Aqueous water barrier coatings

Patent metadata

Field	Value
Publication number	US-10961664-B2
Application number	US-201716305497-A
Country	US
Kind code	B2
Filing date	Jun 2, 2017
Priority date	Jun 3, 2016
Publication date	Mar 30, 2021
Grant date	Mar 30, 2021

Abstract

Described herein is a multi-phase polymer binder including an aqueous polymer dispersion, an optional hydrophobic emulsion, and an optional surfactant. The polymer binder, when dried, provides a water uptake of less than about 5 g/m2/20 min, a seal strength of at least about 200 Newton/meter (N/m) as measured at 25° C. or at 90° C., and sufficient block resistance to impart no substrate damage.

First claim

What is claimed is:

1. A multi-phase polymer binder comprising:
an aqueous polymer dispersion present in an amount of about 65 wt % to about 100 wt %;
a hydrophobic emulsion from 0 wt % to about 25 wt %; and
a surfactant from 0 wt % to about 10 wt %;
wherein:
the aqueous polymer dispersion comprises an acid-free copolymer present in an amount of about 40 wt % to about 95 wt % and an acid-rich copolymer present in an amount of about 1 wt % to about 60 wt %, wherein the acid-rich copolymer comprises carboxylic acid functional monomers in an amount of about 5 wt % to about 25 wt %, styrene in an amount of up to about 70 wt %, and (meth)acrylate monomers in an amount of about 10 wt % to about 90 wt %; and
the polymer binder, when dried, provides a water uptake of less than about 5 g/m 2 /20 min, a seal strength of at least about 200 Newton/meter (N/m) as measured at 25° C. or at 90° C., and sufficient block resistance to impart no substrate damage.

2. The multi-phase polymer binder of claim 1 , wherein the aqueous polymer dispersion is present in an amount of about 80 wt % to about 95 wt %.

3. The multi-phase polymer binder of claim 1 , wherein the hydrophobic emulsion is present in an amount of about 5 wt % to about 10 wt %.

4. The multi-phase polymer binder of claim 1 , wherein the surfactant is present in an amount of about 1 wt % to about 3 wt %.

5. The multi-phase polymer binder of claim 1 , wherein the acid-free copolymer comprises styrene in an amount of 15 wt % to about 40 wt %; and (meth)acrylate monomers in an amount of about 65 wt % to about 90 wt %.

6. The multi-phase polymer binder of claim 1 , wherein the hydrophobic emulsion is a wax emulsion.

7. The multi-phase polymer binder of claim 6 , wherein the wax emulsion comprises paraffin, polyethylene, polypropylene, microcrystalline waxes, fluorinated waxes, ethylene and propylene copolymer waxes, or any combination of two or more thereof.

8. The multi-phase polymer binder of claim 1 , wherein the surfactant is anionic or non-ionic.

9. The multi-phase polymer binder of claim 1 , wherein the surfactant comprises one or more alkyl sulfonates, alkyl benzene sulfonates, alkyl sulfates, alkyl benzene sulfates, phosphates, phosphinates, fatty carboxylates, or any combination of two or more thereof.

10. The multi-phase polymer binder of claim 1 , wherein the surfactant comprises one or more fatty alcohol ethoxylates.

11. The multi-phase polymer binder of claim 1 , wherein the surfactant comprises one or more alkylsulfosuccinate ethoxylates.

12. The multi-phase polymer binder of claim 1 , wherein the surfactant comprises one or more alkylsulfosuccinate ethoxylates and one or more fatty alcohol ethoxylates.

13. The multi-phase polymer binder of claim 1 , wherein the surfactant comprises:
one or more fatty alcohols having an alkyl chain length of about 12 to about 18 carbons; and
a degree of ethoxylation of about 10 to about 80 molar ethylene oxide units.

14. A substrate comprising at least one surface coated with at least one layer comprising a multi-phase polymer binder of claim 1 .

15. The substrate of claim 14 , wherein the substrate is paper or paperboard.

16. A process for making the multi-phase polymer binder of claim 1 , wherein the acid-free copolymer is prepared in the presence of the acid-rich copolymer or the aqueous polymer dispersion is prepared using a free radical emulsion polymerization process.

17. The process of claim 16 , wherein the acid-free copolymer is prepared in the presence of the acid-rich copolymer.

18. The process of claim 16 , wherein the aqueous polymer dispersion is prepared using a free radical emulsion polymerization process.

Assignees

• Basf Se

Inventors

• Deeter Gary A
• Reinhold Frank A
• Sardashti Amirpouyan
• Seecharan Andrew

Classifications

• D21H19/20

  comprising macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• C08F220/1804

  C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate · CPC title

• C09D133/064 Primary

  containing anhydride, COOH or COOM groups, with M being metal or onium-cation · CPC title

• C09D7/45

  Anti-settling agents · CPC title

• C09D5/024

  characterised by the additives · CPC title