Method for preparing titanium dioxide-based synthetic paper

Patent metadata

Field	Value
Publication number	US-11015294-B2
Application number	US-201816009176-A
Country	US
Kind code	B2
Filing date	Jun 14, 2018
Priority date	Oct 31, 2016
Publication date	May 25, 2021
Grant date	May 25, 2021

Abstract

A method for preparing titanium dioxide-based synthetic paper capable of degrading organic pollutants, including: adding thermoplastic polyurethane particles and N,N-dimethylformamide or N,N-dimethylacetamide in a reactor, heating, and stirring to fully dissolve the thermoplastic polyurethane particles in a solvent to obtain a polyurethane solution; adding titanium dioxide powder having photocatalytic degradation property in the polyurethane solution, stirring uniformly to obtain a solid-liquid mixture, and standing for defoaming; uniformly coating the solid-liquid mixture onto a piece of release paper, soaking the release paper coated with the solid-liquid mixture into an aqueous solution of sliver nitrate having photocatalytic degradation property, completely curing the solid-liquid mixture to form a film, and soaking the release paper and the film into an aqueous solution of sodium chloride; drying, cooling, removing the release paper, and cutting the film to a proper size to obtain the titanium dioxide-based synthetic paper.

First claim

What is claimed is:

1. A method for preparing titanium dioxide-based synthetic paper capable of degrading organic pollutants, comprising the following steps:
(1) adding thermoplastic polyurethane particles and N,N-dimethylformamide or N,N-dimethylacetamide in a reactor at a mass ratio of 22-30:110, heating to 50° C. to 80° C., and stirring to fully dissolve the thermoplastic polyurethane particles in a solvent to obtain a polyurethane solution;
(2) adding titanium dioxide powder in the polyurethane solution obtained in the step (1) at a mass ratio of the polyurethane solution to the titanium dioxide powder of 132-140:25-50, stirring uniformly to obtain a solid-liquid mixture, and standing for 5 h to 8 h for defoaming;
(3) uniformly coating the solid-liquid mixture obtained in the step (2) onto a piece of release paper, soaking the release paper coated with the solid-liquid mixture into an aqueous solution of silver nitrate for 30 min to 60 min, completely curing the solid-liquid mixture to form a film, and soaking the release paper and the film into an aqueous solution of sodium chloride for 30 min to 60 min;
(4) drying the release paper and the film obtained in the step (3) in an oven for 1 h to 2 h at 50° C. to 60° C., cooling the release paper and the film, removing the release paper, and cutting the film to a proper size according to practical application requirements to obtain the titanium dioxide-based synthetic paper.

2. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein the titanium dioxide-based synthetic paper obtained in the step (4) is white, the thickness of the titanium dioxide-based synthetic paper is controlled between 0.10 mm to 0.25 mm by adjusting the thickness of the solid-liquid mixture coated onto the release paper in the step (3), and the mass of the titanium dioxide-based synthetic paper as a piece of A4 paper is 5.10 g to 7.14 g.

3. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein the titanium dioxide is titanium dioxide powder having a particle size of 325 to 2500 meshes.

4. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein the thermoplastic polyurethane material is one or two of polyether-based TPU and polyester-based TPU, in form of particles having a Shore hardness of 85 A to 95 A.

5. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein the solvent in the step (1) is one of N,N-dimethylformamide and N,N-dimethylacetamide.

6. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein, in the solid-liquid mixture obtained in the step (2), the mass percentage of the polyurethane is 12.1% to 16.2%, the mass percentage of the solvent is 59.5% to 68.8%, and the mass percentage of the titanium dioxide is 15.6% to 27.5%.

7. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein, in the step (3), the mass percentage of the aqueous solution of silver nitrate is 3% to 6%, and the temperature is 20° C. to 35° C.

8. The method for preparing titanium dioxide-based synthetic paper according to claim 1 , wherein, in the step (3), the mass percentage of the aqueous solution of sodium chloride is 3% to 6%, and the temperature is 20° C. to 35° C.

Assignees

• Univ Hunan Science & Technology

Inventors

• Zhou Hu
• Wang Dongdong
• Qi Zhiling
• Liu Xuan
• Zhou Zhihua
• Liu Qingquan
• Li Xiaofang

Classifications

• D21H13/20

  from macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• D21H27/00

  Special paper not otherwise provided for, e.g. made by multi-step processes · CPC title

• C09D175/08

  from polyethers · CPC title

• C08K2201/005

  Additives being defined by their particle size in general · CPC title

• C08L2205/02

  containing two or more polymers of the same C08L -group · CPC title