Lithium battery cathode and method of manufacturing

Patent metadata

Field	Value
Publication number	US-10985373-B2
Application number	US-201715442803-A
Country	US
Kind code	B2
Filing date	Feb 27, 2017
Priority date	Feb 27, 2017
Publication date	Apr 20, 2021
Grant date	Apr 20, 2021

Abstract

Provided is cathode active material layer for a lithium battery. The cathode active material layer comprises multiple cathode active material particles and an optional conductive additive that are bonded together by a binder comprising a high-elasticity polymer having a recoverable tensile strain from 5% to 700% (preferably from 10% to 100%) when measured without an additive or reinforcement in said polymer and a lithium ion conductivity no less than 10−5 S/cm (preferably and typically from 1.0×10−5 S/cm to 5×10−2 S/cm) at room temperature.

First claim

We claim:

1. A cathode active material layer for a lithium battery, said cathode active material layer comprising multiple cathode active material particles and an optional conductive additive that are bonded together by a binder comprising a high-elasticity polymer having a recoverable tensile strain from 5% to 700% when measured without an additive or reinforcement in said polymer and a lithium ion conductivity no less than 10 −5 S/cm at room temperature, wherein said high-elasticity polymer forms a mixture or interpenetrating network with an elastomer selected from natural polyisoprene, synthetic polyisoprene, polybutadiene, chloroprene rubber, polychloroprene, butyl rubber, styrene-butadiene rubber, nitrile rubber, ethylene propylene rubber, ethylene propylene diene rubber, epichlorohydrin rubber, polyacrylic rubber, silicone rubber, fluorosilicone rubber, perfluoroelastomers, polyether block amides, chlorosulfonated polyethylene, ethylene-vinyl acetate, protein resilin, protein elastin, ethylene oxide-epichlorohydrin copolymer, polyurethane, urethane-urea copolymer, or a combination thereof.

2. The cathode active material layer of claim 1 , wherein said high-elasticity polymer contains a cross-linked network of polymer chains having an ether linkage, nitrile-derived linkage, benzo peroxide-derived linkage, ethylene oxide linkage, propylene oxide linkage, vinyl alcohol linkage, cyano-resin linkage, triacrylate monomer-derived linkage, tetraacrylate monomer-derived linkage, or a combination thereof in said cross-linked network of polymer chains.

3. The cathode active material layer of claim 1 , wherein said high-elasticity polymer contains a cross-linked network of polymer chains selected from nitrile-containing polyvinyl alcohol chains, cyanoresin chains, pentaerythritol tetraacrylate chains, pentaerythritol triacrylate chains, ethoxylated trimethylolpropane triacrylate (ETPTA) chains, ethylene glycol methyl ether acrylate (EGMEA) chains, or a combination thereof.

4. The cathode active material layer of claim 1 , wherein said cathode active material is selected from an inorganic material, an organic material, a polymeric material, or a combination thereof.

5. The cathode active material layer of claim 4 , wherein said inorganic material is selected from a metal oxide, metal phosphate, metal silicide, metal selenide, transition metal sulfide, or a combination thereof.

6. The cathode active material layer of claim 5 , wherein said metal oxide contains a vanadium oxide selected from the group consisting of VO 2 , Li x VO 2 , V 2 O 5 , Li x V 2 O 5 , V 3 O 8 , Li x V 3 O 8 , Li x V 3 O 7 , V 4 O 9 , Li x V 4 O 9 , V 6 O 13 , Li x V 6 O 13 , their doped versions, their derivatives, and combinations thereof, wherein 0.1<x<5.

7. The cathode active material layer of claim 5 , wherein said metal oxide or metal phosphate is selected from a layered compound LiMO 2 , spinel compound LiM 2 O 4 , olivine compound LiMPO 4 , silicate compound Li 2 MSiO 4 , Tavorite compound LiMPO 4 F, borate compound LiMBO 3 , or a combination thereof, wherein M is a transition metal or a mixture of multiple transition metals.

8. The cathode active material layer of claim 5 , wherein said inorganic material is selected from: (a) bismuth selenide or bismuth telluride, (b) transition metal dichalcogenide or trichalcogenide, (c) sulfide, selenide, or telluride of niobium, zirconium, molybdenum, hafnium, tantalum, tungsten, titanium, cobalt, manganese, iron, nickel, or a transition metal; (d) boron nitride, or (e) a combination thereof.

9. The cathode active material layer of claim 4 , wherein said inorganic material is selected from a lithium cobalt oxide, lithium nickel oxide, lithium manganese oxide, lithium vanadium oxide, lithium-mixed metal oxide, lithium iron phosphate, lithium manganese phosphate, lithium vanadium phosphate, lithium mixed metal phosphate, lithium metal silicide, or a combination thereof.

