Surface-treated steel sheet for battery containers

Patent metadata

Field	Value
Publication number	US-10950828-B2
Application number	US-201615780929-A
Country	US
Kind code	B2
Filing date	Dec 5, 2016
Priority date	Dec 3, 2015
Publication date	Mar 16, 2021
Grant date	Mar 16, 2021

Abstract

A surface-treated steel sheet for a battery container, including a steel sheet, an iron-nickel diffusion layer formed on the steel sheet, and a nickel layer formed on the iron-nickel diffusion layer and constituting the outermost layer, wherein when the Fe intensity and the Ni intensity are continuously measured from the surface of the surface-treated steel sheet for a battery container along the depth direction with a high frequency glow discharge optical emission spectrometric analyzer, the thickness of the iron-nickel diffusion layer being the difference between the depth at which the Fe intensity exhibits a first predetermined value and the depth at which the Ni intensity exhibits a second predetermined value is 0.04 to 0.31 μm; and the total amount of the nickel contained in the iron-nickel diffusion layer and the nickel contained in the nickel layer is 10.8 to 26.7 g/m 2 .

First claim

The invention claimed is:

1. A battery container, comprising:
a bottomed cylindrical shaped article made of a surface-treated steel sheet, wherein the surface-treated steel sheet comprises:
a steel sheet;
an iron-nickel diffusion layer formed on the steel sheet; and
a nickel layer formed on the iron-nickel diffusion layer and constituting the outermost layer, the nickel layer consisting of nickel,

wherein when the Fe intensity and the Ni intensity are continuously measured from the surface of the surface-treated steel sheet for a battery container along the depth direction with a high frequency glow discharge optical emission spectrometric analyzer, the thickness of the iron-nickel diffusion layer being the difference (D2−D1) between the depth (D1) at which the Fe intensity exhibits a first predetermined value and the depth (D2) at which the Ni intensity exhibits a second predetermined value is 0.04 to 0.31 μm,
wherein the total amount of the nickel contained in the iron-nickel diffusion layer and the nickel contained in the nickel layer is 10.8 to 26.7 g/m 2 ,
wherein the depth (D1) exhibiting the first predetermined value is the depth exhibiting an intensity of 10% of the saturated value of the Fe intensity measured by the above-described measurement,
wherein the depth (D2) exhibiting the second predetermined value is the depth exhibiting an intensity of 10% of the maximum value when the measurement is further performed along the depth direction after the Ni intensity shows the maximum value by the above-described measurement, and
wherein the iron-nickel diffusion layer is disposed on an inner surface of the bottomed cylindrical shaped article.

2. The battery container according to claim 1 , wherein the ratio of the thickness of the iron-nickel diffusion layer to the thickness of the nickel layer (thickness of iron-nickel diffusion layer/thickness of nickel layer) is 0.013 to 0.50.

3. The battery container according to claim 1 , wherein the thickness of the nickel layer is 1.0 μm or more.

4. The battery container according to claim 1 , wherein the Vickers hardness (HV) of the nickel layer measured with a load of 10 gf is 220 to 280.

5. A battery provided with the battery container according to claim 1 .

6. The battery container according to claim 1 , wherein the bottomed cylindrical shaped article is a battery can.

7. The battery container according to claim 1 , wherein the bottomed cylindrical shaped article is a positive electrode can.

8. A method for producing a battery container having a surface-treated steel sheet, said method comprising:
forming a bottomed cylindrical shaped article having an inner surface; and
forming the surface-treated steel sheet by a method comprising:
forming a nickel plating layer on a surface of a steel sheet with a nickel amount of 10.8 to 26.7 g/m 2 ; and
forming an iron-nickel diffusion layer and a nickel layer constituting an outermost layer by applying a heat treatment to the steel sheet having the nickel plating layer formed thereon by maintaining the steel sheet at a temperature of 450 to 600° C. for 30 seconds to 2 minutes,

wherein the nickel plating layer is formed on the inner surface of the bottomed cylindrical shaped article and consists of nickel.

Assignees

• Toyo Kohan Co Ltd

Inventors

• Sadaki Kota
• Yoshioka Koh

Classifications

• H01M50/134

  Hardness · CPC title

• H01M50/133

  Thickness · CPC title

• H01M50/119

  Metals · CPC title

• C25D7/00

  Electroplating characterised by the article coated · CPC title

• H01M50/107

  having curved cross-section, e.g. round or elliptic (H01M50/103, H01M50/109, H01M50/11 take precedence) · CPC title