Positive electrode active material for lithium secondary battery, method of preparing the same, and positive electrode for lithium secondary battery and lithium secondary battery which include the positive electrode active material

Patent metadata

Field	Value
Publication number	US-11031595-B2
Application number	US-201816486409-A
Country	US
Kind code	B2
Filing date	Sep 5, 2018
Priority date	Sep 8, 2017
Publication date	Jun 8, 2021
Grant date	Jun 8, 2021

Abstract

In one embodiment, the present disclosure relates to a positive electrode active material in which a lithium cobalt oxide is doped with a doping element including a metallic element and a halide element, wherein the positive electrode active material is represented by Formula 1 and satisfies Equation 1, and a positive electrode for a lithium secondary battery and a lithium secondary battery, either of which include the positive electrode active material:Li(Co1-x-y-zM1xM2yM3z)O2-aHa  [Formula 1](2x+3y+4z−a)/(x+y+z+a)<2.5.  [Equation 1]

First claim

The invention claimed is:

1. A positive electrode active material comprising a lithium cobalt oxide doped with a doping element comprising a metallic element and a halide element,
wherein the positive electrode active material is represented by Formula 1 and satisfies Equation 1:
Li(Co 1-x-y-z M 1 x M 2 y M 3 z )O 2-a H a   [Formula 1]

(2 x+ 3 y+ 4 z−a )/( x+y+z+a )<2.5  [Equation 1]

wherein, in Formula 1,
M 1 comprises at least one metallic element with an oxidation number of 2 selected from the group consisting of magnesium (Mg), calcium (Ca), iron (Fe), nickel (Ni), cobalt (Co), copper (Cu), zirconium (Zr), strontium (Sr), cadmium (Cd), and barium (Ba),
M 2 comprises at least one metallic element with an oxidation number of 3 selected from the group consisting of aluminum (Al), scandium (Sc), yttrium (Y), niobium (Nb), indium (In), antimony (Sb), tantalum (Ta), iridium (Ir), and lanthanum (La),
M 3 comprises at least one metallic element with an oxidation number of 4 selected from the group consisting of manganese (Mn), titanium (Ti), tin (Sn), germanium (Ge), molybdenum (Mo), technetium (Tc), hafnium (Hf), tungsten (W), and lead (Pb),
H comprises at least one halogen element selected from the group consisting of F − , Cl − , Br − , I − , and At − ,
0≤x≤0.1, 0≤y≤0.1, 0≤z≤0.1, 0≤x+y+z≤0.1, and 0<a≤0.3, and
wherein, in Equation 1,
x is an amount of moles of the metallic element with an oxidation number of 2, y is an amount of moles of the metallic element with an oxidation number of 3, z is an amount of moles of the metallic element with an oxidation number of 4, and a is an amount of moles of the halide element,
wherein the positive electrode active material has a particle size distribution whereby (D 95 −D 5 )/D 50 of 1.5 to 2.0.

2. The positive electrode active material of claim 1 , wherein the doping element comprises at least two metallic elements selected from the group consisting of M 1 , M 2 , and M 3 and the halide element.

3. The positive electrode active material of claim 1 , wherein a total amount of the doping element in the positive electrode active material is in a range of 100 ppm to 10,000 ppm.

4. The positive electrode active material of claim 1 , wherein the positive electrode active material has an average particle diameter (D 50 ) of 4 μm to 24 μm.

5. A method of preparing a positive electrode active material, the method comprising preparing a positive electrode active material, which is represented by Formula 1 and satisfies Equation 1, by mixing and sintering a cobalt oxide, a lithium-containing raw material, and a doping raw material to form a particle size distribution whereby (D 95 −D 5 )/D 50 is 1.5 to 2.0:
Li(Co 1-x-y-z M 1 x M 2 y M 3 z )O 2-a H a   [Formula 1]

(2 x+ 3 y+ 4 z−a )/( x+y+z+a )<2.5  [Equation 1]

wherein, in Formula 1,
M 1 comprises at least one metallic element with an oxidation number of 2 selected from the group consisting of magnesium (Mg), calcium (Ca), iron (Fe), nickel (Ni), cobalt (Co), copper (Cu), zirconium (Zr), strontium (Sr), cadmium (Cd), and barium (Ba),
M 2 comprises at least one metallic element with an oxidation number of 3 selected from the group consisting of aluminum (Al), scandium (Sc), yttrium (Y), niobium (Nb), indium (In), antimony (Sb), tantalum (Ta), iridium (Ir), and lanthanum (La),
M 3 comprises at least one metallic element with an oxidation number of 4 selected from the group consisting of manganese (Mn), titanium (Ti), tin (Sn), germanium (Ge), molybdenum (Mo), technetium (Tc), hafnium (Hf), tungsten (W), and lead (Pb),
H comprises at least one halogen element selected from the group consisting of F − , Cl − , Br − , I − , and At − ,
0≤x≤0.1, 0≤y≤0.1, 0≤z≤0.1, 0≤x+y+z≤0.1, and 0<a≤0.3, and
wherein, in Equation 1,
x is an amount of moles of the metallic element with an oxidation number of 2, y is an amount of moles of the metallic element with an oxidation number of 3, z is an amount of moles of the metallic element with an oxidation number of 4, and a is an amount of moles of the halide element.

6. The method of claim 5 , wherein the doping element comprises a metal and a metal halide.

7. The method of claim 6 , wherein the metal halide comprises at least one selected from the group consisting of MgF 2 , CaF 2 , MgCl 2 , CaCl 2 , MgI 2 , and CaI 2 .

8. A positive electrode for a lithium secondary battery, the positive electrode comprising:
a positive electrode collector; and
a positive electrode active material layer formed on the positive electrode collector,
wherein the positive electrode active material layer comprises the positive electrode active material of claim 1 .

9. A lithium secondary battery comprising:
the positive electrode of claim 8 ;
a negative electrode;
a separator disposed between the positive electrode and the negative electrode; and
an electrolyte.

10. The lithium secondary battery of claim 9 , wherein, after the lithium secondary battery is charged and discharged at 0.1 C in a constant current/constant voltage (CC/CV) charge mode with an upper limit voltage of 4.55 V and in a CC discharge mode with a lower limit voltage of 2.5 V, capacity retention after 50 cycles of charge and discharge at 0.5 C/1 C is 90% or more.

11. The method of claim 5 , wherein the doping raw material is mixed such that a total amount of the doping raw material in in a range of 10 ppm to 10,000 ppm.

12. The method of claim 5 , wherein the step of sintering occurs after the step of mixing.

13. The method of claim 12 , wherein the step of sintering includes sintering at a temperature range of 800° C. to 1,200° C. for 10 hours to 20 hours.

Assignees

• Lg Chemical Ltd

Inventors

• Hur Hyuck
• You Min Kyu
• Jo Chi Ho
• Park Sung Bin
• Hwang Jin Tae
• Jung Wang Mo

Classifications

• C01G51/82

  Compounds containing cobalt, with or without oxygen or hydrogen, and containing two or more other elements · CPC title

• H01M4/525 Primary

  of mixed oxides or hydroxides containing iron, cobalt or nickel for inserting or intercalating light metals, e.g. LiNiO2, LiCoO2 or LiCoOxFy · CPC title

• H01M4/131

  Electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title

• C01P2004/61

  Micrometer sized, i.e. from 1-100 micrometer · CPC title

• H01M10/052

  Li-accumulators · CPC title