Zeolite membrane composite and process for producing zeolite membrane composite

Patent metadata

Field	Value
Publication number	US-10994247-B2
Application number	US-201916568689-A
Country	US
Kind code	B2
Filing date	Sep 12, 2019
Priority date	Mar 31, 2017
Publication date	May 4, 2021
Grant date	May 4, 2021

Abstract

A process for producing a zeolite membrane composite includes a step of obtaining FAU-type seed crystals, a step of depositing the FAU-type seed crystals on a support, a step of forming an AFX-type zeolite membrane on the support by immersing the support in a raw material solution and growing an AFX-type zeolite from the FAU-type seed crystals by hydrothermal synthesis, and a step of removing a structure-directing agent from the AFX-type zeolite membrane. In this way, the AFX-type zeolite membrane can be provided.

First claim

The invention claimed is:

1. A zeolite membrane composite comprising:
a support;
an FAU type zeolite membrane; and
an AFX type zeolite membrane;
wherein the FAU type zeolite membrane is located between the support and the AFX type zeolite membrane, and the AFX type zeolite membrane is formed on the FAU type zeolite membrane.

2. The zeolite membrane composite according to claim 1 , wherein
the AFX type zeolite membrane is a zeolite membrane made of aluminosilicate zeolite.

3. The zeolite membrane composite according to claim 1 , wherein
the AFX type zeolite membrane is in direct contact with the support.

4. The zeolite membrane composite according to claim 1 , wherein the FAU type zeolite membrane is a Y- or X-type zeolite membrane.

5. The zeolite membrane composite according to claim 1 , wherein the support is porous.

6. The zeolite membrane composite according to claim 1 , wherein
the support is a sintered alumina compact, a sintered mullite compact, or a sintered titania compact.

7. A process for producing a zeolite membrane composite, comprising:
a) obtaining an FAU type seed crystal;
b) depositing the FAU type seed crystal on a support;
c) making the FAU type seed crystal on the support in the form of a membrane by hydrothermal synthesis;
d) forming an AFX type zeolite membrane on the AFX type seed crystal membrane by immersing the support in a raw material solution and growing an AFX type zeolite from the FAU type seed crystal membrane by hydrothermal synthesis; and
e) removing a structure-directing agent from the AFX type zeolite membrane.

8. The process for producing a zeolite membrane composite according to claim 7 , wherein when the operation c) has been completed, the AFX type zeolite membrane is in direct contact with the support.

9. The process for producing a zeolite membrane composite according to claim 7 , wherein the FAU type seed crystal is a Y- or X-type zeolite.

10. The process for producing a zeolite membrane composite according to claim 7 ,
wherein in the operation b), the FAU type seed crystal is deposited on a surface of the support that faces a generally vertical direction or a downward direction during production of the zeolite membrane composite.

11. A zeolite membrane composite produced by the process for producing a zeolite membrane composite according to claim 7 .

Assignees

• Ngk Insulators Ltd

Inventors

• Miyahara Makoto
• Noda Kenichi

Classifications

• B01D71/024

  Oxides · CPC title

• B01D69/108

  Inorganic support material · CPC title

• B01D71/0281 Primary

  Zeolites · CPC title

• B01D2325/30

  Chemical resistance · CPC title

• B01J20/28033

  Membrane, sheet, cloth, pad, lamellar or mat · CPC title