Very soft, non-sticky and transparent styrenic thermoplastic elastomer composition

Patent metadata

Field	Value
Publication number	US-11066503-B2
Application number	US-201816492768-A
Country	US
Kind code	B2
Filing date	Mar 12, 2018
Priority date	Mar 16, 2017
Publication date	Jul 20, 2021
Grant date	Jul 20, 2021

Abstract

Thermoplastic elastomer compositions can be used for medical skin contact applications, comprising: a) 90.9 to 69.0 wt.-% star-shaped block copolymer A with 4 arms of the general structure [S 1 —(S/B) k —(S/B) I —(S/B) m —S 2 ] n —X, where S 1 and S 2 are vinylaro-matic hard polymer and S/B are soft random vinylaromatic/diene copolymer blocks; X is a coupling center; and b) 9.1 to 31.0 wt.-% of a plasticizer B: b1) a mixture of mineral oil B1 and cyclohexane 1,2-dicarboxylic acid C 8 to C 10 dialkyl ester B2; or b2) a mixture of mineral oil B1 and vegetable oil B3.

First claim

The invention claimed is:

1. A thermoplastic elastomer composition comprising components a), b), and c):
a) 90.9 to 69.0 wt.-% of at least one star-shaped block copolymer A of the structure
[S 1 −(S/B) k −(S/B) l −(S/B) m −S 2 ] n −X  (I),

where S 1 and S 2 are polymer blocks made from at least one vinylaromatic monomer and S/B are random copolymer blocks made from at least one vinylaromatic monomer and at least one diene forming a soft phase; X is a coupling center derived from a polyfunctional coupling agent;
b) 9.1 to 31.0 wt.-% of a plasticizer B; and
c) 0 to 2.0 wt.-% of further additives C;
wherein the sum of components a), b), and c) is 100 wt.-%;
the arms S 1 −(S/B) k −(S/B) m −(S/B) m −S 2 are identical;
the proportion of the blocks S 1 and S 2 (forming a hard phase), based on the entire block copolymer A, is from 24 to 40 wt.-%;
the vinylaromatic monomer/diene (=S/B) ratio of all of the blocks (S/B) is from 1/0.45 to 1/2.5;
the S/B-ratio of the blocks (S/B) k , (S/B) l and (S/B) m is different from each other; the S/B-ratio of the blocks (S/B) k and (S/B) m is lower than the S/B-ratio of the block(s) (S/B) l ;
the weight ratio of blocks S 2 /S 1 is from 0.1 to 0.8; and
the weight average molar mass M w (determined by GPC according to ISO 16014-3:2012) of the block copolymer A is from 220000 to 450000 g/mol;
n is a natural number from 1 to 8;
k and m are 1; and
l is a natural number of at least 1; and
the plasticizer B is
b1) a mixture composed of mineral oil B1 and at least one cyclohexane 1,2-dicarboxylic acid C 8 to C 10 dialkyl ester B2; or
b2) a mixture composed of mineral oil B1 and at least one vegetable oil B3 having an iodine value (g/100 g) of no more than 130.

2. The thermoplastic elastomer composition according to claim 1 , wherein the plasticizer in plasticizer mixture b1) or b2) the weight ratio of component B1 to component B2 or B1 to B3 is 80:20 to 40:60.

3. The thermoplastic elastomer composition according to claim 1 , wherein the plasticizer B is mixture b2).

4. The thermoplastic elastomer composition according to claim 1 , wherein the vegetable oil B3 is selected from the group consisting of: rapeseed oil, sunflower oil, grape seed oil, palm oil, olive oil, coconut oil, palm kernel oil, cocoa butter, jojoba oil, cottonseed oil, corn oil, wheat germ oil, soybean oil, peanut oil, castor oil, sesame oil, and rice brain oil.

5. The thermoplastic elastomer composition according to claim 1 , wherein the vegetable oil B3 is rapeseed oil.

6. The thermoplastic elastomer composition according to claim 1 , which melt mass flow index (measured on a polymer melt at 200° C. and 5 kg load according to ISO 1133-1:2011) is in the range of from 8 to 16 cm 3 /10 min.

7. The thermoplastic elastomer composition according to claim 1 comprising 9.1 to 20.0 wt.-% of plasticizer B (component b)) and the Mw of block copolymer A is 250000 to 320000 g/mol.

8. The thermoplastic elastomer composition according to claim 1 comprising more than 20 wt.-% of plasticizer B (component b)) and the Mw of block copolymer A is 325000 to 410000 g/mol.

