White polyester film with properties of lightweight and low-shrinkage

Patent metadata

Field	Value
Publication number	US-11021603-B2
Application number	US-201916238661-A
Country	US
Kind code	B2
Filing date	Jan 3, 2019
Priority date	Jan 3, 2019
Publication date	Jun 1, 2021
Grant date	Jun 1, 2021

Abstract

A white polyester film with a specific weight of 0.6-1.2 has a three-layered structure containing two outer layers (A) having a combined thickness taking up 2% to 30% of an overall thickness of the film and a middle layer (B), and having air-bubble cells in both the outer layers (A) and the middle layer (B). The outer layers (A) are formed from a polyester resin and inorganic particles. The middle layer (B) is formed of a polyester resin, modified polypropylene resin having a heat distortion temperature above 120° C. and a melt flow index (MI) of 0.2-1 g/10 minutes (at 230° C., with a load of 2.16 kg) via crosslinking with 0.1-3 wt % of peroxide with respect to the weight of the polypropylene resin, and inorganic particles.

First claim

The invention claimed is:

1. A white polyester film with lightweight and low-shrinkage, having a specific weight ranging between 0.6 and 1.2, being of three-layered structure containing two outer layers (A) having a combined thickness taking up 2% to 30% of an overall thickness of the polyester film and a middle layer (B), being characterized in a longitudinal thermal shrinkage rate smaller than 1% after baking at 150° C. for 30 minutes, and having air-bubble cells in both the outer layers (A) and the middle layer (B),
each of the outer layers (A) being composed of, with respect to a total composition amount of the layer (A), 65-95 wt % of a polyester resin and 5-35 wt % of inorganic particles, wherein the inorganic particles have an average grain size (D50) of 0.05-5 μm; and
the middle layer (B) being composed of, with respect to a total composition amount of the layer B, 50-90 wt % of a polyester resin, 5-25 wt % of a modified polypropylene resin, and 5-25 wt % of inorganic particles, wherein the inorganic particles have an average grain size (D50) of 0.05-5 μm and the modified polypropylene resin satisfies the following conditions:
(1) being modified using 0.1-3 of wt % a peroxide cross-linking agent with respect to a weight of the underlying polypropylene resin,
(2) having a heat distortion temperature above 120° C., and
(3) having a melt flow index (MI) of 0.2-1 g/10 minutes measured at 230° C. with a load of 2.16 kg.

2. The white polyester film of claim 1 , wherein the inorganic particles in the outer layers (A) and in the middle layer (B) are one or more selected from the group consisting of barium sulfate, calcium carbonate and titanium dioxide.

3. The white polyester film of claim 1 , wherein the polyester resins in the outer layers (A) and in the middle layer (B) are polyethylene terephthalate or polyethylene naphthalate.

4. The white polyester film of claim 1 , wherein the peroxide cross-linking agent is selected from α, α′-bis(t-butylperoxy-m-isopropyl)-benzene or 2,5-dimethyl-2,5-di(tertiary-butylperoxy)-hexyne.

5. The white polyester film of claim 1 , wherein the inorganic particles are pre-added in the polyester resin or the modified polypropylene resin.

6. The white polyester film of claim 1 , wherein the inorganic particle in the outer layers (A) and in the middle layer (B) have and average grain size (D50) of 0.2-1 μm.

7. The white polyester film of claim 1 , wherein the modified polypropylene resin of the middle layer (B) is a propylene homopolymer or a copolymer of propylene and α-olefin.

8. The white polyester film of claim 1 , wherein the modified polypropylene resin of the middle layer (B) is added in an amount equal to 8-15 wt % of the total composition amount of the middle layer (B).

9. The white polyester film of claim 1 , wherein the two outer layers (A) have a combined thickness taking up 5% to 15% of the overall thickness of the polyester film.

Assignees

• Nanya Plastics Corp

Inventors

• Liao Te-Chao
• Yang Wen-Cheng
• Tsao Chun-Che
• HSIAO Chia-Yen
• Wang Chih-Feng

Classifications

• B32B27/16 Primary

  specially treated, e.g. irradiated · CPC title

• B32B2367/00

  Polyesters, e.g. PET, i.e. polyethylene terephthalate · CPC title

• B32B2519/00

  Labels, badges · CPC title

• C08L2203/16

  used for films · CPC title

• Y10T428/258

  Alkali metal or alkaline earth metal or compound thereof · CPC title