Method for manufacturing briquettes containing a calcium-magnesium compound and an iron-based compound, and briquettes thus obtained

Patent metadata

Field	Value
Publication number	US-10947157-B2
Application number	US-201716307567-A
Country	US
Kind code	B2
Filing date	Jul 7, 2017
Priority date	Jul 8, 2016
Publication date	Mar 16, 2021
Grant date	Mar 16, 2021

Abstract

A method for manufacturing green or thermally treated briquettes which are made up of at least one quick calcium-magnesium compound that is an iron-based compound. The method includes the steps of supplying a homogeneous pulverulent mixture to a roller press, the press having pockets where the pulverulent mixture is compressed to form the green briquettes. The rollers of the roller press develop linear speeds at the periphery of the rollers between 10 and 100 cm/s and linear pressures between 60 and 160 kN/cm. The method can also include a thermal treatment of the green briquettes to produce fired briquettes containing calcium ferrite, the briquettes having a Shatter Test Index less than 8%, and a porosity value greater than or equal to 30%.

First claim

The invention claimed is:

1. Method for manufacturing a calcium-magnesium composition in the form of briquettes, comprising the following steps:
i. supplying a homogeneous pulverulent mixture comprising at least one quick calcium-magnesium compound, said mixture comprising at least 40 wt % of CaO+MgO equivalent relative to the weight of said composition and having a Ca/Mg molar ratio greater than or equal to 1;
ii. feeding a roller press with said homogeneous pulverulent mixture, said roller press being equipped with rollers provided with pockets,
iii. compressing said homogeneous pulverulent mixture in said roller press while obtaining a calcium-magnesium composition in the form of green briquettes, and
iv. collecting said green briquettes
said method being characterized in that said homogeneous pulverulent mixture further comprises an iron-based compound present at a content of at least 20 wt % of Fe 2 O 3 equivalent relative to the weight of said composition, said iron-based compound having a granulometric distribution characterized by a median size d 50 below 100 μm as well as a size d 90 below 200 μm, in that said quick calcium-magnesium compound is quicklime, said quicklime having a value of t 60 below 10 min, in that the rollers of the roller press develop linear speeds at the periphery of the rollers between 10 and 100 cm/s and linear pressures between 60 and 160 kN/cm, and in that the method further comprises a thermal treatment of said collected green briquettes at a temperature between 900° C. and 1200° C. for a predetermined duration of between 3 and 20 minutes, while obtaining fired briquettes containing calcium ferrite and having simultaneously a Shatter Test Index less than 8%, and a porosity value greater than or equal to 30%.

2. Method according to claim 1 , in which said compression step is effected in the presence of a binder or a lubricant at a content between 0.1 and 1 wt % relative to the total weight of said green briquettes.

3. Method according to claim 1 , further comprising, before said supplying of a homogeneous pulverulent mixture,
v. feeding a mixer with at least 40 wt % of quicklime having a value of t 60 below 10 min relative to the weight of said composition and with at least 20 wt % of Fe 2 O 3 equivalent of an iron-based compound relative to the weight of said composition, said iron-based compound having a granulometric distribution characterized by a median size d 50 below 100 μm as well as a size d 90 below 200 μm; and
vi. mixing said quicklime with said iron-based compound for a predetermined length of time, sufficient to obtain an approximately homogeneous pulverulent mixture of said quicklime and of said iron-based compound.

4. Method according to claim 3 , in which a binder or lubricant is added to the mixer, and in which said binder or lubricant is included in said homogeneous pulverulent mixture.

5. Method according to claim 1 , in which said quick calcium-magnesium compound contains at least 10 wt % of quicklime in the form of ground particles.

6. Method according to claim 1 , further comprising a pre-treatment step of the collected green briquettes under modified atmosphere containing at least 2 vol % CO 2 and at most 30 vol % CO 2 with respect to the modified atmosphere.

7. Method for manufacturing a calcium-magnesium composition in the form of fired briquettes, comprising the following steps:
i. supplying a homogeneous pulverulent mixture comprising at least one quick calcium-magnesium compound, said mixture comprising at least 40 wt % of CaO+MgO equivalent relative to the weight of said composition and having a Ca/Mg molar ratio greater than or equal to 1,
ii. feeding a roller press with said homogeneous pulverulent mixture, said roller press being equipped with rollers provided with pockets,
iii. compressing said homogeneous pulverulent mixture in said roller press, while obtaining a calcium-magnesium composition in the form of green briquettes, and
iv. collecting said green briquettes,
said method being characterized in that said homogeneous pulverulent mixture further comprises an iron-based compound present at a content of at least 20 wt % of Fe 2 O 3 equivalent relative to the weight of said composition, said iron-based compound having a granulometric distribution characterized by a median size d 50 below 100 μm as well as a size d 90 below 200 μm, in that said “quick” calcium-magnesium compound is burned dolomite, said burned dolomite having a value of t 70 below 10 min, in that the rollers of the roller press develop linear speeds at the periphery of the rollers between 10 and 100 cm/s and linear pressures between 60 and 160 kN/cm, and in that the method further comprises a thermal treatment of said collected green briquettes at a temperature between 900° C. and 1200° C. for a predetermined duration of between 3 and 20 minutes, while obtaining fired briquettes containing calcium ferrite and having simultaneously a Shatter Test Index less than 8%, and a porosity value greater than or equal to 30%.

8. Method according to claim 7 , in which said compression step is effected in the presence of a binder or a lubricant at a content between 0.1 and 1 wt % relative to the total weight of said green briquettes.

9. Method according to claim 7 , further comprising, before said supplying of a homogeneous pulverulent mixture,
i. feeding a mixer with at least 40 wt % of burned dolomite having a value of t 70 below 10 min relative to the weight of said composition and with at least 20 wt % of Fe 2 O 3 equivalent of an iron-based compound relative to the weight of said composition, said iron-based compound having a granulometric distribution characterized by a median size d 50 below 100 μm as well as a size d 90 below 200 μm, and
ii. mixing said burned dolomite with said iron-based compound for a predetermined length of time, sufficient to obtain an approximately homogeneous pulverulent mixture of said burned dolomite and of said iron-based compound.

10. Method according to claim 9 , in which a binder or lubricant is added to the mixer, and in which said binder or lubricant is included in said homogeneous pulverulent mixture.

11. Method according to claim 7 , further comprising a pre-treatment step of the collected green briquettes under modified atmosphere containing at least 2 vol % CO 2 and at most 30 vol % CO 2 with respect to the modified atmosphere.

Assignees

• Lhoist Rech Et Developpement Sa

Inventors

• Criniere Guillaume
• Nispel Michael

Classifications

• C22B1/244

  organic · CPC title

• C22B1/243

  inorganic · CPC title

• C22B1/242 Primary

  with binders · CPC title

• C04B22/064

  of the alkaline-earth metals · CPC title

• C04B35/63

  using additives specially adapted for forming the products {, e.g.. binder binders} · CPC title