Abstract

The present invention relates to a superabsorbent polymer having an improved adsorption rate and a high bulk density, and a preparation method thereof.

First claim

The invention claimed is:

1. A superabsorbent polymer comprising
a base polymer powder containing a crosslinked polymer of a water-soluble ethylenically unsaturated monomer having an acidic group in which at least a part thereof is neutralized,
wherein a plurality of pores having a diameter of 1 μm or greater are formed in the base polymer powder,
wherein the crosslinked polymer has a crosslinked structure and comprises a layered silicate-based particle dispersed in the crosslinked structure, and
wherein the superabsorbent polymer has an bulk density of 0.55 g/ml or greater, and wherein the layered silicate-based particle has a columnar structure in which the maximum diameter of the orthogonal cross-section is 1 nm to 100 nm and the height is 0.01 nm to 20 nm.

2. The superabsorbent polymer of claim 1 , wherein
the plurality of pores having a diameter of 1 μm or greater formed in the base polymer powder comprise micropores having a diameter of 10 μm to 100 μm.

3. The superabsorbent polymer of claim 1 , wherein
a time required to remove a vortex generated by stirring 50 ml of a 0.9 wt % NaCl solution at a rate of 600 rpm at room temperature is 60 seconds or less.

4. The superabsorbent polymer of claim 1 , wherein
the layered silicate-based particle comprises a unit crystal which includes a metal oxide layer containing a metal oxide and a silica layer containing silica which is formed on at least one surface of the metal oxide layer.

5. The superabsorbent polymer of claim 1 , wherein
the layered silicate-based particle is contained in an amount of 0.01 parts by weight to 30 parts by weight based on 100 parts by weight of the base polymer powder.

6. The superabsorbent polymer of claim 1 , wherein
the water-soluble ethylenically unsaturated monomer comprises at least one selected from the group consisting of an anionic monomer of acrylic acid, methacrylic acid, maleic anhydride, fumaric acid, crotonic acid, itaconic acid, 2-acryloylethane sulfonic acid, 2-methacryloylethane sulfonic acid, 2-(meth)acryloylpropane sulfonic acid, and 2-(meth)acrylamide-2-methylpropane sulfonic acid, and a salt thereof;
a nonionic hydrophilic monomer of (meth)acrylamide, N-substituted (meth)acrylate, 2-hydroxyethyl(meth)acrylate, 2-hydroxypropyl(meth)acrylate, methoxypolyethylene glycol (meth)acrylate, or polyethylene glycol (meth)acrylate; and
an unsaturated monomer containing an amino group of (N,N)-dimethylaminoethyl(meth)acrylate or (N,N)-dimethylaminopropyl(meth)acrylamide, and a quaternary compound thereof.

7. The superabsorbent polymer of claim 1 , wherein
the crosslinked polymer comprises a crosslinked structure in which polymer chains of the water-soluble ethylenically unsaturated monomer are crosslinked through a cross-linkable functional group of an internal crosslinking agent.

8. The superabsorbent polymer of claim 1 , wherein
the crosslinked polymer comprises a crosslinked polymer which is polymerized in the presence of an internal crosslinking agent containing a polyfunctional acrylate-based compound having the water-soluble ethylenically unsaturated monomer having a plurality of ethylene oxide groups.

9. The superabsorbent polymer of claim 7 , wherein
the internal crosslinking agent comprises at least one selected from the group consisting of polyethylene glycol diacrylate (PEGDA), glycerin diacrylate, glycerin triacrylate, unmodified or ethoxylated trimethylolpropane triacrylate (TMPTA), hexanediol diacrylate, and triethylene glycol diacrylate.

10. A method for preparing the superabsorbent polymer of claim 1 , comprising the steps of:
crosslinking a monomer composition which contains the layered silicate-based particle, a foaming agent, an internal crosslinking agent, and the water-soluble ethylenically unsaturated monomer having an acidic group in which at least a part thereof is neutralized, and which is stirred at a rate of 1000 rpm or greater, to prepare a hydrogel polymer; and
drying, pulverizing, and classifying the hydrogel polymer to form a base polymer powder,
wherein a concentration of the water-soluble ethylenically unsaturated monomer contained in the monomer composition is 40% by weight to 60% by weight.

