Laminated film, production method thereof, polarizing plate, liquid crystal panel, liquid crystal display, and touch panel

Patent metadata

Field	Value
Publication number	US-10974482-B2
Application number	US-201816161434-A
Country	US
Kind code	B2
Filing date	Oct 16, 2018
Priority date	Apr 19, 2016
Publication date	Apr 13, 2021
Grant date	Apr 13, 2021

Abstract

A laminated film having a haze of 1.0% or less and including two kinds of silica particles (silica particles A and silica particles B) in a cured layer, wherein the occupied area proportion of the silica particles A on a cross-sectional TEM image of the cured layer is 0.5% to 20.0% and satisfies the following relationship with the occupied area proportion of the silica particles B: 0.005≤occupied area proportion of silica particles A/occupied area proportion of silica particles B≤0.400, the variation coefficient of the occupied area proportion of the silica particles A on the cross-sectional TEM image of the cured layer is more than 0.5% and 3.0% or less, and the variation coefficient of the occupied area proportion of the silica particles B is 0.0% to 0.5%; a production method thereof; a polarizing plate; a liquid crystal panel; a liquid crystal display; and a touch panel.

First claim

What is claimed is:

1. A laminated film comprising:
a substrate film; and
a cured layer obtained by curing a curable composition,
wherein the haze of the laminated film is 1.0% or less,
wherein the cured layer includes:
silica particles A: silica particles which have a hydrophobic group on a surface thereof and an average primary particle diameter in the range of 5 to 50 nm, and are observed as a continuous black portion with a length of 100 nm or more in a binarized image obtained by subjecting a cross-sectional transmission electron microscopic image of the cured layer to a binarization processing, and
silica particles B: silica particles other than the silica particles A, which have a hydrophobic group on a surface thereof and an average primary particle diameter in the range of 7 to 50 nm,
wherein an occupied area proportion of the silica particles A in the cross-sectional transmission electron microscopic image of the cured layer is in the range of 0.5% to 20.0%, and satisfies a relationship of the following formula with an occupied area proportion of the silica particles B in the cross-sectional transmission electron microscopic image of the cured layer:
0.005≤occupied area proportion of silica particles A/occupied area proportion of silica particles B≤0.400,
wherein in the cross-sectional transmission electron microscopic image of the cured layer, the variation coefficient of the occupied area proportion of the silica particles A is more than 0.5% and 3.0% or less, and the variation coefficient of the occupied area proportion of the silica particles B is in the range of 0.0% to 0.5%, and
wherein a Brunauer-Emmett-Teller (BET) method specific surface area of the silica particles A is in the range of 30 to 400 m 2 /g.

2. The laminated film according to claim 1 ,
wherein a total amplitude at a wavelength of 2.50 to 5.00 μm of an unevenness profile measured on the surface of a cured layer is in the range of 0.007 to 0.050 nm, and the maximum height St of the unevenness profile measured on the surface of the cured layer is in the range of 7 to 100 nm.

3. The laminated film according to claim 1 ,
wherein the silica particles A have a value obtained by dividing a carbon content of the silica particles A (g/m 2 ) by the Brunauer-Emmett-Teller (BET) method specific surface area in the range of 0.005 to 0.150.

4. The laminated film according to claim 1 ,
wherein the silica particles A have a value obtained by dividing a carbon content of the silica particles A (g/m 2 ) by the Brunauer-Emmett-Teller (BET) method specific surface area in the range of 0.010 to 0.030.

5. The laminated film according to claim 1 ,
wherein the hydrophobic group on the surface of the silica particles B is selected from the group consisting of an alkylsilyl group, a vinylsilyl group-derived residue, an epoxysilyl group-derived residue, and a (meth)acryloxysilyl group-derived residue.

6. The laminated film according to claim 1 ,
wherein the curable composition includes a curable compound selected from the group consisting of a polyfunctional (meth)acrylate compound and an epoxy compound.

7. The laminated film according to claim 1 ,
wherein the curable composition further includes a polymerization initiator.

8. The laminated film according to claim 1 , wherein the content of the silica particles A ranges from 0.3% by mass to 5.0% by mass based on the total mass of the cured layer.

9. The laminated film according to claim 1 ,
wherein the occupied area proportion of the silica particles A in the cross-sectional transmission electron microscopic image of the cured layer satisfies a relationship of the following formula with the occupied area proportion of the silica particles B in the cross-sectional transmission electron microscopic image of the cured layer:
0.005≤occupied area proportion of silica particles A/occupied area proportion of silica particles B≤0.150.

10. A polarizing plate comprising:
a polarizer; and
the laminated film according to claim 1 .

11. A liquid crystal panel comprising:
a liquid crystal display element; and
the polarizing plate according to claim 10 .

12. A liquid crystal display comprising:
the liquid crystal panel according to claim 11 ; and
a backlight unit.

13. A touch panel comprising the laminated film according to claim 1 .

14. A method for producing a laminated film,
wherein the laminated film is the laminated film according to claim 1 , and
the method comprising:
dispersing silica particles having a hydrophobic group on a surface thereof and an average primary particle diameter of 5 to 50 nm in an organic solvent to prepare a silica particle-containing composition 1;
mixing the silica particle-containing composition 1 with a silica particle-containing composition 2 including silica particles having a hydrophobic group on a surface thereof and an average primary particle diameter of 7 to 50 nm in an organic solvent, and a curable compound to prepare a curable composition;
applying the curable composition onto a substrate film; and
curing the applied curable composition.

15. The method for producing the laminated film according to claim 14 ,
wherein an average secondary particle diameter of the silica particles in the silica particle-containing composition 1 is in the range of 100 to 500 nm.

Assignees

• Fujifilm Corp

Inventors

• Suzuki Masaaki
• Iwasaki Tatsuya
• Takada Katsuyuki

Classifications

• G02B1/14 Primary

  Protective coatings, e.g. hard coatings · CPC title

• B32B2307/746

  Slipping, anti-blocking, low friction · CPC title

• G02F1/133502

  Antiglare, refractive index matching layers · CPC title

• G02F1/13338

  Input devices, e.g. touch panels · CPC title

• B32B27/38

  comprising epoxy resins · CPC title