Device comprising a cable or a cable accessory containing a fire-resistant composite layer

Patent metadata

Field	Value
Publication number	US-10961156-B2
Application number	US-201816224339-A
Country	US
Kind code	B2
Filing date	Dec 18, 2018
Priority date	Dec 19, 2017
Publication date	Mar 30, 2021
Grant date	Mar 30, 2021

Abstract

The present invention relates to a device comprising a cable and/or a cable accessory, said cable and/or said cable accessory comprising at least one composite layer obtained from a composite composition based on at least one cellulose derivative, at least one organic compound having a boiling point or a decomposition temperature above about 100° C. and at least one cement composition selected from an aluminosilicate geopolymer composition and a magnesium-based composition, as well as to a method of manufacturing such a device.

First claim

The invention claimed is:

1. A device comprising:
a power cable and/or a telecommunication cable, and/or
an accessory for a power cable and/or a telecommunication cable,
wherein said cable and/or said cable accessory comprise at least one composite layer obtained from a composite composition comprising at least one organic compound having a boiling point or a decomposition temperature above 100° C., at least one cellulose derivative, and at least one cement composition selected from the group consisting of
an aluminosilicate geopolymer composition, and a magnesium-based composition, said magnesium-based composition comprising a magnesium silicate, an alkaline silicate, water, and an alkaline base, and
wherein the organic compound represents from 10 to 70 wt %, relative to the total weight of the composite composition.

2. The device according to claim 1 , wherein the cement composition is selected from the group consisting of:
the aluminosilicate geopolymer composition, and
the magnesium-based composition,
said cement composition comprising water, silicon (Si), aluminium (Al) or magnesium (Mg), oxygen (O), and at least one element selected from potassium (K), sodium (Na), lithium (Li), caesium (Cs), and calcium (Ca).

3. The device according to claim 1 , wherein the aluminosilicate geopolymer composition comprises an alkaline silicate, an aluminosilicate, water, and optionally an alkaline base.

4. The device according to claim 1 , wherein the aluminosilicate geopolymer composition comprises from 10 to 50 wt % of an aluminosilicate, from 8 to 35 wt % of an alkaline silicate, from 0 to 10 wt % of an alkaline base and from 10 to 55 wt % of water.

5. The device according to claim 1 , wherein the magnesium-based composition comprises from 10 to 50 wt % of the magnesium silicate, from 8 to 35 wt % of the alkaline silicate, from 5 to 20 wt % of the alkaline base and from 10 to 55 wt % of water.

6. The device according to claim 1 , wherein the cement composition represents from 10 to 80 wt %, relative to the total weight of the composite composition.

7. The device according to claim 1 , wherein the cellulose derivative is a cellulose ether or a cellulose ester.

8. The device according to claim 1 , wherein the cellulose derivative represents from 1 to 25 wt %, relative to the total weight of the composite composition.

9. The device according to claim 1 , wherein the organic compound is selected from polyols.

10. The device according to claim 1 , wherein the composite composition further comprises an expanded carbon-containing material.

11. The device according to claim 1 , wherein the composite composition further comprises one or more additives selected from starch, a plasticizer, an inert filler, a dye, an organic additive with a polymer structure, a crosslinking agent and a mixture thereof.

12. The device according to claim 1 , wherein the composite layer is in the form of an extruded layer and/or a taped layer, or a layer in the form of a filling.

13. The device according to claim 1 , wherein the composite layer has a thickness ranging from 2 to 6 mm.

14. The device according to claim 1 , wherein the composite layer is an inner layer of said cable or of said cable accessory.

15. A composite composition for a composite layer of a power cable and/or a telecommunication cable, or an accessory for a power cable and/or a telecommunication, said composite composition comprising:
at least one organic compound having a boiling point or a decomposition temperature above 100° C.,
at least one cellulose derivative, and
at least one cement composition selected from the group consisting of;
an aluminosilicate geopolymer composition and
a magnesium-based composition, said magnesium-based composition comprising a magnesium silicate, an alkaline silicate, water, and an alkaline base, and
wherein the organic compound represents from 10 to 70 wt %, relative to the total weight of the composite composition.

16. A device comprising a power cable and/or a telecommunication cable, and/or an accessory for a power cable and/or a telecommunication cable, wherein said cable and/or said cable accessory comprise at least one composite layer obtained from a composite composition comprising at least one organic compound having a boiling point or a decomposition temperature above 100° C., at least one cellulose derivative, and at least one cement composition selected in the group consisting of:
an aluminosilicate geopolymer composition, and
a magnesium-based composition, said magnesium-based composition comprising a magnesium silicate, an alkaline silicate, water, and an alkaline base, and
wherein the composite composition further comprises an expanded carbon-containing material.

17. A device comprising a power cable and/or a telecommunication cable, and/or an accessory for a power cable and/or a telecommunication cable, wherein said cable and/or said cable accessory comprise at least one composite layer obtained from a composite composition comprising at least one organic compound having a boiling point or a decomposition temperature above 100° C., at least one cellulose derivative, and at least one cement composition,
wherein said cement composition is a magnesium-based composition comprising from 10 to 50 wt % of a magnesium silicate, from 8 to 35 wt % of an alkaline silicate, from 5 to 20 wt % of an alkaline base and from 10 to 55 wt % of water.

18. Method of manufacturing a device as defined in claim 1 , wherein said method comprises at least the following steps:
1) preparing a composite composition according to at least the following steps:
i) preparing a cement composition selected from an aluminosilicate geopolymer composition comprising an aluminosilicate, an alkaline silicate, water, and optionally an alkaline base, and a magnesium-based composition comprising a magnesium silicate, an alkaline silicate, water, and an alkaline base,
ii) mixing the cement composition from step i) with a cellulose derivative, an organic compound having a boiling point or a decomposition temperature above about 100° C., and optionally water,
wherein the organic compound represents from 10 to 70 wt %, relative to the total weight of the composite composition; and
2) forming a composite layer starting from the composite composition obtained in step 1):
either around one or more elongated conducting elements and/or around a layer of a power cable and/or telecommunication cable, when the device is a cable,
or around at least one of the layers of a junction or of a termination, when the device is a cable accessory.

Assignees

• Nexans

Inventors

• Auvray Thierry
• Gyppaz Franck
• Estreboou Nicolas

Classifications

• C08L1/286

  substituted with acid radicals, e.g. carboxymethyl cellulose [CMC] (C08L1/282 takes precedence) · CPC title

• H01B13/24

  by extrusion {(extrusion of cables with plastic material in general B29C48/15)} · CPC title

• C08K7/24

  inorganic · CPC title

• C04B14/043

  Alkaline-earth metal silicates, e.g. wollastonite · CPC title

• C08K3/04

  Carbon · CPC title