9. The thermoplastic elastomer composition according to claim 1 , wherein n is a natural number from 3 to 5.

10. The thermoplastic elastomer composition according to claim 1 , wherein X is a coupling center derived from epoxidized linseed oil or epoxidized soybean oil.

11. The thermoplastic elastomer composition according to claim 1 , wherein Mw of the polymer block S 1 is in the range of from 22900 to 54000 g/mol, and Mw of the polymer block S 2 is in the range of from 5000 to 12000 g/mol.

12. The thermoplastic elastomer composition according to claim 1 , wherein the weight ratio of blocks S 2 /S 1 of block copolymer A is from 0.1 to 0.6.

13. The thermoplastic elastomer composition according to claim 1 , wherein the S/B-ratio of the copolymer block (S/B) k is from 0.5 to 1.0; the S/B-ratio of the copolymer block(s) (S/B) l is from 0.5 to 1.2; and the S/B-ratio of the copolymer block (S/B) m is from 0.3 to 0.8.

14. The thermoplastic elastomer composition according to claim 1 , wherein the weight average molar mass M w of the copolymer blocks (S/B) k , (S/B) l and (S/B) m is different from each other;
Mw (S/B) k is in the range of from 16500 to 40000 g/mol; Mw (S/B) l is in the range of from 25800 to 60800 g/mol; and Mw (S/B) m is in the range of from 14300 to 33800 g/mol.

15. A process for the preparation of a thermoplastic elastomer composition according to claim 1 , wherein component a) is introduced continuously into an extruder and then component b) and optionally further components c) are metered in.

16. A process for the preparation of a thermoplastic elastomer composition according to claim 1 , wherein component b) and optional component c)—as such or in solution—are added into a solution of block copolymer A, then to homogenize the liquids, and subsequently to free the product from the solvent.

17. A shaped article produced from the thermoplastic elastomer composition according to claim 1 .

18. A star-shaped block copolymer A of the structure
[S 1 −(S/B) k −(S/B) l −(S/B) m −(S/B) m −S 2 ] n −X  (I),

wherein:
S 1 and S 2 are polymer blocks made from at least one vinylaromatic monomer and S/B are random copolymer blocks made from at least one vinylaromatic monomer and at least one diene forming a soft phase;
X is a coupling center derived from a polyfunctional coupling agent;
the arms S 1 −(S/B) k −(S/B) m −(S/B) m −S 2 are identical;
the proportion of the blocks S 1 and S 2 (forming a hard phase), based on the entire block copolymer A, is from 24 to 40 wt.-%;
the vinylaromatic monomer/diene (=S/B) ratio of all of the blocks (S/B) is from 1/0.45 to 1/2.5;
the S/B-ratio of the blocks (S/B) k , (S/B) l , and (S/B) m is different from each other;

the S/B-ratio of the blocks (S/B) k and (S/B) m is lower than the S/B-ratio of the block(s) (S/B) l ;
the weight ratio of blocks S 2 /S 1 is from 0.1 to 0.8;
the weight average molar mass M w (determined by GPC according to ISO 16014-3:2012) of the block copolymer A is from 220000 to 450000 g/mol;
n is a natural number from 1 to 8;
k and m are 1; and
l is a natural number of at least 1.

19. A process for the preparation of block copolymer A of formula (I) according to claim 18 characterized by
i) a single initiation;
ii) first addition and polymerization of vinyl aromatic monomer;
iii) at least 3 times addition and polymerization of vinyl aromatic monomer and diene mixture;
iv) second addition and polymerization of vinyl aromatic monomer; and
v) a coupling step after the addition and polymerization of the vinylaromatic monomers of the last polymer block.

20. The shaped article of claim 17 , wherein the shaped article is a medical article.

21. The shaped article of claim 20 , wherein the medical article is for skin contact applications or intravenous applications.

22. An elastic and flexible molding produced from the thermoplastic elastomer composition according to claim 1 .

Assignees

• Ineos Styrolution Group Gmbh

Inventors

• Verswyvel Michiel
• Niessner Norbert
• Jahnke Eike
• Wagner Daniel
• Knoll Konrad

Classifications

• C08L2203/02

  for biomedical use · CPC title

• C08L91/00

  Compositions of oils, fats or waxes; Compositions of derivatives thereof · CPC title

• C08L53/02 Primary

  of vinyl-aromatic monomers and conjugated dienes · CPC title

• C08K5/12

  of cyclic polycarboxylic acids · CPC title

• C08K5/103

  with polyalcohols · CPC title