Resin composition, molded product and method for its production, prepreg and method for its production, and fiber-reinforced molded product and method for its production

Patent metadata

Field	Value
Publication number	US-10982063-B2
Application number	US-202016751301-A
Country	US
Kind code	B2
Filing date	Jan 24, 2020
Priority date	Sep 14, 2017
Publication date	Apr 20, 2021
Grant date	Apr 20, 2021

Abstract

To provide a resin composition, wherein the resin composition is excellent in impregnation into a reinforcing fiber sheet as it contains a polyamide having a low viscosity number; wherein the resin composition can be molded into a film, a fiber, etc., even though it contains a polyamide having a low viscosity number; and wherein the resin composition can produce a fiber-reinforced molded product having excellent impact resistance; a molded product and a method for its production; and a fiber-reinforced molded product having excellent impact resistance and a method for its production.
A resin composition comprising:
a polyamide having a viscosity number of from 100 to 170 determined by a method specified in ISO 307: 2007; and a melt-processable fluororesin having at least one type of a functional group selected from the group consisting of a carbonyl group-containing group, a hydroxy group, an epoxy group and an isocyanate group, and having a melting point of from 100 to 325° C.

First claim

What is claimed is:

1. A resin composition comprising:
a polyamide haying a viscosity number of from 100 to 170 determined by a method specified in ISO 307: 2007; and
a melt-processable fluororesin having at least one type of a functional group selected from the group consisting of a carbonyl group-containing group, a hydroxy group, an epoxy group and an isocyanate group, the melt-processable fluororesin haying a melting point of from 100 to 325°C.,
wherein the polyamide and the melt-processable fluororesin are melt-blended.

2. The resin composition according to claim 1 , wherein the polyamide is at least one type selected from the group consisting of polyamide 6, polyamide 66, polyamide 46, polyamide 11, polyamide 12, polyamide 9T, polyamide 610, polyamide 612, polyamide 6/66 copolymer, polyamide 6/66/610 copolymer, polyamide 6T, polyamide 6I and polyamide MXD6.

3. The resin composition according to claim 1 , wherein the polyamide is polyamide 6, and the melt flow rate of the resin composition measured at a temperature of 260° C. under a load of 21.2N is from 20 to 150 g/10 min.

4. The resin composition according to claim 1 , wherein the polyamide is polyamide 12 and the melt flow rate of the resin composition measured at a temperature of 250° C. under a load of 21.2N is from 20 to 120 g/10 min.

5. The resin composition according to claim 1 , wherein, in the total volume of the polyamide and the fluororesin, the polyamide is from 55 to 95% by volume and the fluororesin is from 5 to 45% by volume, and the total of the polyamide and the fluororesin is from 80 to 100 mass % of the resin composition.

6. A prepreg comprising a matrix resin and a reinforcing fiber, wherein the matrix resin is the resin composition as defined in claim 1 .

7. The prepreg according to claim 6 , wherein the reinforcing fiber is a spread reinforcing fiber.

8. The prepreg according to claim 6 , wherein the reinforcing fiber is a reinforcing fiber textile, a reinforcing fiber knitting, or a unidirectional reinforcing fiber bundle.

9. A fiber-reinforced molded product, formed by molding the prepreg as defined in claim 6 .

10. A molded product made of the resin composition as defined in claim 1 .

11. The molded product according to claim 10 , wherein the molded product is a film or a fiber.

12. A method for producing a fiber-reinforced molded product, wherein a reinforcing fiber sheet and the film as defined in claim 11 are laminated in a mold and then molded by hot pressing.

13. A method for producing a prepreg, wherein the molded product as defined in claim 10 is melted in the presence of a reinforcing fiber sheet and impregnated in the reinforcing fiber sheet.

14. The method for producing a prepreg according to claim 13 , wherein the reinforcing fiber sheet is a spread reinforcing fiber sheet.

15. The method for producing a prepreg according to claim 13 , wherein the reinforcing fiber sheet is a reinforcing fiber textile, a reinforcing fiber knitting, or a unidirectional reinforcing fiber bundle.

16. A method for producing a fiber-reinforced molded product, wherein a prepreg is obtained in accordance with the method for producing a prepreg as defined in claim 13 and then the prepreg is molded.

Assignees

• Agc Inc

Inventors

• Ozawa Norio
• Hosoda Tomoya
• Sato Takashi

Classifications

• B29C70/465 Primary

  and impregnating by melting a solid material, e.g. sheets, powders of fibres · CPC title

• C08J5/243

  using carbon fibres · CPC title

• B29C70/003

  characterised by the matrix material, e.g. material composition or physical properties · CPC title

• B32B15/14

  next to a fibrous or filamentary layer · CPC title

• B32B2260/046

  Synthetic resin · CPC title