Semi-rigid polyurethane foam and process to make

Patent metadata

Field	Value
Publication number	US-10975211-B2
Application number	US-201716089015-A
Country	US
Kind code	B2
Filing date	Mar 8, 2017
Priority date	Mar 29, 2016
Publication date	Apr 13, 2021
Grant date	Apr 13, 2021

Abstract

Disclosed is a composition and process for making a water blown semi-rigid polyurethane foam wherein the polyisocyanate side and the polyol side are combined under ambient temperature conditions. Said foams are particularly suited for sound and vibration management, especially in motor vehicles.

First claim

What is claimed is:

1. A process to form a semi-rigid polyurethane foam, comprising the reaction product of:
a) an A-side comprising
i) 65 to 85 wt % of a polymeric MDI blend,
ii) 10 to 35 wt % of a plasticizer, and
iii) 0.2 to 1.5 wt % of a first A-side surfactant,
wherein the A-side weight percents are based on the total weight of the A-side,

b) a B-side comprising:
i) 10 to 40 wt % of a copolymer polyol containing at least 40% solids,
ii) 10 to 40 wt % of a polyether polyol having a functionality equal to or greater than 3 and equal to and less than 8, wherein said polyether polyol has a viscosity at 25° C. of at least about 500 cP, as measured according to ASTM D455, and wherein said polyether polyol has an average molecular weight of from 100 to 10,000,
iii) 10 to 25 wt % of an autocatalytic aromatic polyol,
iv) 1 to 10 wt % of a tertiary amine catalyst,
v) 0.5 to 2 wt % of a first B-side surfactant, and
vi) 5 to 15 wt % water,
wherein the B-side weight percents are based on the total weight of the B-side, said process comprising the steps of:

A) forming a reactive blend by mixing said A-side and said B-side at 130° F. or less in a ratio, (A-side):(B-side), of 1:1 to 5:1 by volume; and
B) subjecting the resulting reactive blend to conditions sufficient to cure the reactive blend to form a semi-rigid polyurethane foam,

wherein said semi-rigid polyurethane foam fails to resist permanent deformation after repeated compression in excess of 50%.

2. The process of claim 1 wherein the B-side further comprises:
vii) 2 to 6 wt % of a crosslinker.

3. The process of claim 1 wherein the polymeric MDI blend a) i) has an NCO range of 18 to 25%.

4. The process of claim 1 wherein the first A-side surfactant a) iii) is an organosilicone.

5. The process of claim 4 further comprising a)iv) 0.2 to 1.5 wt % of a second A-side surfactant different from the first A-side surfactant, wherein the said second A-side surfactant is an organosilicone.

6. The process of claim 1 wherein the semi-rigid polyurethane foam is used in an automobile noise and vibration-absorbing application.

Assignees

• Dow Global Technologies Llc

Inventors

• El-Khatib Ali J

Classifications

• C08J2375/04

  Polyurethanes · CPC title

• C08G18/329 Primary

  containing aromatic groups · CPC title

• C08G18/632

  onto polyethers · CPC title

• C08G18/4841 Primary

  containing oxyethylene end groups · CPC title

• C08G18/425

  the polyols containing one or two ether groups · CPC title