Method for manufacturing molded product including real wood

Patent metadata

Field	Value
Publication number	US-10981309-B2
Application number	US-201916280189-A
Country	US
Kind code	B2
Filing date	Feb 20, 2019
Priority date	May 3, 2018
Publication date	Apr 20, 2021
Grant date	Apr 20, 2021

Abstract

The present disclosure relates to a method for manufacturing a molded product including real wood capable of forming a real wood layer on the surface of an injected molded product by using an IMD film provided with a real wood stacked body. According to the method, it is possible to manufacture the IMD film provided with the real wood stacked body on the release film, and to form the real wood layer on the surface of the injected molded product without breakage by using the IMD film.

First claim

What is claimed is:

1. A method for manufacturing a molded product comprising:
preparing an in-mold decoration film provided with a real wood stacked body on a release film, said real wood stacked body including a real wood layer and one or more of an adhesive layer and a fiber layer;
supplying the in-mold decoration film so that the real wood stacked body is disposed at an injecting point;
fixing the in-mold decoration film by deforming and reshaping the real wood stacked body to correspond to the shape of a mold cavity of a lower mold and contacting the in-mold decoration film to the mold cavity of the lower mold through vacuum absorption;
forming an injecting layer by coupling an upper mold and the lower mold, and injecting a melted injecting material into the mold cavity of the lower mold through the upper mold and then curing the injecting material; and
ejecting a molded product in which the release film has been separated from the real wood stacked body by separating the lower mold and the upper mold,
wherein preparing the in-mold decoration film comprises:
forming the real wood layer in the form of a thin film having a predetermined thickness by cutting natural wood;
attaching the fiber layer on the lower surface of the real wood layer;
pre-processing the real wood stacked body having the fiber layer stacked thereon in order to prevent discoloration of the real wood layer; and
manufacturing the in-mold decoration film by attaching a plurality of pre-processed real wood stacked bodies to the release film to be spaced at a certain interval apart from each other, and attaching the real wood layer of each of the stacked bodies to the release film.

2. The method for manufacturing the molded product of claim 1 , wherein the forming of the real wood layer comprises cutting the real wood layer into a thin film having a thickness of 0.1 mm to 1.0 mm.

3. The method for manufacturing the molded product of claim 1 , wherein the fiber layer is attached to the real wood layer by using the adhesive layer, or by using a thermal compression bonding method.

4. The method for manufacturing the molded product of claim 1 , wherein the pre-processing comprises:
decolorizing the real wood stacked body by using decolorizing agent;
washing the real wood stacked body upon having completed decolorization; and
drying the washed real wood stacked body.

5. The method for manufacturing the molded product of claim 4 , wherein the decolorizing is accomplished by using the decolorizing agent prepared with a hydrogen peroxide dilution solution to which no ammonia is added, or the hydrogen peroxide dilution solution to which ammonia is added.

6. The method for manufacturing the molded product of claim 5 , wherein the hydrogen peroxide dilution solution is prepared by mixing pure water and hydrogen peroxide at a weight percent ratio of 80:20 to 50:50.

7. The method for manufacturing the molded product of claim 5 , wherein the hydrogen peroxide dilution solution is prepared by mixing pure water and hydrogen peroxide at a weight percent ratio of 80:20 to 50:50 and then adding ammonia such that the ammonia constitutes 5 to 20 wt. % of the hydrogen peroxide dilution solution.

8. The method for manufacturing the molded product of claim 1 , wherein the release film is prepared from any one of polyethylene terephthalate, polyethylene, polypropylene, and cast polypropylene, and a thickness the film is 0.1 mm to 1.0 mm.

9. The method for manufacturing the molded product of claim 1 , wherein the in-mold decoration film is supplied in the form of a roll in order to continuously supply the real wood stacked body to the lower mold.

10. The method for manufacturing the molded product of claim 1 , wherein said method further comprises forming a coating layer for covering the real wood layer in order to protect the real wood layer.

11. The method for manufacturing the molded product of claim 10 , wherein the coating layer is formed by attaching a resin in the form of a film to the real wood layer after the pre-processing, or the coating layer is formed by applying a resin in a liquid state to the real wood layer.

12. The method for manufacturing the molded product of claim 10 , wherein the coating layer is formed on the real wood layer by using an insert injecting molding after disposing the molded product in the lower mold after the ejection of the molded product, or the coating layer is formed by applying a resin in a liquid state to the real wood layer of the molded product.

13. The method for manufacturing the molded product of claim 1 , wherein the fixing of the in-mold decoration film comprises:
fixing the position of the in-mold decoration film by contacting the portion of the release film whereon the in-mold decoration film is disposed to the upside surface of the lower mold, by operating a close contact part provided at the outside of a mold cavity in the lower mold; and
vacuum-absorbing the portion of the release film provided with the real wood stacked body comprising the in-mold decoration film to the inside surface of the mold cavity by performing vacuum exhaust through a suction hole formed in the lower mold.

14. The method for manufacturing the molded product of claim 1 , wherein the molded product is ejected after separating the release film from the real wood stacked body when the upper mold is separated from the lower mold, wherein the adhesive force between the upper mold and the injecting layer is stronger than the adhesive force between the real wood stacked body and the release firm, so that the molded product is detached from the release film.

15. A method for manufacturing a molded product comprising:
providing a real wood stacked body, said real wood stacked body including a real wood layer and a fiber layer adhesively connected to a bottom surface of said real wood layer, said real wood layer having a thickness of 0.1-1 mm, said fiber layer including a woven fabric or non-woven fabric, said fiber layer having a thickness of 0.1-1 mm;
providing a release film, said release film having a thickness of 0.1-1 mm, said release film including one or more materials selected from the group consisting of polyethylene terephthalate, polyethylene, polypropylene, casting polypropylene, thermoplastic polyurethane, ethylene-vinyl acetate, polyethersulfone, and polyamide;
applying said release film to a) a top surface of said real wood layer or b) a top surface of a coating layer, said coating layer applied to said top surface of said real wood layer, said coating layer including one or more materials selected from the group consisting of polycarbonate resin, polyurethane resin, epoxy resin, acrylonitrile butadiene styrene resin, polypropylene resin, and polyacetal resin;
providing a molding machine, said molding machine including a top and bottom mold portion, said bottom mold portion including a bottom mold cavity, said bottom mold cavity including a plurality of vacuum passages connected to a bottom surface of said bottom mold cavity;
positioning said release film and said real wood stacked body over said bottom mold cavity, said release film positioned between said bottom mold cavity and said real wood stacked body;
deforming and reshaping said real wood stacked body by causing said real wood stacked body to be moved into said bottom mold cavity, said step of deforming including applying a vacuum to said plurality of vacuum passages causing said real wood stacked body to be drawn into said bottom mold cavity;
forming an injecting layer on a bottom surface of said real wood stacked body to form said molded product, said step of formi

Assignees

• Seoyon E Hwa Co Ltd

Inventors

• Song Su Wan

Classifications

• B32B2262/0284

  Polyethylene terephthalate [PET] or polybutylene terephthalate [PBT] · CPC title

• B29C45/14008

  Inserting articles into the mould (B29C45/14827 takes precedence) · CPC title

• B29C2045/14155

  using vacuum or suction · CPC title

• B29C45/14827

  using a transfer foil detachable from the insert · CPC title

• B32B21/10

  Next to a fibrous or filamentary layer · CPC title