Silicone adhesive composition, adhesive tape, and method for producing adhesive tape

Patent metadata

Field	Value
Publication number	US-10995248-B2
Application number	US-201816212217-A
Country	US
Kind code	B2
Filing date	Dec 6, 2018
Priority date	Feb 13, 2014
Publication date	May 4, 2021
Grant date	May 4, 2021

Abstract

A silicone adhesive composition includes 100 parts by weight of a peroxide-curable silicone, 1.2 to 3.2 parts by weight of an organic peroxide curing agent, and 2 to 9 parts by weight of an addition reaction-curable silicone rubber. An adhesive tape includes a base and an adhesive layer placed on the base, the adhesive layer being formed from the above silicone adhesive composition. The adhesive composition exhibits high load bearing capacity even in higher-temperature environments than ever before. The adhesive tape exhibits high load bearing capacity and good shelf life even in such high-temperature environments.

First claim

The invention claimed is:

1. An adhesive tape comprising:
a base; and
an adhesive layer placed on the base, the adhesive layer being formed from a silicone adhesive composition comprising:
100 parts by weight of a peroxide-curable silicone;
1.2 to 3.2 parts by weight of an organic peroxide curing agent; and
2 to 9 parts by weight of an addition reaction-curable silicone rubber, wherein
the peroxide-curable silicone includes (1) at least one selected from the group consisting of a dimethylpolysiloxane, which may optionally have a hydroxy group, and a partial condensate thereof and (2) at least one selected from the group consisting of an MQ resin, which comprises a M unit and a Q unit, and a partial condensate thereof,
the addition reaction-curable silicone rubber contains an addition-polymerizable group, and
the adhesive tape satisfies at least one of the following conditions: (a) a gel fraction of a cured product of the silicone adhesive composition is 40 to 60%; or (b) in the adhesive tape, an amount of peel in 90° direction is 0 (mm),
wherein the amount of peel in 90° direction is determined by:
(i) cutting the adhesive tape to obtain a 10-mm-wide test specimen;
(ii) attaching the test specimen to a stainless steel plate so that an adhesive area is 10 mm×20 mm and one edge of the test specimen is not in contact with the stainless steel plate;
(iii) applying a load of 20 g, acting in a direction perpendicular to the surface of the stainless steel plate, to the one edge of the test specimen;
(iv) quickly heating the test specimen and the stainless steel plate to 250° C. and holding at 250° C. for 1 hour; and
(v) evaluating an amount of peel of the test specimen.

2. The adhesive tape according to claim 1 , wherein the base is a glass cloth base impregnated with polytetrafluoroethylene (PTFE).

3. The adhesive tape according to claim 1 , wherein a molar ratio of the M unit and the Q unit in the MQ resin is from 0.3:1 to 1.5:1.

4. A method for producing an adhesive tape according to claim 1 , the method comprising:
heating an original tape including the base and the silicone adhesive composition placed on the base and thereby forming the composition into an adhesive layer, so as to obtain the adhesive tape including the base and the adhesive layer placed on the base.

5. The method for producing the adhesive tape according to claim 4 , wherein the base is a glass cloth base impregnated with polytetrafluoroethylene (PTFE).

6. A method for producing an adhesive tape according to claim 1 , the method comprising:
heating a transfer base on which the silicone adhesive composition is placed and thereby forming the silicone adhesive composition into the adhesive layer; and
transferring the adhesive layer from the transfer base to the base so as to obtain the adhesive tape including the base and the adhesive layer placed on the base.

7. The method for producing the adhesive tape according to claim 6 , wherein the base is a glass cloth base impregnated with polytetrafluoroethylene (PTFE).

Assignees

• Nitto Denko Corp

Inventors

• Kigami Hiroki
• Watanabe Yoshinori

Classifications

• C08K5/14

  Peroxides · CPC title

• C09J7/38

  Pressure-sensitive adhesives [PSA] · CPC title

• C09J2483/00

  Presence of polysiloxane · CPC title

• C09J7/21

  Paper; Textile fabrics · CPC title

• C08K5/56

  Organo-metallic compounds, i.e. organic compounds containing a metal-to-carbon bond · CPC title