The bio-electrode composition according to claim 1 , wherein the polymer compound is a polymer compound copolymerized with at least one of a repeating unit C having a fluorine atom or a silicon atom and a repeating unit D having one or more groups selected from the group consisting of a hydroxy group, a carboxy group, an oxirane group, and an oxetane group, in addition to the repeating unit A and the repeating unit B.

4. The bio-electrode composition according to claim 2 , wherein the polymer compound is a polymer compound copolymerized with at least one of a repeating unit C having a fluorine atom or a silicon atom and a repeating unit D having one or more groups selected from the group consisting of a hydroxy group, a carboxy group, an oxirane group, and an oxetane group, in addition to the repeating unit A and the repeating unit B.

5. The bio-electrode composition according to claim 1 , further comprising a carbon material, an ITO particle, or a particle coated with a metal selected from silver, gold, platinum, copper, and nickel.

6. The bio-electrode composition according to claim 5 , wherein the carbon material is either or both of carbon black and carbon nanotube.

7. A bio-electrode comprising an electro-conductive base material and a living body contact layer formed on the electro-conductive base material;
wherein the living body contact layer is a cured material of the bio-electrode composition according to claim 1 .

8. The bio-electrode according to claim 7 , wherein the electro-conductive base material comprises one or more species selected from gold, silver, silver chloride, platinum, aluminum, magnesium, tin, tungsten, iron, copper, nickel, stainless, chromium, titanium, and carbon.

9. A method for manufacturing a bio-electrode having an electro-conductive base material and a living body contact layer formed on the electro-conductive base material, comprising:
applying the bio-electrode composition according to claim 1 onto the electro-conductive base material; and curing the bio-electrode composition; thereby forming the living body contact layer.

10. A method for manufacturing a bio-electrode having an electro-conductive base material and a living body contact layer formed on the electro-conductive base material, comprising:
applying the bio-electrode composition according to claim 2 onto the electro-conductive base material; and curing the bio-electrode composition; thereby forming the living body contact layer.

11. A method for manufacturing a bio-electrode having an electro-conductive base material and a living body contact layer formed on the electro-conductive base material, comprising:
applying the bio-electrode composition according to claim 3 onto the electro-conductive base material; and curing the bio-electrode composition; thereby forming the living body contact layer.

12. A method for manufacturing a bio-electrode having an electro-conductive base material and a living body contact layer formed on the electro-conductive base material, comprising:
applying the bio-electrode composition according to claim 4 onto the electro-conductive base material; and curing the bio-electrode composition; thereby forming the living body contact layer.

13. A method for manufacturing a bio-electrode having an electro-conductive base material and a living body contact layer formed on the electro-conductive base material, comprising:
applying the bio-electrode composition according to claim 5 onto the electro-conductive base material; and curing the bio-electrode composition; thereby forming the living body contact layer.

14. A method for manufacturing a bio-electrode having an electro-conductive base material and a living body contact layer formed on the electro-conductive base material, comprising:
applying the bio-electrode composition according to claim 6 onto the electro-conductive base material; and curing the bio-electrode composition; thereby forming the living body contact layer.

15. The method for manufacturing a bio-electrode according to claim 9 , wherein the electro-conductive base material comprises one or more species selected from gold, silver, silver chloride, platinum, aluminum, magnesium, tin, tungsten, iron, copper, nickel, stainless, chromium, titanium, and carbon.

16. The method for manufacturing a bio-electrode according to claim 10 , wherein the electro-conductive base material comprises one or more species selected from gold, silver, silver chloride, platinum, aluminum, magnesium, tin, tungsten, iron, copper, nickel, stainless, chromium, titanium, and carbon.

17. The method for manufacturing a bio-el

Assignees

• Shinetsu Chemical Co

Inventors

• Hatakeyama Jun
• Hasegawa Koji
• Watanabe Osamu
• Iwabuchi Motoaki

Classifications

• A61B5/265

  containing silver or silver chloride · CPC title

• A61B5/27

  Conductive fabrics or textiles · CPC title

• A61B5/251

  Means for maintaining electrode contact with the body · CPC title

• A61B5/266

  containing electrolytes, conductive gels or pastes · CPC title

• A61B5/268

  containing conductive polymers, e.g. PEDOT:PSS polymers · CPC title