Methods for making high sound transmission class gypsum boards and gypsum boards made by the method

Patent metadata

Field	Value
Publication number	US-11002010-B2
Application number	US-201916356303-A
Country	US
Kind code	B2
Filing date	Mar 18, 2019
Priority date	May 1, 2018
Publication date	May 11, 2021
Grant date	May 11, 2021

Abstract

A layered gypsum wallboard can include: a gypsum board having opposing front and back faces, wherein the gypsum board comprises a first cover sheet material at the front face, a second cover sheet material at the back face, and a gypsum core layer comprising gypsum; an adhesive layer on the second cover sheet material of the gypsum board, the adhesive including a polymer having a glass transition temperature (Tg) of −10° C. to 30° C.; an intermediate gypsum layer including gypsum on the adhesive layer such that the adhesive layer is between the second cover sheet material and the intermediate gypsum layer, wherein the adhesive layer and the intermediate gypsum layer have a combined thickness of 0.09 inches to 0.25 inches; and a third cover sheet material, wherein the intermediate gypsum layer is between and in contact with the adhesive layer and the third cover sheet material.

First claim

What is claimed is:

1. A layered wallboard comprising:
a gypsum board having opposing front and back faces, wherein the gypsum board comprises a first cover sheet material at the front face, a second cover sheet material at the back face, and a gypsum core layer comprising gypsum, wherein the gypsum board has a thickness of 0.25 inches to 1.5 inches, the first cover sheet and the second cover sheet adhering to the gypsum core layer;
an adhesive layer directly on and adhering to the second cover sheet material of the gypsum board, said adhesive comprising a polymer having a glass transition temperature (T g ) of −10° C. to 30° C.;
an intermediate gypsum layer comprising gypsum directly on and adhering to the adhesive layer such that the adhesive layer is between the second cover sheet material and the intermediate gypsum layer, wherein the adhesive layer and the intermediate gypsum layer have a combined thickness of 0.09 inches to 0.25 inches; and
a third cover sheet material, wherein the intermediate gypsum layer is between and in contact with the adhesive layer and the third cover sheet material,
wherein the first cover sheet material is paper for cover sheet or fiberglass for cover sheet,
the second cover sheet material is paper for cover sheet or fiberglass for cover sheet and
the third cover sheet material is paper for cover sheet or fiberglass for cover sheet, and
wherein the first cover sheet material, the second cover sheet material and the third cover sheet material are the only layers of cover sheet of the layered wallboard.

2. The layered wallboard of claim 1 , wherein the polymer of the adhesive layer comprises a latex polymer selected from the group consisting of acrylics, styrene acrylics, acrylic esters, vinyl acrylics, vinyl chloride acrylic, styrene acetate acrylics, butyl acrylics, ethyl acrylics, ethylene polyvinyl acetate, polyvinyl acetate, styrene butadiene, and combinations thereof.

3. The layered wallboard of any of claim 1 , wherein the adhesive layer further comprises alkyl abietate and a plant resin and polyvinyl alcohol.

4. The layered wallboard of claim 1 , wherein the adhesive layer has a thickness of about 0.02 inches to about 0.06 inches.

5. The layered wallboard of claim 1 , wherein the intermediate gypsum layer is a foamed intermediate gypsum layer and has a total void volume of 30 to 90 volume percent.

6. The layered wallboard of claim 1 , wherein the intermediate gypsum layer has a total void volume of less than 30 volume percent.

7. The layered wallboard claim 1 , wherein the adhesive layer has an absence of gypsum, wherein the adhesive layer has an absence of calcium carbonate, wherein the adhesive layer has an absence of magnesium carbonate, wherein the adhesive layer has an absence of pigment, wherein the adhesive layer has an absence of polyurea, wherein the adhesive layer has an absence of organic particles, and wherein the adhesive layer has an absence of inorganic particles.

8. The layered wallboard of claim 1 , wherein an outer surface of the third cover sheet material is in contact with no additional layers.

9. The layered wallboard of claim 1 , wherein the gypsum core layer and the intermediate gypsum layer comprise about 70 wt % to about 98 wt % calcium sulfate dihydrate, about 0.1 wt % to about 28 wt % additives, and about 0.01 wt % to about 2 wt % dispersant.

10. The layered wallboard of claim 1 , wherein the entire back face of the gypsum board is coated with the adhesive layer.

