Production equipment line for hot-rolled steel strip and production method for hot-rolled steel strip

Patent metadata

Field	Value
Publication number	US-11020780-B2
Application number	US-201716072968-A
Country	US
Kind code	B2
Filing date	Jan 16, 2017
Priority date	Jan 27, 2016
Publication date	Jun 1, 2021
Grant date	Jun 1, 2021

Abstract

A production equipment line for a hot-rolled steel strip comprises a rough rolling mill comprising rough rolling mills for hot rolling a material, which is heated to a predetermined temperature to a finish rolling start sheet thickness and a finish rolling mill comprising finish rolling mills for controlled-rolling the material to a final sheet thickness. At least one of the rough rolling mills is a reversible rolling mill. The production equipment line is provided on an upstream side of the reversible rolling mill with one of a slow cooling apparatus for slowly cooling at a water volume density of less than 1000 L/min·m2 and a rapid cooling apparatus for rapidly cooling after the slow-cooling at a water volume density of not less than 1000 L/min·m2 and the other of the slow cooling apparatus and rapid cooling apparatus on a downstream side of the reversible rolling mill.

First claim

The invention claimed is:

1. A production equipment line for a hot-rolled steel strip comprising a rough rolling mill group comprised of plural rough rolling mills for hot rolling a material to be rolled which is heated up to a predetermined temperature to a finish rolling start sheet thickness and a finish rolling mill group comprised of plural finish rolling mills for controlled-rolling the material to be rolled to a final sheet thickness,
characterized in that at least one of the plural rough rolling mills is a reversible rolling mill,
and one of a slow cooling apparatus for slowly cooling the material to be rolled at a water volume density of less than 1000 L/min·m 2 or a rapid cooling apparatus for rapidly cooling the material to be rolled after the slow cooling at a water volume density of not less than 1000 L/min·m 2 is arranged on an upstream side of the reversible rolling mill and the other of the slow cooling apparatus or the rapid cooling apparatus is arranged on a downstream side of the reversible rolling mill, such that at least one of the slow cooling apparatus and the rapid cooling apparatus is arranged between the reversible rolling mill and another one of the plural rough rolling mills.

2. The production equipment line for a hot-rolled steel strip according to claim 1 , wherein at least a rough rolling mill arranged on a most downstream side among the plural rough rolling mills is a reversible rolling mill.

3. The production equipment line for a hot-rolled steel strip according to claim 1 , wherein the slow cooling apparatus is arranged on the upstream side of the reversible rolling mill and the rapid cooling apparatus is arranged on the downstream side thereof.

4. The production equipment line for a hot-rolled steel strip according to claim 2 , wherein the slow cooling apparatus is arranged on the upstream side of the reversible rolling mill and the rapid cooling apparatus is arranged on the downstream side thereof.

5. The production equipment line for a hot-rolled steel strip according to claim 1 , wherein the slow cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and the rapid cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

6. The production equipment line for a hot-rolled steel strip according to claim 2 , wherein the slow cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and the rapid cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

7. The production equipment line for a hot-rolled steel strip according to claim 3 , wherein the slow cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and the rapid cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

8. The production equipment line for a hot-rolled steel strip according to claim 4 , wherein the slow cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and the rapid cooling apparatus is positioned relative to the plural rough rolling mills such that the material to be rolled is rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

9. The production equipment line for a hot-rolled steel strip according to claim 1 , wherein each cooling time in the slow cooling apparatus and the rapid cooling apparatus is set so as to render a surface temperature of the material to be rolled during the cooling into not lower than 600° C.

10. The production equipment line for a hot-rolled steel strip according to claim 1 , wherein a sheet thickness at an exit side of a final-stage finish rolling mill among the plural finish rolling mills is not less than 12 mm.

11. A method for producing a hot-rolled steel strip by hot rolling a material to be rolled which is heated to a predetermined temperature by a plurality of rough rolling mills to provide a finish rolling start sheet thickness and controlled-rolling the material to be rolled to a finish sheet thickness by a plurality of finish rolling mills,
characterized in that at least one of the plural rough rolling mills is a reversible rolling mill,
and one of a slow cooling apparatus for slowly cooling the material to be rolled at a water volume density of less than 1000 L/min·m 2 or a rapid cooling apparatus for rapidly cooling the material to be rolled at a water volume density of not less than 1000 L/min·m 2 is arranged on an upstream side of the reversible rolling mill and the other of the slow cooling apparatus or the rapid cooling apparatus is arranged on a downstream side of the reversible rolling mill, such that at least one of the slow cooling apparatus and the rapid cooling apparatus is arranged between the reversible rolling mill and another one of the plural rough rolling mills,
and the material to be rolled is slowly cooled by the slow cooling apparatus at a water volume density of less than 1000 L/min·m 2 and thereafter the material to be rolled is rapidly cooled by the rapid cooling apparatus at a water volume density of not less than 1000 L/min·m 2 .

12. The production method for a hot-rolled steel strip according to claim 11 , wherein at least a rough rolling mill arranged on a most downstream side among the plural rough rolling mills is a reversible rolling mill.

13. The production method for a hot-rolled steel strip according to the claim 11 , wherein the slow cooling apparatus is arranged on the upstream side of the reversible rolling mill and the rapid cooling apparatus is arranged on the downstream side thereof.

14. The production method for a hot-rolled steel strip according to the claim 12 , wherein the slow cooling apparatus is arranged on the upstream side of the reversible rolling mill and the rapid cooling apparatus is arranged on the downstream side thereof.

15. The production method for a hot-rolled steel strip according to claim 11 , wherein the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

16. The production method for a hot-rolled steel strip according to claim 12 , wherein the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

17. The production method for a hot-rolled steel strip according to claim 13 , wherein the material to be rolled is slowly cooled by the slow cooling apparatus when the sheet thickness is not less than 80 mm and rapidly cooled by the rapid cooling apparatus when the sheet thickness is less than 80 mm.

Assignees

• Jfe Steel Corp

Inventors

• Ueoka Satoshi
• Tamura Yuta
• Shirasaki Sonomi
• Katayama Yukako
• Matsumoto Takashi

Classifications

• B21B45/0218

  for strips, sheets, or plates (B21B45/023, B21B45/0233 take precedence) · CPC title

• B21B1/34

  by hot-rolling · CPC title

• B21B45/02

  for lubricating, cooling, or cleaning {(in particular in combination with forging or pressing devices B21B15/005, control of flatness or profile using lubricating or cooling B21B37/44)} · CPC title

• B21B1/26 Primary

  by hot-rolling {, e.g. Steckel hot mill} · CPC title

• B21B1/18

  in a continuous process · CPC title