Method for producing positive electrode active material for nonaqueous electrolyte secondary batteries, positive electrode active material for nonaqueous electrolyte secondary batteries, and nonaqueous electrolyte secondary battery

Patent metadata

Field	Value
Publication number	US-11069884-B2
Application number	US-201414914188-A
Country	US
Kind code	B2
Filing date	May 29, 2014
Priority date	Aug 28, 2013
Publication date	Jul 20, 2021
Grant date	Jul 20, 2021

Abstract

A method produces a positive electrode active material that does not impair the original battery characteristics of the positive electrode active material. The method can improves water resistance, and suppress the gelation of a positive electrode mixture material paste. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries can include a mixing step of preparing a mixture including fine carbon particles, an organic dispersant, a hydrophobic coat forming agent, an organic solvent, and positive electrode active material particles, a drying step of drying the mixture to obtain the mixture containing the organic solvent in a reduced amount, and a heat treatment step of heat-treating the mixture containing the organic solvent in the reduced amount to obtain a coated positive electrode active material.

First claim

The invention claimed is:

1. A method for producing a positive electrode active material comprising: positive electrode active material particles each serving as a core; and a coating layer on each of the positive electrode active material particles, the coating layer comprising fine carbon particles of average particle diameter of 10 to 100 nm, an organic dispersant, and a hydrophobic coat forming agent, the method comprising:
a mixing step of preparing a mixture comprising the fine carbon particles, the organic dispersant, the hydrophobic coat forming agent, the organic solvent, and the positive electrode active material particles;
a drying step of drying the mixture to obtain the mixture containing the organic solvent in a reduced amount; and
a heat treatment step of heat-treating the mixture containing the organic solvent in the reduced amount to obtain the positive electrode active material having the coating layer comprising at least the fine carbon particles, the organic dispersant, and the hydrophobic coat forming agent,
wherein the fine carbon particles are dispersed in the coating layer,
wherein the hydrophobic coat forming agent is prepared using hydroxyl-containing polydimethylsiloxane, and
wherein the organic dispersant contains a polycarboxylic acid polymeric dispersant.

2. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the mixing step comprises previously mixing the fine carbon particles, the organic dispersant, the hydrophobic coat forming agent, and at least part of the organic solvent to obtain a carbon-containing composition (1) and then mixing the carbon-containing composition (1) and other components to prepare the mixture.

3. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the mixing step comprises previously mixing the fine carbon particles, the organic dispersant, and at least part of the organic solvent to obtain a carbon-containing composition (2) and then mixing the carbon-containing composition (2) and other components to prepare the mixture.

4. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the mixing step comprises preparing the mixture in such a manner that an average particle diameter of the fine carbon particles in the mixture is 10 to 100 nm.

5. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the organic solvent in the mixture is a solvent obtained by mixing at least one selected from lower alcohols consisting of 2-propanol and ethanol and at least one selected from glycols consisting of ethylene glycol, propylene glycol, and hexylene glycol.

6. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the mixing step comprises adjusting viscosity of the mixture so that the viscosity is in a range of 100 to 10000 mPa·s.

7. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the mixing step comprises preparing the mixture using a rotation-revolution kneading mixer.

8. The method for producing a positive electrode active material for nonaqueous electrolyte secondary batteries of claim 1 , wherein the heat treatment step comprises controlling a heat treatment temperature to a range of 80 to 400° C. in an atmosphere selected from an oxygen-containing atmosphere, an inert atmosphere, and a vacuum atmosphere.

9. A positive electrode active material for nonaqueous electrolyte secondary batteries, the positive electrode active material comprising:
positive electrode active material particles each serving as a core, and
a coating layer on each of the positive electrode active material particles,

wherein the coating layer comprises
fine carbon particles of average particle diameter of 10 to 100 nm,
an organic dispersant, and
a hydrophobic coat forming agent,
wherein the fine carbon particles are dispersed in the coating layer,
wherein the hydrophobic coat forming agent is prepared using hydroxyl-containing polydimethylsiloxane, and
wherein the organic dispersant contains a polycarboxylic acid polymeric dispersant.

10. The positive electrode active material for nonaqueous electrolyte secondary batteries of claim 9 , wherein the positive electrode active material particles are formed of one or more selected from the group consisting of a lithium-nickel composite oxide, a lithium-cobalt composite oxide, a lithium-nickel-cobalt-manganese composite oxide, and a lithium-manganese composite oxide.

11. The positive electrode active material for nonaqueous electrolyte secondary batteries of claim 9 , wherein if 1 g of the positive electrode active material for nonaqueous electrolyte secondary batteries is added to 50 ml of pure water of 24° C. to prepare slurry and then the slurry is left alone for 60 minutes, then pH of the slurry at 24° C. is 11 or less, and then conductivity thereof is 200 μS/cm or less, and
if the positive electrode active material is exposed to a thermohygrostat having a temperature of 30° C. and a humidity of 70% RH for six days, the rate of increase of a mass of the positive electrode active material after exposure with respect to the mass thereof before the exposure is 1.0% or less.

12. The positive electrode active material for nonaqueous electrolyte secondary batteries of claim 9 , wherein the positive electrode active material particles represented by the following general formula (1):
Li a Ni 1-b M b O 2   General Formula (1)

where M represents at least one element selected from transition metal elements other than Ni, Group 2 elements, and Group 13 elements; 1.00≤a≤1.10, and 0.01≤b≤0.5.

13. The positive electrode active material for nonaqueous electrolyte secondary batteries of claim 9 , wherein the positive electrode active material particles represented by the following general formula (2):
Li t Ni 1-x-y Co x M y O 2   General Formula (2)

where M represents at least one element selected from the group consisting of Mg, Al, Ca, Ti, V, Cr, Mn, Zr, Nb, Mo, and W; 0.95≤t≤1.20; 0≤x≤0.22; and 0≤y≤0.1.

14. The positive electrode active material for nonaqueous electrolyte secondary batteries of claim 9 , wherein the content of the hydrophobic coat forming agent is 0.1 to 5 parts by mass of the positive electrode active material particles serving as the core.

15. A nonaqueous electrolyte secondary battery comprising:
a positive electrode comprising a positive electrode active material and a conductive material;
a negative electrode comprising a negative electrode active material;
a separator; and
a nonaqueous electrolyte, wherein
the positive electrode active material for nonaqueous electrolyte secondary batteries of claim 9 is used as the positive electrode active material.

Assignees

• Sumitomo Metal Mining Co

Inventors

• Takanashi Shoji
• Komukai Tetsufumi

Classifications

• C01G53/42

  containing alkali metals, e.g. LiNiO2 · CPC title

• H01M4/505

  of mixed oxides or hydroxides containing manganese for inserting or intercalating light metals, e.g. LiMn2O4 or LiMn2OxFy · CPC title

• C01P2006/12

  Surface area · CPC title

• H01M4/587

  for inserting or intercalating light metals · CPC title

• H01M10/052

  Li-accumulators · CPC title