Method for joining heat transfer plates of a plate heat exchanger

Patent metadata

Field	Value
Publication number	US-11059092-B2
Application number	US-201716080486-A
Country	US
Kind code	B2
Filing date	Mar 20, 2017
Priority date	Mar 31, 2016
Publication date	Jul 13, 2021
Grant date	Jul 13, 2021

Abstract

A method for joining heat transfer plates, comprising: applying a melting depressant composition on individual application areas of a first metal sheet, each application area comprising a mid-section and two end-sections; pressing ridges and grooves in the metal sheet, the ridges extending in a direction that extends between the end-sections of the application areas, such that the application areas are located on top of the ridges; bringing the metal sheet into contact with a second, pressed metal sheet, such that contact points are formed where the mid-sections of the application areas relocated; heating the sheets until melted metal is formed at the application areas where the melting depressant composition is applied; and allowing the melted metal to solidify such that a joint is obtained at the contact points.

First claim

The invention claimed is:

1. A method for joining heat transfer plates of a plate heat exchanger, the method comprising
applying a melting depressant composition on a surface of a first metal sheet and in a pattern on the first metal sheet, the pattern comprising a plurality of individual application areas where the melting depressant composition is applied, the plurality of individual application areas being spaced apart from one another, each application area comprising a mid-section, and a first end section and a second end-section that are located on a respective side of the mid-section, each of the plurality of application areas having an elongated shape that extends in a direction from the first end-section to the second end-section, each of the plurality of application areas having a length as measured in the direction from the first end-section to the second end-section, each of the plurality of application areas also having a width as measured in a direction perpendicular to the length, each of the plurality of application areas being configured so that the length of the application area is at least three times greater than the width of the application area at the mid-section of the application area,
pressing a plurality of ridges and grooves in the first metal sheet, each of the plurality of ridges extending in the direction that extends from the first end-section to the second end-section of a plurality of the application areas, such that the application areas are located on top of and along the ridges, the pressing of the plurality of ridges and grooves in the first metal sheet occurring after the applying of the melting depressant composition on the surface of the first metal sheet, the pressing of the plurality of ridges and grooves in the first metal sheet resulting in a plurality of the application areas having the elongated shape being positioned on top of, and spaced apart along, each of the plurality of ridges,
bringing the pressed first metal sheet into contact with a second, pressed metal sheet, such that contact points are formed between the metal sheets where the mid-sections of the application areas are located,
heating the first and second metal sheets until said surface of the first metal sheet melts and forms melted metal at the areas where the melting depressant composition is applied, at the contact points between the sheets, and
allowing the melted metal to solidify, such that joints are obtained at the contact points.

2. A method according to claim 1 , wherein the length of each of the plurality of application areas is at least five times greater than the width of the application area at the mid-section of the application area.

3. A method according to claim 1 , wherein the width of the first and second end-sections of each of the plurality of application areas is greater than the width of the mid-section of the application area.

4. A method according to claim 3 , wherein the width of the first and second end-sections of each application area is at least 50% wider than the width of the mid-section of the application area.

5. A method according to claim 1 , wherein the ridges and grooves form a heat transfer area of the metal sheet, and wherein maximum 50% of the heat transfer area is covered by the applied melting depressant composition.

6. A method according to claim 1 , wherein the ridges and grooves form a heat transfer area of the metal sheet, and wherein minimum 20% of the heat transfer area is covered by the applied melting depressant composition.

7. A method according to claim 1 , wherein the melting depressant composition comprises
a melting depressant component that comprises at least 25 wt % silicon for decreasing a melting temperature of the first metal sheet, and
a binder component.

8. A method according to claim 1 , wherein the melting depressant composition comprises less than 50 wt % metallic elements.

9. A method according to claim 1 , wherein each joint comprises at least 50 wt % metal that, before the heating, was part of any of the first metal sheet and the second metal sheet.

10. A method according to claim 1 , wherein the melting depressant composition comprises
a melting depressant component that comprises at least 85 wt % silicon for decreasing a melting temperature of the first metal sheet, and
a binder component for facilitating the applying of the melting depressant composition on the surface.

11. A method according to claim 1 , wherein the melting depressant composition comprises less than 10 wt % metallic elements.

12. A method according to claim 1 , wherein each joint comprises at least 70 wt % metal that, before the heating, was part of any of the first metal sheet and the second metal sheet.

13. A method for joining heat transfer plates of a plate heat exchanger, the method comprising
applying a melting depressant composition on a surface of a first metal sheet and in a pattern on the first metal sheet, the pattern comprising a plurality of individual application areas where the melting depressant composition is applied, the plurality of individual application areas being spaced apart from one another so that regions devoid of melting depressant composition are located between the application areas, each of the plurality of application areas comprising a mid-section, a first end section and a second end-section, the first and second end sections of each of the plurality of application areas being located at opposite sides of the mid-section of the application area so that the mid-section of each of the plurality of application areas is positioned between the first and second end sections of the application area, each of the plurality of application areas having an elongated shape that is elongated in a direction from the first end-section to the second end-section, each of the plurality of application areas having a lenth as measured in the direction from the first end-section to the second end-section, each of the plurality of application areas also having a width as measured in a direction perpendicular to the length, the width of the first end-section of each of the plurality of application areas being greater than the width of the mid-section of the respetive application area;
pressing a plurality of ridges and grooves in the first metal sheet so that each of the plurality of ridges extends in the direction from the first end-section to the second end-section of several of the application areas, the pressing of the plurality of ridges and grooves in the first metal sheet occurring after the applying of the melting depressant composition on the surface of the first metal sheet, the pressing of the plurality of ridges and grooves in the first metal sheet resulting in a plurality of the application areas having the elongated shape being positioned on top of, and spaced aport along, each of the plurality of ridges;
bringing the pressed first metal sheet into contact with a second, pressed metal sheet, such that contact points are formed between the metal sheets where the mid-sections of the application areas are located;
heating the first and second metal sheets until said surface of the first metal sheet melts and forms melted metal at the areas where the melting depressant composition is applied, at the contact points between the sheets; and
allowing the melted metal to solidify, such that joints are obtained at the contact points.

14. A method according to claim 13 , wherein, each of the plurality of application areas is configured so that the length of the application area is at least three times greater than the width of the application area at a mid-section of the appli

Assignees

• Alfa Laval Corp Ab

Inventors

• Sjödin Per
• Walter Kristian

Classifications

• B23K1/0012

  Brazing of heat exchangers · CPC title

• B23K33/00

  Specially-profiled edge portions of workpieces for making soldering or welding connections; Filling the seams formed thereby · CPC title

• B23K3/0607

  Solder feeding devices · CPC title

• B23K1/0008

  specially adapted for particular articles or work · CPC title

• B23P15/00 Primary

  Making specific metal objects by operations not covered by a single other subclass or a group in this subclass · CPC title