11. A method for preparing the superabsorbent polymer of claim 1 , comprising the steps of:
crosslinking a monomer composition which contains the layered silicate-based particle, a foaming agent, an internal crosslinking agent, and the water-soluble ethylenically unsaturated monomer having an acidic group in which at least a part thereof is neutralized, and which is stirred at a rate of 1000 rpm or greater to prepare a hydrogel polymer; and
drying, pulverizing, and classifying the hydrogel polymer to form a base polymer powder,
wherein the step of drying, pulverizing, and classifying the hydrogel polymer to form a base polymer powder comprises a course pulverization step of pulverizing the hydrogel polymer so that the particle diameter thereof is 2 mm to 10 mm, and
wherein the course pulverizing step is carried out at a temperature of 50° C. or greater and a frequency of 15 Hz or greater.

12. A method for preparing the superabsorbent polymer of claim 1 , comprising the steps of:
crosslinking a monomer composition which contains the layered silicate-based particle, a foaming agent, an internal crosslinking agent, and the water-soluble ethylenically unsaturated monomer having an acidic group in which at least a part thereof is neutralized, and which is stirred at a speed of 1000 rpm or greater, to prepare a hydrogel polymer; and
drying, pulverizing, and classifying the hydrogel polymer to form a base polymer powder,
wherein the step of drying, pulverizing, and classifying the hydrogel polymer to form a base polymer powder comprises a course pulverization step of pulverizing the hydrogel polymer so that the diameter thereof is 2 mm to 10 mm, and
wherein the method further comprises, before or after the course pulverization, a step of adding water in an amount of less than 20 parts by weight based on 100 parts by weight of the hydrogel polymer.

13. The method for preparing a superabsorbent polymer of claim 10 , wherein
the layered silicate-based particle is used in an amount of 1 to 50 parts by weight based on 100 parts by weight of the foaming agent.

14. The method for preparing a superabsorbent polymer of claim 10 , wherein
the foaming agent comprises at least one selected from the group consisting of azodicarbonamide, azodicarboxylamide, benzenesulfonyl hydrazide, dinitrosopentamethylenetetramine, toluenesulfonyl hydrazide, azobisisobutyronitrile, barium azodicarboxylate, and sodium bicarbonate.

15. The superabsorbent polymer of claim 8 , wherein
the internal crosslinking agent comprises at least one selected from the group consisting of polyethylene glycol diacrylate (PEGDA), glycerin diacrylate, glycerin triacrylate, unmodified or ethoxylated trimethylolpropane triacrylate (TMPTA), hexanediol diacrylate, and triethylene glycol diacrylate.

16. The method for preparing a superabsorbent polymer of claim 11 , wherein
the layered silicate-based particle is used in an amount of 1 to 50 parts by weight based on 100 parts by weight of the foaming agent.

17. The method for preparing a superabsorbent polymer of claim 12 , wherein
the layered silicate-based particle is used in an amount of 1 to 50 parts by weight based on 100 parts by weight of the foaming agent.

18. The method for preparing a superabsorbent polymer of claim 11 , wherein
the foaming agent comprises at least one selected from the group consisting of

Assignees

• Lg Chemical Ltd

Inventors

• Lee Kum Hyoung
• Kim Gi Cheul
• Park Sung Soo
• Yang Ye Sol
• Seong Bo Hyun

Classifications

• C08J9/0066

  Use of inorganic compounding ingredients · CPC title

• C08F2500/24

  Polymer with special particle form or size · CPC title

• C08J3/245

  Differential crosslinking of one polymer with one crosslinking type, e.g. surface crosslinking · CPC title

• C08J9/08

  developing carbon dioxide · CPC title

• C08J3/075 Primary

  Macromolecular gels · CPC title