Weld schedule for resistance spot welding of aluminum alloy workpieces

Patent metadata

Field	Value
Publication number	US-11045894-B2
Application number	US-201815953546-A
Country	US
Kind code	B2
Filing date	Apr 16, 2018
Priority date	Aug 25, 2011
Publication date	Jun 29, 2021
Grant date	Jun 29, 2021

Abstract

Aluminum-base alloy workpieces have surfaces with films of aluminum oxide which inhibit good contact with weld faces of resistance spot weld electrodes and the faying surfaces of, for example, sheet workpieces stacked for welding. Sometimes, the surfaces of the sheets also are coated with an adhesive or a sealer which further complicates welding. But in accordance with this invention, weld faces of opposing, round, copper welding electrodes are pressed against opposite outside surfaces of the sheets at a spot weld site and weld current is applied to the electrodes in accordance with a three-stage weld schedule to better form each weld. The weld schedule comprises a Conditioning stage (stage 1), a weld nugget Shaping stage (stage 2), and a weld nugget Sizing stage (stage 3).

First claim

The invention claimed is:

1. A method of forming resistance spot welds on aluminum-based alloy workpieces, the method comprising:
forming a stack of two or more aluminum-based alloy workpieces, the two or more aluminum-based alloy workpieces having faying surfaces at a resistance weld site and opposing outer surfaces at the resistance weld site;
pressing weld faces of opposing resistance weld electrodes against the outer surfaces of the two or more aluminum-based alloy workpieces at the resistance weld site; and while pressing the weld faces against the two or more aluminum-based alloy workpieces,
passing a first stage weld current between the opposing resistance weld electrodes and through the two or more aluminum-based alloy workpieces at the opposing resistance weld site for a first stage time of milliseconds, the first stage weld current being ramped to a first stage peak current value that reduces an electrical resistance between the weld faces to a stable resistance value and heats the two or more aluminum-based alloy workpieces for engagement with the weld faces without melting of the two or more aluminum-based alloy workpieces at their faying surfaces, and then, momentarily reducing current flow with the opposing resistance weld electrodes still pressed against the outer surfaces of the two or more aluminum-based alloy workpieces;
passing a second stage weld current between the opposing resistance weld electrodes and through the two or more aluminum-based alloy workpieces at the weld site for a second stage time of milliseconds, the second stage weld current being ramped to a second stage peak value, larger than the first stage peak current value, for initiating a molten weld nugget formation at the faying surfaces of the weld site, and then, reducing current flow with the opposing resistance weld electrodes still pressed against the outer surfaces of the two or more aluminum-based alloy workpieces to stabilize temperature distribution at the faying surfaces of the weld site;
passing a third stage weld current between the opposing resistance weld electrodes and through the two or more aluminum-based alloy workpieces at the weld site for a third stage time of milliseconds, the third stage weld current being at a third stage value, smaller than the second stage peak current value, for completing the molten weld nugget formation of a predetermined weld nugget diameter at the faying surfaces of the weld site, the third stage time being longer than the second stage time, and stopping current flow for cooling of the weld site and solidification of the molten weld nugget; and then
removing the weld faces of the opposing-resistance weld electrodes from contact with the outer surfaces of the two or more aluminum-based alloy workpieces.

2. The method of forming resistance spot welds on aluminum-based alloy workpieces as stated in claim 1 in which the weld faces of the opposing resistance weld electrodes are convex and engage the two or more aluminum-based alloy workpieces with intruding grooves, protruding ridges, or a combination of both, formed on the weld faces.

3. The method of forming resistance spot welds on aluminum-based alloy workpieces as stated in claim 1 in which the weld faces of the opposing resistance weld electrodes are convex and engage the two or more aluminum-based alloy workpieces with roughened surfaces.

4. The method of forming resistance spot welds on aluminum-based alloy workpieces as stated in claim 1 in which the first stage weld current is slowly ramped to a value for removing adhesive or other unwanted non-metallic material at the faying surfaces of the two or more aluminum-based alloy workpieces.

5. The method of forming resistance spot welds on aluminum-based alloy workpieces as stated in claim 1 in which the second stage weld current is ramped to about twenty to about fifty kilo-amperes and the second stage time lasts about six to about fifty milliseconds, the second stage weld current and the second stage time providing for formation of the molten weld nugget of the predetermined weld nugget diameter and centered at a contact area of the weld site of the faying surfaces.

6. The method of forming resistance spot welds on aluminum-based alloy workpieces as stated in claim 1 in which the third stage value is about fifteen to about forty kilo-amperes and the third stage time lasts for a period determined for the formation of a required size of the molten weld nugget depending on a thicknesses of the two or more aluminum-based alloy workpieces.

7. The method of forming resistance spot welds on aluminum-based workpieces as stated in claim 1 in which the third stage weld current is passed between the opposing resistance weld electrodes as two or more pulses with heat times of up to thirty milliseconds and cool times of one to ten milliseconds.

8. A method of forming resistance spot welds on aluminum-based alloy workpieces, the method comprising:
forming a stack of two or more aluminum-based alloy workpieces, the two or more aluminum-based alloy workpieces having faying surfaces at a resistance weld site and opposing outer surfaces at the resistance weld site;
providing a medium frequency direct current (MFDC) using an inverter type weld control that initially receives a three-phase alternating current of set frequency and rms voltage which is converted to a single phase, medium frequency primary current, which is then fed to a MFDC transformer and rectifier to convert to a direct welding secondary current,
pressing weld faces of opposing resistance weld electrodes against the outer surfaces of the two or more aluminum-based alloy workpieces at the resistance weld site; and while pressing the weld faces against the two or more aluminum-based alloy workpieces,
passing a first stage direct weld current between the opposing resistance weld electrodes and through the two or more aluminum-based alloy workpieces at the resistance weld site lasting for a first period of milliseconds, the first stage direct weld current being increased to a first stage peak direct current value that reduces an electrical resistance between the weld faces to a stable resistance value and heats the two or more aluminum-based alloy workpieces for engagement with the weld faces without melting of the two or more aluminum-based alloy workpieces at their faying surfaces, and then, momentarily reducing a primary alternating current flow with the opposing resistance weld electrodes still pressed against the outer surfaces of the two or more aluminum-based alloy workpieces;
passing a second stage direct weld current between the opposing resistance weld electrodes and through the two or more aluminum-based alloy workpieces at the resistance weld site lasting for a second period of milliseconds, the second stage direct weld current being increased to a second stage direct current value, larger than the first stage peak direct current value, for initiating a molten weld nugget formation at the faying surfaces of the resistance weld site, and, when a molten weld nugget of predetermined size has been formed, reducing the primary current flow with the opposing resistance weld electrodes still pressed against the outer surfaces of the two or more aluminum-based alloy workpieces;
passing a third stage direct weld current between the opposing resistance weld electrodes and through the two or more aluminum-based alloy workpieces at the resistance weld site lasting for a third period of milliseconds, the third stage direct weld current being at a third stage rms current value, smaller than the second stage peak direct current value, for completing the molten weld nugget formation at the faying surfaces of the resistance weld site, the third period being longer than the second period,

Assignees

• Gm Global Tech Operations Llc

Inventors

• Sigler David R
• Karagoulis Michael J

Classifications

• B23K11/115 Primary

  by means of two electrodes placed opposite one another on both sides of the welded parts · CPC title

• B23K11/257

  the measured parameter being an electrical current · CPC title

• B23K11/185

  of aluminium or aluminium alloys · CPC title