Cationic electrodeposition coating material composition

Patent metadata

Field	Value
Publication number	US-11034855-B2
Application number	US-201816495867-A
Country	US
Kind code	B2
Filing date	Mar 22, 2018
Priority date	Mar 23, 2017
Publication date	Jun 15, 2021
Grant date	Jun 15, 2021

Abstract

The present invention relates to a cationic electrodeposition coating composition containing a resin emulsion containing an aminated resin (A) and a blocked isocyanate curing agent (B), characterized in that a deposited electrodeposition coating film of the cationic electrodeposition coating composition has a coating film viscosity in a range of 5,000 to 1,000,000 mPa·s at 110° C., and a portion resulting from removal of a resin component from the deposited electrodeposition coating film of the cationic electrodeposition coating composition has a polarity term in a range of 2 to 30 mN/m.

First claim

The invention claimed is:

1. A cationic electrodeposition coating composition comprising:
a resin emulsion containing an aminated resin (A) and a blocked isocyanate curing agent (B), and
an epoxy viscosity agent (D),
wherein,
a deposited electrodeposition coating film of the cationic electrodeposition coating composition has a coating film viscosity in a range of 5,000 to 1,000,000 mPa·s 110° C.,
a portion resulting from removal of a resin component from the deposited electrodeposition coating film of the cationic electrodeposition coating composition has a polarity term in a range of 2 to 30 mN/m, and
the epoxy viscosity agent (D) has an average particle size of 1 to 200 nm and a number-average molecular weight in a range of 100,000 to 10,000,000, and the epoxy viscosity agent (D) has amino groups, in which 30 to 100% of the amino groups is neutralized with acetic acid.

2. The cationic electrodeposition coating composition according to claim 1 , further comprising at least one metal element compound (C) selected from the group consisting of a Group 3 element compound, a zinc compound, and a bismuth compound,
wherein a content of the metal element compound (C) contained in the cationic electrodeposition coating composition is in a range of 0.02 to 1% by mass in terms of metal element.

3. The cationic electrodeposition coating composition according to claim 2 , wherein an amount of the metal element compound (C) in the portion resulting from the removal of the resin component from the cationic electrodeposition coating composition from the deposited electrodeposition coating film of the cationic electrodeposition coating composition is in a range of 1 to 100 mg/m 2 in terms of metal element.

4. The cationic electrodeposition coating composition according to claim 1 , wherein a hydroxyl value of the aminated resin (A) is 150 to 400 mg KOH/g.

5. The cationic electrodeposition coating composition according to claim 1 ,
wherein an amount of the epoxy viscosity agent (D) contained in the cationic electrodeposition coating composition is 0.1 to 15 parts by mass in terms of resin solid content relative to 100 parts by mass of a total of a resin solid content of the resin emulsion and a resin solid content of the epoxy viscosity agent (D).

6. The cationic electrodeposition coating composition according to claim 1 , further comprising a metal nitrite (E).

7. A method for forming a cured electrodeposition coating film, the method comprising a step of performing electrodeposition coating by immersing an object to be coated in the cationic electrodeposition coating composition according to claim 1 , and then forming a cured electrodeposition coating film on the object to be coated by performing heating and curing.

8. The method according to claim 7 , wherein the object to be coated has an edge part, and in an event that the object to be coated having the cured electrodeposition coating film formed has been subjected to a salt water spray test, a number of rust colonies formed per 1 cm 2 of a coated edge part is less than 3 colonies/cm 2 .

Assignees

• Nippon Paint Automotive Coatings Co Ltd

Inventors

• Ohara Tetsuya
• Miyamae Nobuhiro
• Shimodaira Yosuke
• Inbe Toshio

Classifications

• C08G18/755 Primary

  and at least one isocyanate or isothiocyanate group linked to a secondary carbon atom of the cycloaliphatic ring, e.g. isophorone diisocyanate · CPC title

• C08K2003/0893

  Zinc · CPC title

• C08K2003/0837

  Bismuth · CPC title

• C09D5/4453

  characterised by the nature of the curing agent · CPC title

• C08K5/21

  Urea; Derivatives thereof, e.g. biuret · CPC title