10. The cathode active material layer of claim 4 , wherein said inorganic material is selected from a metal fluoride or metal chloride including the group consisting of CoF 3 , MnF 3 , FeF 3 , VF 3 , VOF 3 , TiF 3 , BiF 3 , NiF 2 , FeF 2 , CuF 2 , CuF, SnF 2 , AgF, CuCl 2 , FeCl 3 , MnCl 2 , and combinations thereof.

11. The cathode active material layer of claim 4 , wherein said inorganic material is selected from a lithium transition metal silicate, denoted as Li 2 MSiO 4 or Li 2 Ma x Mb y SiO 4 , wherein M and Ma are selected from Fe, Mn, Co, Ni, V, or VO; Mb is selected from Fe, Mn, Co, Ni, V, Ti, Al, B, Sn, or Bi; and x+y≤1.

12. The cathode active material layer of claim 4 , wherein said inorganic material is selected from a transition metal dichalcogenide, a transition metal trichalcogenide, or a combination thereof.

13. The cathode active material layer of claim 4 , wherein said inorganic material is selected from TiS 2 , TaS 2 , MoS 2 , NbSe 3 , MnO 2 , CoO 2 , an iron oxide, a vanadium oxide, or a combination thereof.

14. The cathode active material layer of claim 4 , wherein said organic material or polymeric material is selected from poly(anthraquinonyl sulfide) (PAQS), a lithium oxocarbon, 3,4,9,10-perylenetetracarboxylic dianhydride (PTCDA), poly(anthraquinonyl sulfide), pyrene-4,5,9,10-tetraone (PYT), polymer-bound PYT, quino(triazene), redox-active organic material, tetracyanoquinodimethane (TCNQ), tetracyanoethylene (TCNE), 2,3,6,7,10,11-hexamethoxytriphenylene (HMTP), poly(5-amino-1,4-dyhydroxy anthraquinone) (PADAQ), phosphazene disulfide polymer ([(NPS 2 ) 3 ]n), lithiated 1,4,5,8naphthalenetetraol formaldehyde polymer, hexaazatrinaphtylene (HATN), hexaazatriphenylene hexacarbonitrile (HAT(CN) 6 ), 5-benzylidene hydantoin, isatine lithium salt, pyromellitic diimide lithium salt, tetrahydroxy-p-benzoquinone derivatives (THQLi 4 ), N,N′-diphenyl-2,3,5,6-tetraketopiperazine (PHP), N,N′-diallyl-2,3,5,6-tetraketopiperazine (AP), N,N′-dipropyl-2,3,5,6-tetraketopiperazine (PRP), a thioether polymer, a quinone compound, 1,4-benzoquinone, 5,7,12,14-pentacenetetrone (PT), 5-amino-2,3-dihydro-1,4-dyhydroxy anthraquinone (ADDAQ), 5-amino-1,4-dyhydroxy anthraquinone (ADAM), calixquinone, Li 4 C 6 O 6 , Li 2 C 6 O 6 , Li 6 C 6 O 6 , or a combination thereof.

15. The cathode active material layer of claim 14 , wherein said thioether polymer is selected from poly[methanetetryl-tetra(thiomethylene)] (PMTTM), poly(2,4-dithiopentanylene) (PDTP), a polymer containing poly(ethene-1,1,2,2-tetrathiol) (PETT) as a main-chain thioether polymers, a side-chain thioether polymer having a main-chain consisting of conjugating aromatic moieties, and having a thioether side chain as a pendant, poly(2-phenyl-1,3-dithiolane) (PPDT), poly(1,4-di(1,3-dithiolan-2-yl)benzene) (PDDTB), poly(tetrahydrobenzodithiophene) (PTHBDT), poly[1,2,4,5-tetrakis(propylthio)benzene] (PTKPTB), or poly[3,4(ethylenedithio)thiophene] (PEDTT).

16. The cathode active material layer of claim 4 , wherein said organic material contains a phthalocyanine compound selected from copper phthalocyanine, zinc phthalocyanine, tin phthalocyanine, iron phthalocyanine, lead phthalocyanine, nickel phthalocyanine, vanadyl phthalocyanine, fluorochromium phthalocyanine, magnesium phthalocyanine, manganous phthalocyanine, dilithium phthalocyanine, aluminum phthalocyanine chloride, cadmium phthalocyanine, chlorogallium phthalocyanine, cobalt phthalocyanine, silver phthalocyanine, a metal-free phthalocyanine, a chemical derivative thereof, or a combination thereof.

17. The cathode active material layer of claim 1 , wherein said cathode active material is in a form of nano particle, nano

Assignees

• Global Graphene Group Inc

Inventors

• Pan Baofei
• He Hui
• Zhamu Aruna
• Jang Bor Z

Classifications

• Y02E60/10

  Energy storage using batteries · CPC title

• H01M2300/0091

  in the form of mixtures · CPC title

• H01M2300/0082

  Organic polymers · CPC title

• H01M2300/0068

  inorganic · CPC title

• H01M2004/028

  Positive electrodes · CPC title