Methods of making paper products using a molding roll

Patent metadata

Field	Value
Publication number	US-11035077-B2
Application number	US-201716069910-A
Country	US
Kind code	B2
Filing date	Jan 31, 2017
Priority date	Feb 8, 2016
Publication date	Jun 15, 2021
Grant date	Jun 15, 2021

Abstract

A method of making a fibrous sheet. The method includes forming a nascent web from an aqueous solution of papermaking fibers, dewatering the nascent web to form a dewatered web having a consistency from about ten percent solids to about seventy percent solids, moving the dewatered web on a transfer surface, and transferring the dewatered web from the transfer surface to a molding roll at a molding zone. The molding roll includes an exterior and a patterned surface on the exterior of the molding roll. Papermaking fibers of the dewatered web are redistributed on the patterned surface in order to form a molded paper web. The method also includes transferring the molded paper web to a drying section and drying the molded paper web in the drying section to form a fibrous sheet.

First claim

I claim:

1. A method of making a fibrous sheet, the method comprising:
(a) forming a nascent web from an aqueous solution of papermaking fibers;
(b) dewatering the nascent web to form a dewatered web having a consistency from about ten percent solids to about seventy percent solids;
(c) moving the dewatered web on a transfer surface;
(d) transferring the dewatered web from the transfer surface to a molding roll at a molding nip formed between a backing roll and the molding roll, the dewatered web being transferred to the molding roll as the transfer surface moves through the molding nip, the molding roll including an exterior and a patterned surface on the exterior of the molding roll, the patterned surface having at least one of a plurality of recesses and a plurality of projections;
(e) molding the dewatered web over a molding zone of the molding roll to form a molded paper web, wherein the molding nip is located within the molding zone such that the dewatered web is transferred from the transfer surface to the patterned surface of the molding roll and papermaking fibers of the dewatered web are redistributed on the patterned surface by the least one of the plurality of recesses and the plurality of projections in order to form the molded paper web;
(f) transferring the molded paper web to a drying section; and
(g) drying the molded paper web in the drying section to form a fibrous sheet.

2. The method of claim 1 , wherein the dewatered web has a consistency from about ten percent solids to about thirty-five percent solids.

3. The method of claim 2 , wherein dewatering the nascent web to form dewatered web having the consistency from about ten percent solids to about thirty-five percent solids occurs during the forming of the nascent web.

4. The method of claim 1 , wherein the dewatered web has a consistency from about twenty percent solids to about seventy percent solids.

5. The method of claim 1 , wherein the dewatered web has a consistency from about thirty percent solids to about sixty percent solids.

6. The method of claim 1 , wherein the dewatering step comprises dewatering the nascent web using at least one of a shoe press, a roll press, vacuum dewatering, a displacement press, and thermal drying.

7. The method of claim 1 , wherein the transfer surface is moving at a transfer surface speed and the molding roll is rotating at a molding roll speed, the molding roll speed being less than the transfer surface speed.

8. The method of claim 7 , wherein the creping ratio between the transfer surface and the molding roll is from about five percent to about sixty percent.

9. The method of claim 7 , wherein the papermaking fibers of the dewatered web are pushed into the plurality of recesses.

10. The method of claim 7 , further comprising:
(h) measuring a property of the fibrous sheet to obtain a measured value for the property measured;
(i) determining the measured value is outside a desired range of the property measured; and
(j) adjusting at least one of the transfer surface speed and the molding roll speed such that a measured value of the property, measured during a subsequent measurement, is within the desired range.

11. The method of claim 1 , further comprising using a doctor blade to transfer the dewatered web from the transfer surface to the patterned surface of the molding roll.

12. The method of claim 1 , wherein the drying section comprises a Yankee dryer and the drying step includes drying the molded paper web using the Yankee dryer.

13. The method of claim 1 , wherein the drying section comprises a through-air dryer and the drying step includes drying the molded paper web using the through-air dryer.

14. The method of claim 13 , wherein the drying section further comprises a through-air drying fabric, the molded paper web being transferred to the drying section by transferring the molded paper web to the through-air drying fabric.

15. The method of claim 14 , wherein the molding roll is rotating at a molding roll speed and the through-air drying fabric traveling at a fabric speed, the fabric speed being less than the molding roll speed.

16. The method of claim 15 , further comprising:
(h) measuring a property of the fibrous sheet to obtain a measured value for the property measured;
(i) determining the measured value is outside a desired range of the property measured; and
(j) adjusting at least one of the molding roll speed and the fabric speed such that a measured value of the property, measured during a subsequent measurement, is within the desired range.

17. The method of claim 1 , further comprising applying a load between the backing roll and the molding roll at the molding nip.

18. The method of claim 17 , further comprising:
(h) measuring a property of the fibrous sheet to obtain a measured value for the property measured;
(i) determining the measured value is outside a desired range of the property measured; and
(j) adjusting the load such that a measured value of the property, measured during a subsequent measurement, is within the desired range.

19. The method of claim 1 , further comprising cleaning the patterned surface of the molding roll at a free surface of the molding roll.

20. The method of claim 19 , wherein the cleaning includes directing a cleaning medium toward the patterned surface in a direction that is capable of removing particulate matter from the patterned surface.

21. The method of claim 20 , wherein the cleaning medium is a fluid and the fluid includes at least one of water and a cleaning solution.

22. The method of claim 1 , further comprising applying the dewatered web to a heated surface to heat the dewatered web.

23. The method of claim 22 , wherein the heated surface is the transfer surface and the transfer surface is a surface of the backing roll.

24. The method of claim 1 , wherein the transfer surface is a surface of the backing roll.

25. The method of claim 1 , wherein the transfer surface is a fabric that moves between the backing roll and the molding roll in the molding nip.

26. A method of making a fibrous sheet, the method comprising:
(a) forming a nascent web from an aqueous solution of papermaking fibers;
(b) dewatering the nascent web to form a dewatered web having a consistency from about fifteen percent solids to about seventy percent solids;
(c) moving the dewatered web on a transfer surface;
(d) transferring the dewatered web from the transfer surface to a first molding roll at a first molding nip formed between a backing roll and the first molding roll, the dewatered web being transferred to the first molding roll as the transfer surface moves through the first molding nip, the first molding roll including an exterior and a patterned surface on the exterior of the first molding roll, the patterned surface of the first molding roll having at least one of a plurality of recesses and a plurality of projections;
(e) molding the dewatered web over a first molding zone of the first molding roll to form a paper web having a molded first side, wherein the first molding nip is located within the first molding zone such that the dewatered web is transferred from the transfer surface to the patterned surface of the first molding roll and papermaking fibers on the first side of the dewatered web are redistributed on the patterned surface of the first molding roll by the least one of the plurality of recesses and the pluralit

Assignees

• Gpcp Ip Holdings Llc

Inventors

• Beck David A

Classifications

• D21F11/14

  Making cellulose wadding, filter or blotting paper · CPC title

• D21H27/002

  Tissue paper; Absorbent paper (D21H21/22, D21H27/02, D21H27/20 take precedence; toilet paper A47K10/00; absorbent pads for physiological fluids A61L15/16; making on paper-making machines D21F11/00) · CPC title

• D21F11/06

  of the cylinder type · CPC title

• D21F11/145 Primary

  including a through-drying process · CPC title

• D21F5/18

  Drying webs by hot air · CPC title