11. The layered wallboard of claim 1 , wherein an entire surface of the intermediate gypsum layer is in contact with the adhesive layer, and an entire opposing surface of the intermediate gypsum layer is in contact with the third cover sheet material.

12. The layered wallboard of claim 1 , wherein the polymer having the glass transition temperature (T g ) of −10° C. to 30° C. is acrylic polymer, wherein the adhesive layer consists of acrylic polymer, alkyl abietate and a plant resin and polyvinyl alcohol.

13. The layered wallboard of claim 1 , wherein the adhesive layer comprises about 60 wt. % acrylic-vinyl chloride polymer, about 10 wt. % natural resin, about 10 wt. % polyvinyl alcohol, and about 20 wt. % methyl abietate.

14. The layered wallboard of claim 1 , wherein each of the first, second and third cover sheets are paper cover sheet.

15. A method of making the layered wallboard of claim 1 , wherein the method comprises:
applying an adhesive coating having a thickness of 0.02 inches to 0.06 inches on a back face of a gypsum board having opposing front and back faces, said adhesive comprising a polymer having a glass transition temperature (Tg) of −10° C. to about 30° C., wherein the gypsum board comprises a first cover sheet material at the front face, a second cover sheet material at the back face, and a gypsum core layer comprising gypsum, wherein the gypsum board has a thickness of 0.25 inches to 1.5 inches,
applying an intermediate gypsum slurry comprising calcium sulfate hemihydrate on the adhesive coating to form an intermediate gypsum layer, wherein the adhesive coating and the gypsum slurry have a combined thickness of 0.09 inches to 0.25 inches; and
applying a third cover sheet material on the intermediate gypsum slurry,
wherein the first cover sheet material is paper for cover sheet or fiberglass for cover sheet,
the second cover sheet material is paper for cover sheet or fiberglass for cover sheet, and
the third cover sheet material is paper for cover sheet or fiberglass for cover sheet, and
wherein the first cover sheet material, the second cover sheet material and the third cover sheet material are the only layers of cover sheet of the layered wallboard; and allowing the calcium sulfate hemihydrate of the gypsum slurry to set to form a layered wallboard.

16. The method of claim 15 , wherein the polymer of the adhesive comprises a latex polymer selected from the group consisting of acrylics, styrene acrylics, acrylic esters, vinyl acrylics, vinyl chloride acrylic, styrene acetate acrylics, butyl acrylics, ethyl acrylics, ethylene polyvinyl acetate, polyvinyl acetate, styrene butadiene, and combinations thereof.

17. The method of claim 15 , wherein the intermediate gypsum slurry is foamed and sets to form an intermediate gypsum layer having a total void volume of 30 to 90 volume percent.

18. A method of making the layered wallboard of claim 1 , wherein the method comprises:
optionally applying a skim layer slurry to a first cover sheet material, the skim layer slurry comprising water and calcium sulfate hemihydrate;
applying a gypsum core slurry to either the first cover sheet material when the skim layer slurry is not present or the skim layer slurry when present, the gypsum core slurry comprising water and calcium sulfate hemihydrate;
applying a second cover sheet material to the gypsum core slurry, wherein a first side of the second cover sheet material faces toward the gypsum core slurry;
applying a polymer adhesive coating on a second side of the second cover sheet material opposed to the first side of the second cover sheet material, wherein the polymer adhesive comprises a polymer has a glass transition temperature (T g ) of −10° C. to about 30° C.;
applying an intermediate gypsum slurry onto the polymer adhesive coating, the intermediate gypsum slurry comprising water and calcium sulfate hemihydrate,
wherein the polymer adhesive coating and the second gypsum slurry have a combined thickness of 0.09 inches to 0.25 inches; and
applying a third cover sheet material on the intermediate gypsum slu

Assignees

• United States Gypsum Co

Inventors

• Ray Suman Sinha
• Antosh Mark
• Hemphill Mark
• Sang Yijun

Classifications

• B32B2262/101

  Glass fibres · CPC title

• B32B2307/718

  Weight, e.g. weight per square meter · CPC title

• B32B7/12 Primary

  using interposed adhesives or interposed materials with bonding properties · CPC title

• B32B5/32

  at least two} layers being foamed {and next to each other · CPC title

• E04B2/723

  constituted of gypsum elements · CPC title