Polychromatic articles and methods of making the same

Patent metadata

Field	Value
Publication number	US-11053159-B2
Application number	US-201816190712-A
Country	US
Kind code	B2
Filing date	Nov 14, 2018
Priority date	Dec 13, 2017
Publication date	Jul 6, 2021
Grant date	Jul 6, 2021

Abstract

An article includes SiO 2 from about 40 mol % to about 80 mol %, Al 2 O 3 from about 1 mol % to about 20 mol %, B 2 O 3 from about 3 mol % to about 50 mol %, WO 3 plus MoO 3 from about 1 mol % to about 18 mol % and at least one of: (i) Au from about 0.001 mol % to about 0.5 mol %, (ii) Ag from about 0.025 mol % to about 1.5 mol %, and (iii) Cu from about 0.03 mol % to about 1 mol %, and R 2 O from about 0 mol % to about 15 mol %. The R 2 O is one or more of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O. R 2 O minus Al 2 O 3 ranges from about −12 mol % to about 3.8 mol %.

First claim

What is claimed is:

1. An article, comprising:
SiO 2 from 40 mol % to 80 mol %;
Al 2 O 3 from 1 mol % to 20 mol %;
B 2 O 3 from 3 mol % to 50 mol %;
WO 3 plus MoO 3 from 1 mol % to 18 mol %;
at least one of: (i) Au from 0.001 mol % to 0.5 mol %, (ii) Ag from 0.025 mol % to 1.5 mol %, and (iii) Cu from 0.03 mol % to 1 mol %; and
R 2 O from 0 mol % to 15 mol %, wherein the R 2 O is one or more of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O,
wherein R 2 O minus Al 2 O 3 ranges from −12 mol % to 3.8 mol %.

2. The article of claim 1 , wherein the Ag is from 0.1 mol % to 1 mol %.

3. The article of claim 1 , wherein the Au is from 0.001 mol % to 0.5 mol %.

4. The article of claim 1 , wherein the Cu is from 0.03 mol % to 1 mol %.

5. The article of claim 1 , wherein the article comprises WO 3 from 0 mol % to 15 mol %.

6. The article of claim 1 , wherein the article comprises MoO 3 from 0 mol % to 15 mol %.

7. The article of claim 1 , wherein the Al 2 O 3 is from 7 mol % to 15 mol %.

8. The article of claim 1 , further comprising:
RO from 0.01 mol % to 2 mol %, wherein the RO is one or more of MgO, CaO, SrO and BaO.

9. The article of claim 1 , wherein the R 2 O minus Al 2 O 3 ranges from −8 mol % to 3.8 mol %.

10. An article, comprising:
SiO 2 from 60 mol % to 72 mol %;
Al 2 O 3 from 7 mol % to 12 mol %;
B 2 O 3 from 8 mol % to 15 mol %;
WO 3 plus MoO 3 from 3 mol % to 6 mol %;
RO from 0 mol % to 0.5 mol %, wherein the RO is one or more of MgO, CaO, SrO, BaO;
at least one of: (i) Au from 0.001 mol % to 0.5 mol %, (ii) Ag from 0.025 mol % to 1.5 mol %, and (iii) Cu from 0.03 mol % to 1 mol %; and
R 2 O from 7 mol % to 12 mol %, wherein R 2 O is one or more of Li 2 O, Na 2 O, K 2 O, Rb 2 O and Cs 2 O,
wherein R 2 O minus Al 2 O 3 ranges from −5 mol % to 1.5 mol %.

11. The article of claim 10 , further comprising:
at least one dopant selected from the group consisting of Ti, V, Cr, Mn, Fe, Co, Ni, Se, Nb, Tc, Ru, Rh, Pd, Cd, Te, Ta, Re, Os, Ir, Pt, Tl, Pb, Bi, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu.

12. The article of claim 10 , further comprising:
V 2 O 5 from 0.0001 mol % to 0.5 mol %.

13. The article of claim 10 , wherein the WO 3 is from 0 mol % to 4 mol %.

14. The article of claim 10 , wherein the MoO 3 is from 0 mol % to 4 mol %.

15. The article of claim 10 , wherein the article comprises a plurality of crystalline precipitates comprising at least one of WO 3 and MoO 3 .

16. The article of claim 10 , further comprising:
a compressive stress region.

17. An article, comprising:
SiO 2 from 40 mol % to 80 mol %;
Al 2 O 3 from 1 mol % to 20 mol %;
B 2 O 3 from 3 mol % to 50 mol %;
WO 3 plus MoO 3 from 1 mol % to 18 mol %;
at least one of: (i) Au from 0.001 mol % to 0.5 mol %, (ii) Ag from 0.025 mol % to 1.5 mol %, and (iii) Cu from 0.03 mol % to 1 mol %; and
a plurality of crystalline precipitates comprising: (i) at least one of Au, Ag and Cu; and (ii) at least one of W and Mo.

18. The article of claim 17 , further comprising:
a plurality of metallic Ag particles proximate a surface of the article.

19. The article of claim 17 , wherein the article exhibits a set of transmitted color coordinates having: an L* value of from 14 to 90, an a* value from −18.6 to 49 and a b* value from −7.8 to 53.5 at a thickness of 0.5 mm under D65-10 illumination.

20. The article of claim 17 , wherein the article exhibits an average transmittance of from 0.01% to 49% over a wavelength band of from 280 nm to 380 nm at a 0.5 mm thickness.

21. The article of claim 17 , wherein the article exhibits an average transmittance of from 0.8% to 86% over a wavelength band of from 400 nm to 700 nm at a 0.5 mm thickness.

22. The article of claim 21 , wherein the article exhibits a scattering of 25% or less over a wavelength band of 400 nm to 700 nm at a thickness of 1 mm.

23. The article of claim 17 , wherein the article exhibits an average transmittance of from 0.13% to 88.7% over a wavelength band of from 700 nm to 2000 nm at a 0.5 mm thickness.

Assignees

• Corning Inc

Inventors

• Dejneka Matthew John
• Kohl Jesse
• Logunov Stephan Lvovich
• Moore Galan Gregory

Classifications

• C03C10/0054

  containing PbO, SnO2, B2O3 · CPC title

• C03C2214/08

  Metals · CPC title

• C03C10/0045

  containing SiO2, Al2O3 and MgO as main constituents · CPC title

• C03C2214/16

  Microcrystallites, e.g. of optically or electrically active material · CPC title

• C03C14/006

  the non-glass component being in the form of microcrystallites, e.g. of optically or electrically active material · CPC title