Multilayer hard film-coated cutting tool

Patent metadata

Field	Value
Publication number	US-11014167-B2
Application number	US-201716322258-A
Country	US
Kind code	B2
Filing date	Jul 28, 2017
Priority date	Aug 1, 2016
Publication date	May 25, 2021
Grant date	May 25, 2021

Abstract

A multilayer hard film-coated cutting tool including a cutting tool body and a multilayer hard film formed on a surface of the cutting tool body, wherein the multilayer hard film comprises at least an upper layer and a lower layer; the upper layer is made of a Ti and Si compound layer; the lower layer is made of a multi-layered film of an A-layer and a B-layer, a layer thickness of the B-layer is equal to or thicker than a layer thickness of the A-layer, a ratio of the layer thicknesses of the A-layer and the B-layer being A-layer:B-layer=1:1 to 1:2, the multilayer hard films having 2 to 8 pairs of the A-layer and the B-layer in a case where a single pair is defined by a combination of a single A-layer and a single B-layer.

First claim

The invention claimed is:

1. A multilayer hard film-coated cutting tool comprising:
a cutting tool body; and
a multilayer hard film formed on a surface of the cutting tool body, wherein
(a) the multilayer hard film comprises at least an upper layer provided as an outermost layer, and a lower layer provided between the upper layer and the cutting tool body;
(b) the upper layer is made of a Ti and Si compound layer, which includes X, and has a layer thickness of 0.075 μm to 1.5 μm, 0.7≤z≤0.99 (z in atomic ratio) being satisfied in a case where the chemical composition of the Ti and Si compound layer is expressed by a composition formula of (Ti z Si 1-z )X and X being any one of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO;
(c) the lower layer is made of a multi-layered film formed of pairs of layers, each pair comprising a single A-layer and a single B-layer, wherein the layer thickness of the B-layer is equal to or thicker than the layer thickness of the A-layer, a ratio of the layer thicknesses of the A-layer and the B-layer being A-layer:B-layer=1:1 to 1:2, the multilayered-film having 2 to 8 pairs of the A-layer and the B-layer;
(d) the A-layer is a layer made of a compound including at least Al and Cr, 0.2≤y≤0.7 (y in atomic ratio) being satisfied in a case where the compound including at least Al and Cr is expressed by a composition formula of (Al y Cr 1-y )X and X being any one of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO; and
(e) the B-layer is a mixed layer of (Ti z Si 1-z )X and (Al y Cr 1-y )X, X being any one of N, C, B, CN, BN, CBN, NO, CO, BO, CNO, BNO, and CBNO.

2. The multilayer hard film-coated cutting tool according to claim 1 , wherein the mixed layer is formed of (Ti z Si 1-z )X layers and (Al y Cr 1-y )X layers, and each individual (Ti z Si 1-z )X layer and each individual (Al y Cr 1-y )X layer is deposited alternate one on each other, and each individual (Ti z Si 1-z )X layer and each individual (Al y Cr 1-y )X layer comprised in the mixed layer has preferably an individual layer thickness not thicker than 100 nm.

3. The multilayer hard film-coated cutting tool according to claim 1 , wherein the upper layer has a layer thickness of 0.2 μm to 1.5 μm.

4. The multilayer hard film-coated cutting tool according to claim 1 , wherein the upper layer has a layer thickness of 0.6 μm to 1.5 μm.

5. The multilayer hard film-coated cutting tool according to claim 1 , wherein the A-layer has a layer thickness of 0.25 μm to 1.5 μm.

6. The multilayer hard film-coated cutting tool according to claim 1 , wherein the B-layer has a layer thickness of 0.25 μm to 2.5 μm.

7. The multilayer hard film-coated cutting tool according to claim 1 , wherein at least one layer of the A-layers and at least one layer of the B-layers comprised in the multi-layered film further include at least any one of components elements selected from W, V, Mo, Nb, Ta, Hf, and Zr; or Si.

8. The multilayer hard film-coated cutting tool according to claim 1 , wherein
a width of a periodical composition fluctuation of the B-layer is 20 nm to 200 nm, the width of the periodical composition fluctuation (nm) being obtained as a thickness between a location having a local maximum content of a Ti component and an adjacent location having a local maximum content of the Ti component obtained by measurement of TEM-EDS; and
a composition variation rate of the periodical composition fluctuation is 5% to 95%, the composition variation rate being obtained as a ratio (%) in which a difference of the local maximum content and a local minimum content is divided by the local maximum content between the location having the local maximum content of the Ti component and the adjacent location having the local maximum content of the Ti component obtained by measurement of TEM-EDS.

9. The multilayer hard film-coated cutting tool according to claim 1 , wherein
a bottom layer is formed between the cutting tool body and the lower layer; and
the bottom layer is made of the A-layer having a layer thickness of 0.05 μm to 1.5 μm and the B-layer having a layer thickness of 0.05 μm to 2.5 μm.

Assignees

• Mitsubishi Materials Corp
• Oerlikon Surface Solutions Ag Pfaffikon

Inventors

• Takahashi Masakuni
• Kurapov Denis
• Derflinger Volker
• Kalss Wolfgang

Classifications

• C23C14/0641 Primary

  Nitrides (C23C14/0617 takes precedence) · CPC title

• B23B2228/10

  Coatings · CPC title

• C23C14/505

  for rotation of the substrates · CPC title

• C23C28/42

  characterized by the composition of the alternating layers · CPC title

• B23B51/00

  Tools for drilling machines · CPC title