Cross-linkable coating compositions based on organyl oxysilane-terminated polymers

Patent metadata

Field	Value
Publication number	US-11059970-B2
Application number	US-201616321058-A
Country	US
Kind code	B2
Filing date	Aug 3, 2016
Priority date	Aug 3, 2016
Publication date	Jul 13, 2021
Grant date	Jul 13, 2021

Abstract

Crosslinkable compositions especially useful for coatings containing an alkoxysilyoxy-terminated polymer and a silicone resin.

First claim

The invention claimed is:

1. A crosslinkable floor coating composition (M), comprising:
(A) 100 parts by weight of compounds of formula
Y—[(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] x   (I),

wherein
Y is an x-valent polymer radical bonded via nitrogen, oxygen, sulfur or carbon to a carbon of the (CR 1 2 ) group, and which has a number-average molecular mass of 200 to 10,000 g/mol and which contains no aromatic structural elements having nitrogen or oxygen atoms bonded directly to an aryl ring of the aromatic structure,
R are identical or different and are monovalent, optionally substituted SiC-bonded hydrocarbon radicals,
R 1 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical that may be attached to the carbon atom via nitrogen, phosphorus, oxygen, sulfur or a carbonyl group,
R 2 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical,
x is an integer from 1 to 10,
a is identical or different and is 0, 1 or 2, and
b is identical or different and is an integer from 1 to 10 and
(B) at least 100 parts by weight of silicone resin(s) containing units of formula
R 3 c (R 4 O) d R 5 e SiO (4-c-d-e)/2   (II),

wherein
R 3 are identical or different and are hydrogen, a monovalent, SiC-bonded, optionally substituted aliphatic hydrocarbon radical or a divalent, optionally substituted aliphatic hydrocarbon radical that bridges two units of formula (II),
R 4 are identical or different and are hydrogen or a monovalent, optionally substituted hydrocarbon radical,
R 5 are identical or different and represents a monovalent, SiC-bonded, optionally substituted aromatic hydrocarbon radical,

c is 0, 1, 2 or 3,
d is 0, 1, 2 or 3 and
e is 0, 1 or 2,
with the proviso that the sum of c+d+e is less than or equal to 3 and in at least 40% of the units of formula (II) the sum of c+e is 0 or 1,
wherein
the composition (M) contains less than 100 parts by weight of compounds (C1) of formula
Y 1 —[(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] x   (I′),

wherein Y 1 is an x-valent polymer radical bonded via nitrogen, oxygen, sulfur or carbon which has a number-average molecular mass M n of more than 10,000 g/mol and R, R 1 , R 2 , a, b and x are as defined in formula (I) and in each case are identical or different.

2. The crosslinkable floor coating composition of claim 1 , wherein the composition (M) contains less than 10 parts by weight of organic solvents based on 100 parts by weight of the composition (M) according to the invention.

3. The crosslinkable floor coating composition of claim 1 , wherein the composition (M) contains less than 100 parts by weight of compounds (C2) of formula
Y 2 —[(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] x   (I″),

wherein Y 2 is an x-valent polymer radical bonded via nitrogen, oxygen, sulfur or carbon which contains aromatic structural elements comprising nitrogen or oxygen atoms bonded directly to an aryl ring of the aromatic structural element and R, R 1 , R 2 , a, b and x are as defined in formula (I) and in each case are identical or different.

4. The crosslinkable floor coating composition as claimed in claim 1 , wherein radical Y in formula (I) is a polyoxypropylene radical having a number-average molecular mass of 200 to 10,000 g/mol.

5. The crosslinkable floor coating composition of claim 1 , wherein radical Y in formula (I) is a polyoxypropylene radical having a number-average molecular mass of 500 to 8000 g/mol.

6. The crosslinkable floor coating composition of claim 1 , comprising, based on 100 parts by weight of component (A), at least 200 parts by weight of component (B).

7. The crosslinkable floor coating composition of claim 1 , wherein said composition contains
(A) 100 parts by weight of compounds of formula (I) and
(B) at least 100 parts by weight of silicone resins containing units of formula (II) and at least one further component selected from:
(D) nitrogen-containing organosilicon compound,
(E) catalysts,
(F) adhesion promoters,
(G) water scavengers,
(H) fillers,
(I) additives and
(J) admixture agents.

8. The crosslinkable floor coating composition of claim 1 , wherein in the compounds (A) of formula (I), Y is a polyether, a polyester, a polyurethane or mixture thereof, bonded to the [(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] groups by —O—, —O—C(═O)—NH—, and mixtures thereof.

9. The crosslinkable floor coating composition of claim 1 , wherein Y is a polyether, polyester, polyurethane, or mixture thereof, bonded to the [(CR 1 2 ) b —SiR a (OR 2 ) 3-a ] groups by —O—C(═O)—NH— and —NH—C(═O)—NH groups, wherein of these two latter groups ≥85 mol percent are —O—C(═O)—NH— groups.

10. A process for producing the crosslinkable floor coating composition of claim 1 , comprising mixing the individual components in any desired sequence.

11. A process for producing a floor coating in which a floor coating composition of claim 1 is applied to at least one substrate and subsequently allowed to undergo crosslinking.

12. A floor coating produced by crosslinking a composition of claim 1 .

Assignees

• Wacker Chemie Ag

Inventors

• Stanjek Volker
• Anders Udo
• Reitmajer Kurt
• Zander Lars

Classifications

• C09D183/04 Primary

  Polysiloxanes · CPC title

• C08G77/80

  Siloxanes having aromatic substituents, e.g. phenyl side groups · CPC title

• C08L83/04 Primary

  Polysiloxanes · CPC title

• C08L2312/08

  by silane · CPC title

• C09D7/40

  Additives · CPC title