Method for producing a multilayer coating on a metallic substrate

Patent metadata

Field	Value
Publication number	US-10953434-B2
Application number	US-201615546837-A
Country	US
Kind code	B2
Filing date	Jan 28, 2016
Priority date	Feb 6, 2015
Publication date	Mar 23, 2021
Grant date	Mar 23, 2021

Abstract

The present invention relates to a method for producing a multilayer coating on a metallic substrate, comprising, in the given order, (1) producing a polyvinyl chloride plastisol layer on the metallic substrate, comprising the application of a polyvinyl chloride plastisol material to the metallic substrate, (2) producing a thermosetting and/or thermoplastic topcoat layer directly on the polyvinyl chloride plastisol layer, comprising the application of a thermosetting and/or thermoplastic coating material directly to the polyvinyl chloride plastisol layer, wherein both the polyvinyl chloride plastisol material and the thermosetting and/or thermoplastic coating material comprise a layered double hydroxide.

First claim

The invention claimed is:

1. A method for producing a multilayer coating on a metallic substrate, comprising, in the given order,
(1) producing a polyvinyl chloride plastisol layer on the metallic substrate, comprising the application of a polyvinyl chloride plastisol material to the metallic substrate and curing the polyvinyl chloride plastisol layer,
(2) producing a thermosetting topcoat layer directly on the polyvinyl chloride plastisol layer, comprising the application of a thermosetting coating material directly to the polyvinyl chloride plastisol layer and curing the thermosetting topcoat layer,
wherein the layer thickness of the cured polyvinyl chloride plastisol layer is from 50 to 400 micrometer and the layer thickness of the cured thermosetting topcoat layer is 2 to 50 micrometers,

wherein both the polyvinyl chloride plastisol material and the thermosetting coating material comprise a layered double hydroxide, and
wherein
both the polyvinyl chloride plastisol material and the thermosetting coating material comprise, as a UV stabilizer, a blend of at least one 2-(2-hydroxyphenyl)-benzotriazole with at least one hindered amine selected from 2,2,6,6-tetramethyl piperidine and derivatives thereof,
the amounts of layered double hydroxide is from 0.1 to 5% by weight based on the total amount of polyvinyl chloride plastisol material and the thermosetting coating material, respectively, and the amounts of the UV stabilizer blend is from 0.1 to 5% by weight based on the total amount of polyvinyl chloride plastisol material and the thermosetting coating material, respectively,
the thermosetting coating material comprises at least one hydroxy-functional acrylic resin as binder component and at least one polyisocyanate as crosslinker component, or at least one hydroxy-functional polyester resin as binder component and at least one polyisocyanate as crosslinker component, and
wherein the thermosetting coating material is free from thermoplastic coating material.

2. A method for producing a multilayer coating on a metallic substrate, comprising, in the given order,
(1) producing a polyvinyl chloride plastisol layer on the metallic substrate, comprising the application of a polyvinyl chloride plastisol material to the metallic substrate and curing the polyvinyl chloride plastisol layer,
(2) producing a thermosetting topcoat layer directly on the polyvinyl chloride plastisol layer, comprising the application of a thermosetting coating material directly to the polyvinyl chloride plastisol layer and curing the thermosetting topcoat layer,
wherein the layer thickness of the cured PVC plastisol layer is from 50 to 400 micrometer and the layer thickness of the cured thermosetting topcoat layer is 2 to 50 micrometers

wherein both the polyvinyl chloride plastisol material and the thermosetting coating material comprise a layered double hydroxide, and
wherein
both the polyvinyl chloride plastisol material and the thermosetting coating material comprise, as a UV stabilizer, a blend of at least one 2-(2-hydroxyphenyl)-benzotriazole with at least one hindered amine selected from 2,2,6,6-tetramethyl piperidine and derivatives thereof,
the amounts of layered double hydroxide is from 0.1 to 5% by weight based on the total amount of polyvinyl chloride plastisol material and the thermosetting coating material, respectively, and the amounts of the UV stabilizer blend is from 0.1 to 5% by weight based on the total amount of polyvinyl chloride plastisol material and the thermosetting coating material, respectively, and
the thermosetting coating material comprises at least one hydroxy-functional acrylic resin as the only binder component and at least one polyisocyanate as crosslinker component, or at least one hydroxy-functional polyester resin as the only binder component and at least one polyisocyanate as crosslinker component.

