Production method of mold, manufacturing method of pattern sheet, production method of electroform, and production method of mold using electroform

Patent metadata

Field	Value
Publication number	US-11007678-B2
Application number	US-201815933573-A
Country	US
Kind code	B2
Filing date	Mar 23, 2018
Priority date	Sep 30, 2015
Publication date	May 18, 2021
Grant date	May 18, 2021

Abstract

A production method of a mold includes: preparing a plate precursor having a protruding pattern formed of protrusions in a pattern presence region on a base, and a thermoplastic resin sheet; determining a position at which the plate precursor is to be pressed against the thermoplastic resin sheet by moving the plate precursor and the thermoplastic resin sheet relative to each other; and forming a recessed pattern on the thermoplastic resin sheet by pressing the protrusions of the plate precursor which is heated against the thermoplastic resin sheet at a position where a part of the pattern presence region of the plate precursor excluding the protrusions is separated from a surface of the thermoplastic resin sheet, cooling the plate precursor in a state in where the pressed protrusions and the thermoplastic resin sheet are in contact with each other, and separating the plate precursor from the thermoplastic resin sheet.

First claim

What is claimed is:

1. A production method of a mold comprising:
a preparation process of preparing a plate precursor having a protruding pattern formed of a plurality of protrusions in a pattern presence region on a base, and a thermoplastic resin sheet;
an alignment process of determining a position at which the plate precursor is to be pressed against the thermoplastic resin sheet by moving the plate precursor and the thermoplastic resin sheet relative to each other; and
a forming process of forming a recessed pattern having an inverted shape of the protruding pattern on the thermoplastic resin sheet by pressing the protrusions of the plate precursor which is heated against the thermoplastic resin sheet at a position where a part of the pattern presence region of the plate precursor excluding the protrusions is separated from a surface of the thermoplastic resin sheet, cooling the plate precursor in a state in which the pressed protrusions and the thermoplastic resin sheet are in contact with each other, and separating the plate precursor from the thermoplastic resin sheet,
wherein a depression is formed in advance in a pressing surface in the surface of the thermoplastic resin sheet, against which the protrusions forming the protruding pattern of the plate precursor are pressed.

2. The production method of a mold according to claim 1 ,
wherein a thickness of the thermoplastic resin sheet is equal to or greater than a height of the protrusions of the plate precursor.

3. The production method of a mold according to claim 1 ,
wherein, in the forming process, in a case where a heating temperature of the plate precursor is equal to or lower than a melting point of the thermoplastic resin sheet, a vertical sectional shape of the depression is an arcuate shape.

4. The production method of a mold according to claim 1 ,
wherein, in the forming process, in a case where a heating temperature of the plate precursor is equal to or higher than a melting point of the thermoplastic resin sheet, a vertical sectional shape of the depression is a rectangular shape.

5. The production method of a mold according to claim 1 ,
wherein a pressing surface in the surface of the thermoplastic resin sheet, against which the protrusions forming the protruding pattern of the plate precursor are pressed, is flat, and
in the forming process, the part of the pattern presence region of the plate precursor excluding the protrusions is stopped before reaching the flat pressing surface.

6. The production method of a mold according to claim 1 ,
wherein, in a case where the plate precursor is pressed against the thermoplastic resin sheet, a position of the surface of the thermoplastic resin sheet is detected, and the plate precursor is pushed from the position of the surface of the thermoplastic resin sheet by a certain amount.

7. The production method of a mold according to claim 1 ,
wherein, in a case where the plate precursor is pressed against the thermoplastic resin sheet, a pressure applied to the plate precursor is measured and is compared to a certain pressure value which is set, and the amount of the plate precursor being pushed is determined.

8. The production method of a mold according to claim 1 ,
wherein the protrusion has a frustum portion and a needle portion which is tapered, in a direction away from the base of the plate precursor, and in the forming process, in a case where the plate precursor is pressed against the thermoplastic resin sheet, the frustum portion is brought into contact with the surface of the thermoplastic resin sheet.

9. A manufacturing method of a pattern sheet having a protruding pattern, comprising:
a process of producing a mold using the production method according to claim 1 ;
a supplying process of supplying a polymer solution to a recessed pattern of the mold;
a drying process of drying the polymer solution to form a polymer sheet; and
a polymer sheet peeling process of peeling the polymer sheet from the mold.

10. A production method of an electroform having a protruding pattern, comprising:
a process of producing a mold using the production method according to claim 1 ;
an electroforming process of forming a metal body on a recessed pattern of the mold using an electroforming method; and
a peeling process of peeling the metal body from the mold.

11. A production method of a mold using an electroform, comprising:
a process of producing an electroform using the production method according to claim 10 ; and
a process of, by using the electroform having a protruding pattern, producing a mold which has a recessed pattern which is an inverted shape of the protruding pattern of the electroform and is made of a resin.

12. A manufacturing method of a pattern sheet having a protruding pattern, comprising:
a process of producing a mold, which is made of a resin, using the production method according to claim 11 ;
a supplying process of supplying a polymer solution to a recessed pattern of the mold;
a drying process of drying the polymer solution to form a polymer sheet; and
a peeling process of peeling the polymer sheet from the mold made of a resin.

Assignees

• Fujifilm Corp

Inventors

• Ogawa Shotaro
• Chai Satoshi
• Ichikawa Kenji
• Komatsu Kazunori
• Ikeda Kozue
• Hibino Ryo

Classifications

• B81C99/00

  Subject matter not provided for in other groups of this subclass · CPC title

• B29C43/52

  Heating or cooling · CPC title

• A61M37/0015 Primary

  by using microneedles · CPC title

• A61M37/00

  Other apparatus for introducing media into the body (for reproduction or fertilisation A61B17/425; apparatus for iontophoresis or cataphoresis A61N1/30); Percutany, i.e. introducing medicines into the body by diffusion through the skin (salt baths A61H33/04) · CPC title

• B29C33/3857 Primary

  by making impressions of one or more parts of models, e.g. shaped articles and including possible subsequent assembly of the parts · CPC title