Grease composition, method for manufacturing grease composition, and method for using grease composition

Patent metadata

Field	Value
Publication number	US-11028335-B2
Application number	US-201816469302-A
Country	US
Kind code	B2
Filing date	Jan 17, 2018
Priority date	Jan 18, 2017
Publication date	Jun 8, 2021
Grant date	Jun 8, 2021

Abstract

Provided is a grease composition which is excellent in fire extinguishing performance without water and can suppress fuming, malodor, and liquefaction on burning and a method for producing the grease composition.A grease composition contains a base oil (A), a thickener (B), and a fire retardant (C), wherein the base oil (A) contains a base oil (A1) having a 40° C. kinematic viscosity of 300 mm2/s or more, a sulfur content of 20 ppm by mass or less, and an initial boiling point of 400° C. or higher, the fire retardant (C) is at least one of aluminum hydroxide (C1) and 1,3,5-triazine-1,3,5 (2H, 4H, 6H)-tris(ethanol) (C2), and a content of the fire retardant (C) is 1.0 to 12.0 mass % based on a total amount of the grease composition.

First claim

The invention claimed is:

1. A grease composition comprising:
a base oil (A),
a thickener (B), and
a fire retardant (C),
wherein
the base oil (A) comprises a base oil (A1) having a 40° C. kinematic viscosity of 300 mm 2 /s or more, a sulfur content of 20 ppm by mass or less, and an initial boiling point of 400° C. or higher,
the fire retardant (C) comprises aluminum hydroxide (C1), 1,3,5-triazine-1,3,5 (2H, 4H, 6H)-tris(ethanol) (C2), or a combination thereof,
a content of the fire retardant (C) is from 1.0 to 12.0 mass % based on a total amount of the grease composition, and
a water content of the grease composition is less than 1.0 mass % based on the total amount of the grease composition.

2. The grease composition according to claim 1 , wherein a content of the base oil (A1) is 80 mass % or more based on a total amount of the base oil (A).

3. The grease composition according to claim 2 , wherein the base oil (A1) has a 40° C. kinematic viscosity of from 300 to 1,000 mm 2 /s.

4. The grease composition according to claim 1 , wherein the base oil (A1) is a bright stock.

5. The grease composition according to claim 1 , wherein the thickener (B) is a soap-based thickener.

6. The grease composition according to claim 1 , wherein the aluminum hydroxide (C1) has an average particle diameter of 5.0 μm or less.

7. The grease composition according to claim 1 , further comprising at least one retardant promotor (D) selected from the group consisting of zinc carbonate (D1), polyhydric alcohol (D2), and sulfurized fats or fatty oils (D3).

8. The grease composition according to claim 1 , wherein the sulfur content of the grease composition is less than 2.0 mass % based on the total amount of the grease composition.

9. A grease composition for steel manufacturing equipment, forging equipment, or a heat treatment apparatus, comprising the grease composition according to claim 1 .

10. A method for producing a grease composition, comprising:
mixing a base oil (A) comprising a base oil (A1) having a 40° C. kinematic viscosity of 300 mm 2 /s or more, a sulfur content of 20 ppm by mass or less, and an initial boiling point of 400° C. or higher, with a thickener (B) to form a grease; and
mixing the grease with aluminum hydroxide (C1), 1,3,5-triazine-1,3,5 (2H, 4H, 6H)-tris(ethanol) (C2), or a combination thereof, as a fire retardant (C), after the mixing the base oil (A) and the thickener (B), to obtain a grease composition in which a content of the fire retardant (C) is from 1.0 to 12.0 mass % based on a total amount of the grease composition,
wherein a water content of the grease composition is less than 1.0 mass % based on the total amount of the grease composition.

11. A process, comprising applying the grease composition of claim 1 as a grease composition in lubricating steel manufacturing equipment, a forging equipment, or a heat treatment apparatus.

12. The grease composition according to claim 1 , wherein the content of the fire retardant (C) is from 1.0 to 10.0 mass % based on a total amount of the grease composition.

Assignees

• Idemitsu Kosan Co

Inventors

• Shishikura Akihiro
• Takada Tomonobu
• Sekiguchi Hiroki
• Koga Asami
• Watanabe Go
• Ikeda Harutomo

Classifications

• C10M141/06

  at least one of them being an organic nitrogen-containing compound · CPC title

• C10M125/10 Primary

  Metal oxides, hydroxides, carbonates or bicarbonates · CPC title

• C10M101/02

  Petroleum fractions · CPC title

• C10M2219/024

  of esters, e.g. fats · CPC title

• C10M135/06

  Esters, e.g. fats · CPC title