3. The method according to claim 2 , wherein the polyvinyl chloride plastisol layer and the thermosetting topcoat layer are produced by coil coating.

4. The method according to claim 2 , wherein, prior to stage (1), a cured conversion coating layer is produced directly on the metallic substrate and a cured primer coating layer is produced directly on the cured conversion coating layer, whereby the polyvinyl chloride plastisol layer is then produced directly on the cured primer coating layer.

5. The method according to claim 2 , wherein the at least one layered double hydroxide is a hydrotalcite.

6. The method according to claim 2 , wherein both the polyvinyl chloride plastisol material and the thermosetting coating layer comprise the same layered double hydroxide.

7. The method according to claim 2 , wherein both the polyvinyl chloride plastisol layer and the thermosetting coating layer are cured at peak metal temperatures of between 180 to 300° C. for a period of 10 to 300 seconds.

8. The method according to claim 2 , wherein the metallic substrate is selected from substrates consisting of iron, aluminum, copper, zinc, magnesium and alloys thereof, and steel.

9. A multilayer coating produced by a method according to claim 2 .

10. A metallic substrate, wherein the metallic substrate is coated with a multilayer coating according to claim 9 .

11. A method for producing a multilayer coating on a metallic substrate, comprising, in the given order,
(1) producing a polyvinyl chloride plastisol layer on the metallic substrate, comprising the application of a polyvinyl chloride plastisol material to the metallic substrate,
(2) producing a thermosetting topcoat layer directly on the polyvinyl chloride plastisol layer, comprising the application of a thermosetting coating material directly to the polyvinyl chloride plastisol layer,
wherein both the polyvinyl chloride plastisol layer and the thermosetting coating layer are cured at peak metal temperatures of between 180 to 300° C. for a period of 10 to 300 seconds,
wherein both the polyvinyl chloride plastisol material and the thermosetting coating material comprise a layered double hydroxide, and
wherein
both the polyvinyl chloride plastisol material and the thermosetting coating material comprise, as a UV stabilizer, a blend of at least one 2-(2-hydroxyphenyl)-benzotriazole with at least one hindered amine selected from 2,2,6,6-tetramethyl piperidine and derivatives thereof,
the amounts of layered double hydroxide is from 0.1 to 5% by weight based on the total amount of polyvinyl chloride plastisol material and the thermosetting coating material, respectively, and the amounts of the UV stabilizer blend is from 0.1 to 5% by weight based on the total amount of polyvinyl chloride plastisol material and the thermosetting coating material, respectively,
the thermosetting coating material comprises at least one hydroxy-functional acrylic resin as binder component and at least one polyisocyanate as crosslinker component, or at least one hydroxy-functional polyester resin as binder component and at least one polyisocyanate as crosslinker component, and
wherein the thermosetting coating material is free from thermoplastic coating material.

12. The method according to claim 11 , wherein stage (1) further comprises the curing of the polyvinyl chloride plastisol layer and stage (2) further comprises the curing of the thermosetting topcoat layer.

13. The method according to claim 12 , wherein the layer thickness of the cured PVC plastisol layer is from 50 to 400 micrometer and the layer thickness of the cured thermosetting topcoat layer is 2 to 50 micrometers.

14. The method according to claim 11 , wherein the polyvinyl chloride plastisol layer and the thermosetting topcoat layer a

Assignees

• Akzo Nobel Coatings Int Bv

Inventors

• Bautista Mester Rafael
• Davies Paul
• Corkish Stephen
• Birch Stephen

Classifications

• B05D7/536

  each layer being cured, at least partially, separately · CPC title

• C09D175/06

  from polyesters · CPC title

• B05D2601/20

  used for non-pigmentation effect · CPC title

• C09D127/06

  Homopolymers or copolymers of vinyl chloride · CPC title

• B05D7/52 Primary

  Two layers · CPC title